Method of forming a relatively stable slip of silicon metal particles and yttrium containing particles
Assignee: Ceradyne Inc
•
Filing: 1983-07-08
•
Granted: 1984-09-11
•
Expires: 2003-07-08
Abstract
Abstract The method concerns forming a relatively stable slip of silicon metal particles and yttrium containing particles. In one embodiment, a casting slip of silicon metal particles is formed in water. Particles of a yttrium containing sintering aid are added to the casting slip. The yttrium containing sintering aid is a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating the silicon metal particles into a semiporous solid. A small amount of a fluoride salt is added to the casting slip which contains the yttrium containing sintering aid. The fluoride salt is one which will produce fluoride anions when dissolved in water. The small amount of the fluoride anions produced are effective to suppress the flocculation of the silicon metal particles by the Y +3 ions so that all particles remain in suspension in the casting slip and the casting slip has both an increased shelf life and can be used to cast articles having a relatively thick cross-section. The pH of the casting slip is maintained in a range from 7.5 to 9. Preferably, the fluoride salt used is one which is based on a monovalent cation such as sodium or ammonia. The steps of adding the yttrium containing sintering aid and the fluoride salt may be interchanged if desired, and the salt may be added to a solution containing the sintering aid prior to addition of the silicon metal particles.
Inventors
- 👤 Ray A. Dickie
- 👤 John A. Mangels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:31
CPC Classifications
C; C04; C04B; C04B33/00; C04B33/28; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/591
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
179 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to said casting slip particles of a yttrium containing sintering aid, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid; adding to said casting slip which contains said yttrium containing sintering aid a small amount of a fluoride salt which will produce fluoride anions when dissolved in water, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 2
Independent Claim
179 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to said casting slip particles of a yttrium containing sintering aid, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid; adding to said casting slip which contains said yttrium containing sintering aid a small amount of a fluoride salt which will produce fluoride anions when dissolved in water, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 3
Dependent Claim
17 words
The method of claim 1, in which said fluoride salt is one based on a monovalent cation.
Claim 4
Dependent Claim
71 words
The method of claim 1, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% by weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
Claim 5
Dependent Claim
70 words
The method of claim 2, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
Claim 6
Independent Claim
175 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to said casting slip a small amount of a fluoride salt which will produce fluoride anions when dissolved in water; adding to said fluoride anion containing casting slip particles of a yttrium containing sintering aid, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 7
Independent Claim
175 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to said casting slip a small amount of a fluoride salt which will produce fluoride anions when dissolved in water; adding to said fluoride anion containing casting slip particles of a yttrium containing sintering aid, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 8
Dependent Claim
17 words
The method of claim 5, in which said fluoride salt is one based on a monovalent cation.
Claim 9
Dependent Claim
71 words
The method of claim 5, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% by weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
Claim 10
Dependent Claim
71 words
The method of claim 6, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% by weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
Claim 11
Independent Claim
188 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to a solution of particles of a yttrium containing sintering aid a small amount of a fluoride salt which will produce fluoride anions when dissolved in water; adding to said casting slip said solution of said particles of a yttrium containing sintering aid having said fluoride salt therein, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 12
Independent Claim
188 words
A method of forming a relatively stable slip of silicon metal particles and yttrium containing particles, characterized by the steps of: forming a casting slip of silicon metal particles in water; adding to a solution of particles of a yttrium containing sintering aid a small amount of a fluoride salt which will produce fluoride anions when dissolved in water; adding to said casting slip said solution of said particles of a yttrium containing sintering aid having said fluoride salt therein, said yttrium containing sintering aid being a compound which has at least some solubility in water to form Y +3 ions which have a high potential for totally flocculating said silicon metal particles into a semiporous solid, said small amount of said fluoride anions being effective to suppress the flocculation of said silicon metal particles by said Y +3 ions so that said silicon metal particles as well as said particles of said yttrium containing sintering aid remain in suspension in said casting slip and said casting slip has an increased shelf life; and maintaining the pH of said casting slip in a range from 7.5 to 9.
Claim 13
Dependent Claim
17 words
The method of claim 9, in which said fluoride salt is one based on a monovalent cation.
Claim 14
Dependent Claim
71 words
The method of claim 9, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% by weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
Claim 15
Dependent Claim
71 words
The method of claim 10, wherein said silicon metal particles have a size range less than 10 microns, wherein said silicon metal particles make up 95.5-77% by weight of the total weight of the particles in suspension, wherein said yttrium compound has a size range less than five microns, and wherein said fluoride salt is in an amount of 0.01-0.25% by weight of the total weight of the particles in suspension.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |