Method for high resolution lithography
Assignee: Fujitsu IT Holdings Inc
•
Filing: 1983-08-09
•
Granted: 1984-10-09
•
Expires: 2003-08-09
Abstract
Abstract A method for performing high resolution lithography. The first step involves disposing on a substructure having a surface layer to be patterned a layer of a resist material characterized by both substantial degradation sensitivity for incident ionizing radiation of a predetermined type and substantial instability of undegraded regions for a predetermined plasma etchant which attacks the surface layer. The next step is to expose a prearranged pattern of regions of the resist layer to the predetermined type of radiation to produce a corresponding pattern of degraded resist regions. Then the pattern of degraded resist regions is removed using a preselected developing solution. The next step is to modify the resist material to increase the stability thereof for the plasma etchant by exposing the developed resist layer to ionizing radiation of a type which has been predetermined to degrade the resist material and then baking the degraded resist layer. The final step is to etch the exposed regions of the surface layer using said plasma etchant.
Inventors
- 👤 Eric Tobias
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:42
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/20; G03F7/2022; G03F7/2024; G03F7/004; G03F7/039
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
139 words
In a method for performing high resolution lithography, the steps of: disposing on a substructure having a surface layer to be patterned a layer of a positive electron beam resist material characterized by both substantial degradation sensitivity for incident electron beams and substantial instability of undegraded regions for a predetermined plasma etchant which attacks said surface layer; exposing a prearranged pattern of regions of said resist layer to said electron beams to produce a corresponding pattern of degraded resist regions; removing said pattern of degraded resist regions using a preselected developing solution to form a developed resist layer; modifying said resist material to increase the stability thereof for said plasma etchant by exposing said developed resist layer to paid electron beam and baking said degraded resist layer; and etching exposed regions of said surface layer using said plasma etchant.
Claim 2
Dependent Claim
139 words
In a method for performing high resolution lithography, the steps of: disposing on a substructure having a surface layer to be patterned a layer of a positive electron beam resist material characterized by both substantial degradation sensitivity for incident electron beams and substantial instability of undegraded regions for a predetermined plasma etchant which attacks said surface layer; exposing a prearranged pattern of regions of said resist layer to said electron beams to produce a corresponding pattern of degraded resist regions; removing said pattern of degraded resist regions using a preselected developing solution to form a developed resist layer; modifying said resist material to increase the stability thereof for said plasma etchant by exposing said developed resist layer to paid electron beam and baking said degraded resist layer; and etching exposed regions of said surface layer using said plasma etchant.
Claim 3
Dependent Claim
49 words
The method of claim 1, wherein; said step of exposing said resist layer comprises scanning a beam of electrons in a prearranged modulated pattern across said resist layer; and said step of exposing said developed resist layer comprises scanning a beam of electrons uniformly over said developed resist layer.
Claim 4
Dependent Claim
14 words
The method of claim 2, wherein said electron beam resist is a Poly(olefin sulfone).
Claim 5
Dependent Claim
13 words
The method of claim 2, wherein said electron beam resist is Poly(butene-1 sulfone).
Claim 6
Dependent Claim
136 words
In a method for forming a high resolution masking layer pattern on a semiconductor wafer, the steps of: forming on said wafer a layer of masking material; disposing directly on said layer of masking material a layer of electron beam resist material characterized by both substantial degradation sensitivity for electron beam radiation and substantial instability of undegraded regions for a predetermined plasma etchant which attacks said masking material; esposing a prearranged pattern of regions of said resist layer to scanning electron beam radiation to produce a corresponding pattern of degraded resist regions; removing said pattern of degraded resist regions using a preselected developing solution; exposing said developed resist layer to scanning electron beam radiation to degrade said resist material; baking said degraded resist material; and etching exposed regions of said surface layer using said plasma etchant.
Claim 7
Dependent Claim
136 words
In a method for forming a high resolution masking layer pattern on a semiconductor wafer, the steps of: forming on said wafer a layer of masking material; disposing directly on said layer of masking material a layer of electron beam resist material characterized by both substantial degradation sensitivity for electron beam radiation and substantial instability of undegraded regions for a predetermined plasma etchant which attacks said masking material; esposing a prearranged pattern of regions of said resist layer to scanning electron beam radiation to produce a corresponding pattern of degraded resist regions; removing said pattern of degraded resist regions using a preselected developing solution; exposing said developed resist layer to scanning electron beam radiation to degrade said resist material; baking said degraded resist material; and etching exposed regions of said surface layer using said plasma etchant.
Claim 8
Dependent Claim
49 words
The method of claim 5, wherein said step of exposing said resist layer comprises scanning a beam of electrons in a prearranged modulated pattern across said resist layer; and said step of exposing said developed resist layer comprises scanning a beam of electrons uniformly over said developed resist layer.
Claim 9
Dependent Claim
44 words
The method of claim 5, wherein said layer of masking material is a layer of silicon formed to a thickness of at least about one micron; said resist material is Poly(butene-1sulfone) formed to a thickness in the range of about 3,000 to 5,000 Angstroms.
Claim 10
Dependent Claim
45 words
The method of claim 5, wherein said layer of masking material is a layer of silicon nitride formed to a thickness of about 1,000 Angstroms; and said resist material is Poly(butene-1 sulfone) formed to a thickness in the range of about 3,000 to 5,000 Angstroms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |