Multicomponent thermoplastic polymer blends
Assignee: Honeywell International Inc
•
Filing: 1984-02-02
•
Granted: 1984-08-14
•
Expires: 2004-02-02
Abstract
Abstract The invention is a multicomponent thermoplastic interpenetrating polymer network blend having a particulate loaded homopolymer as the network stabilizing phase.
Inventors
- 👤 Ian W. Sorensen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:22
CPC Classifications
C; C08; C08L; C08L101/00; Y; Y10; Y10S; Y10S525/00; Y10S525/903
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
113 words
A thermoplastic polymer blend comprising: a least one dissimilar thermoplastic resin having Newtonian rheological behavior and a determinable viscosity at a blending temperature; at least one other polymer having Newtonian rheological behavior at low shearing frequencies loaded with a predetermined quantity of particulates, said preloaded other polymer shear stress blended with said at least one dissimilar thermoplastic resin at said blending temperature and with a predetermined shear stress to form at least partially continuous interpenetrating network with each other, said predetermined quantity of particulates selected to impart to said other polymer a Non-Newtonian rheological behavior having a viscosity approximately equal to said determinable viscosity at said blending temperature and said predetermined stress rate.
Claim 2
Dependent Claim
113 words
A thermoplastic polymer blend comprising: a least one dissimilar thermoplastic resin having Newtonian rheological behavior and a determinable viscosity at a blending temperature; at least one other polymer having Newtonian rheological behavior at low shearing frequencies loaded with a predetermined quantity of particulates, said preloaded other polymer shear stress blended with said at least one dissimilar thermoplastic resin at said blending temperature and with a predetermined shear stress to form at least partially continuous interpenetrating network with each other, said predetermined quantity of particulates selected to impart to said other polymer a Non-Newtonian rheological behavior having a viscosity approximately equal to said determinable viscosity at said blending temperature and said predetermined stress rate.
Claim 3
Dependent Claim
48 words
The thermoplastic polymer blend of claim 1 wherein the ratio of the viscosity of the dissimilar thermoplastic resin at said blending temperature to the viscosity of said other polymer loaded with said particulate at said same temperature and said predetermined stress rate is preferably between 0.8 and 1.2.
Claim 4
Dependent Claim
19 words
The thermoplastic polymer blend of claim 1 wherein said at least one dissimilar resin is only one dissimilar resin.
Claim 5
Dependent Claim
33 words
The thermoplastic polymer blend of claim 1 wherein said at least one dissimilar resin is one dissimilar resin loaded with a particulate to impart to said dissimilar resin a Non Newtonian rheological behavior.
Claim 6
Dependent Claim
34 words
The thermoplastic polymer blend of claim 1 wherein said blending temperature is a temperature higher than the highest melting temperature of said at least one dissimilar thermoplastic resin and said at least one polymer.
Claim 7
Dependent Claim
119 words
A thermoplastic polymer blend having at least one dissimilar thermoplastic resin having a determinable viscosity at a blending temperature stress blended with at least one other polymer constituent to form an interpenetrating polymer network with said at least one dissimilar thermoplastic resin characterized by said other polymer constituent comprising: at least one other polymer having a Newtonian rheological behavior at low shearing frequencies; and a predetermined quantity of a particulate loaded into said at least one other polymer to impart to said at least one other polymer a Non Newtonian rheological behavior, said at least one other polymer loaded with said particulate having a viscosity approximately equal to said determinable viscosity at said blending temperature during said stress blending.
Claim 8
Dependent Claim
119 words
A thermoplastic polymer blend having at least one dissimilar thermoplastic resin having a determinable viscosity at a blending temperature stress blended with at least one other polymer constituent to form an interpenetrating polymer network with said at least one dissimilar thermoplastic resin characterized by said other polymer constituent comprising: at least one other polymer having a Newtonian rheological behavior at low shearing frequencies; and a predetermined quantity of a particulate loaded into said at least one other polymer to impart to said at least one other polymer a Non Newtonian rheological behavior, said at least one other polymer loaded with said particulate having a viscosity approximately equal to said determinable viscosity at said blending temperature during said stress blending.
Claim 9
Dependent Claim
38 words
The polymer blend of claim 6 wherein the ratio of said determinable viscosity and the viscosity of the particulate loaded at least one other polymer is between 0.8 and 1.2 at said blending temperature and blending stress rate.
Claim 10
Dependent Claim
52 words
The thermoplastic polymer blend of claim 6 wherein said dissimilar thermoplastic resin comprises: a predetermined thermoplastic polymer having Newtonian rheological behavior; and a predetermined quantity of a second particulate loaded into said thermoplastic polymer to impart to said thermoplastic polymer a Non-Newtonian rheological behavior exhibiting said determinable viscosity at said blending temperature.
Claim 11
Independent Claim
127 words
A method for making a thermoplastic interpenetrating polymer network blend comprising the steps of: mixing a predetermined quantity of particulate with a polymer having Newtonian rheological properties at low shearing frequencies to form a dispersed phase polymer having Non-Newtonian rheological behavior, heating said dispersed phase polymer along with at least one dissimilar thermoplastic resin to a blending temperature; blending said dispersed phase polymer with said dissimilar thermoplastic resin in a shear blender at a predetermined shear rate to produce at least partial continuous interlocked networks between said dispersed phased polymer and said dissimilar thermoplastic resin; and terminating said blending to freeze said dispersed phase polymer in said interlocked network to form said thermoplastic interpenetrating polymer network blend with said dispersed phase polymer being the structure stabilizing phase.
Claim 12
Independent Claim
127 words
A method for making a thermoplastic interpenetrating polymer network blend comprising the steps of: mixing a predetermined quantity of particulate with a polymer having Newtonian rheological properties at low shearing frequencies to form a dispersed phase polymer having Non-Newtonian rheological behavior, heating said dispersed phase polymer along with at least one dissimilar thermoplastic resin to a blending temperature; blending said dispersed phase polymer with said dissimilar thermoplastic resin in a shear blender at a predetermined shear rate to produce at least partial continuous interlocked networks between said dispersed phased polymer and said dissimilar thermoplastic resin; and terminating said blending to freeze said dispersed phase polymer in said interlocked network to form said thermoplastic interpenetrating polymer network blend with said dispersed phase polymer being the structure stabilizing phase.
Claim 13
Dependent Claim
28 words
The method of claim 9 wherein said step of heating includes the step of heating said dispersed phase polymer with one dissimilar thermoplastic resin to said blending temperature.
Claim 14
Dependent Claim
26 words
The method of claim 9 wherein said step of heating includes the step of heating said dispersed phase polymer with at least two dissimilar thermoplastic resins.
Claim 15
Dependent Claim
40 words
The method of claim 10 wherein said method further includes the step of premixing said dissimilar thermoplastic resin with at least one viscosity modifier to change the viscosity of said thermoplastic resin to be approximately equal to said predetermined viscosity.
Claim 16
Dependent Claim
56 words
The method of claim 10 wherein said method further includes the step of premixing said dissimilar thermoplastic resin with at least one viscosity modifier to change the viscosity of said dissimilar thermoplastic resin and reduce the ratio between the viscosity of the dissimilar thermoplastic resin and the predetermined viscosity to the range between 0.8 and 1.2.
Claim 17
Dependent Claim
46 words
The method of claim 9 wherein said step of mixing includes the step of mixing said predetermined quantity of particulates to cause said predetermined viscosity to be approximately equal to the viscosity of said dissimilar thermoplastic resin at said blending temperature and said blending stress rate.
Claim 18
Dependent Claim
52 words
The method of claim 9 wherein said step of mixing includes the step of mixing said predetermined quantity of particulates to cause the ratio of said predetermined viscosity to the viscosity of said dissimilar thermoplastic resin to be between 0.8 and 1.2 at said blending temperature and said blending shear stress rate.
Claim 19
Dependent Claim
49 words
The method of claim 9 wherein said method further includes the step of mixing a particulate with at least one of said dissimilar thermoplastic resins to form a dispersed phase resin having Non Newtonian rheological behavior having a viscosity approximately equal to said predetermined viscosity at said blending temperature.
References Cited (Backward Citations)
CA705481A
Cited
US3431224A
Cited
US3422056A
Cited
US3393174A
Cited
US3437631A
Cited
US3660347A
Cited
US3629154A
Cited
US4302553A
Cited
US3742088A
Cited
US3816373A
Cited
US3932323A
Cited
US3976618A
Cited
US3933730A
Cited
US4111875A
Cited
US4161419A
Cited
US4088627A
Cited
US4102854A
Cited
US4088626A
Cited
US4281084A
Cited
US4117894A
Cited
US4201704A
Cited
US4280948A
Cited
US4263196A
Cited
US4243575A
Cited
US4338227A
Cited
US4335032A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-14 | 1988-02-13 | 1988-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-14 | 1992-02-13 | 1992-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-14 | 1996-02-13 | 1996-08-14 | $7700.00 | Window Closed / Lapsed |