Interpenetrating polymeric networks
Assignee: Individual
•
Filing: 1972-11-02
•
Granted: 1981-11-24
•
Expires: 1992-11-02
Abstract
Abstract Synthetic resins having a topologically interpenetrating polymeric network comprise macrocyclic structures of chemically different, crosslinking polymers which are permanently entangled with each other. The several macrocyclic structures that are present are characterized by the absence of chemical bonds between the individual networks.
Inventors
- 👤 Harry L. Frisch
- 👤 Kurt C. Frisch
- 👤 Daniel Klempner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:44
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08G; C08G83/00; C08L101/00; C08L21/00; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L25/10; C08L33/00; C08L33/04; C08L33/06; C08L33/08; C08L63/00; C08L75/00; C08L75/04; C08L2205/00; C08L2205/04; Y; Y10; Y10S; Y10S525/00; Y10S525/903
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
90 words
A synthetic resin having a topologically interpenetrating polymeric network characterized by a single glass transition temperature comprising at least two separate chemically dissimilar macrocyclic structures of crosslinked polymer chains which do not contain ionizable groups and which are crosslinked by different crosslinking agents which crosslink by different crosslinking mechanisms, the polymer chains of one macrocyclic structure being threaded through, but having substantially no intermolecular chemical bonding with, another macrocyclic structure of the interpenetrating polymeric network, with the proviso that the macrocyclic structures have rings of at least 20 ring atoms.
Claim 2
Dependent Claim
90 words
A synthetic resin having a topologically interpenetrating polymeric network characterized by a single glass transition temperature comprising at least two separate chemically dissimilar macrocyclic structures of crosslinked polymer chains which do not contain ionizable groups and which are crosslinked by different crosslinking agents which crosslink by different crosslinking mechanisms, the polymer chains of one macrocyclic structure being threaded through, but having substantially no intermolecular chemical bonding with, another macrocyclic structure of the interpenetrating polymeric network, with the proviso that the macrocyclic structures have rings of at least 20 ring atoms.
Claim 3
Dependent Claim
24 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked poly(urethaneurea) chains and another macrocyclic structure comprises crosslinked polyacrylate chains.
Claim 4
Dependent Claim
24 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polychloroprene chains and another macrocyclic structure comprises crosslinked poly(urethane-urea) chains.
Claim 5
Dependent Claim
24 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked poly(styrenebutadiene) chains and another macrocyclic structure comprises crosslinked poly(urethane-urea) chains.
Claim 6
Dependent Claim
23 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked poly(dimethylsiloxane) chains and another macrocyclic structure comprises poly(urethane-urea) chains.
Claim 7
Dependent Claim
23 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked poly(dimethylsiloxane) chains and another macrocyclic structure comprises polyacrylate chains.
Claim 8
Dependent Claim
23 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyesterstyrene chains and another macrocyclic structure comprises polyurethane chains.
Claim 9
Dependent Claim
24 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyurethane chains and another macrocyclic structure comprises crosslinked polyepoxide chains.
Claim 10
Dependent Claim
25 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked poly(ethyl acrylate) chains and another macrocyclic structure comprises crosslinked polyurethane chains.
Claim 11
Dependent Claim
29 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked copolymers of ethyl acrylate with methyl methacrylate and another macrocyclic structure comprises crosslinked polyurethane chains.
Claim 12
Dependent Claim
25 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyepoxide chains and another macrocyclic structure comprises crosslinked polyester-urethane adduct chains.
Claim 13
Dependent Claim
26 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyesterurethane adduct chains and another macrocyclic structure comprises crosslinked poly(ethyl acrylate) chains.
Claim 14
Dependent Claim
25 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyepoxide chains and another macrocyclic structure comprises crosslinked poly(ethyl acrylate) chains.
Claim 15
Dependent Claim
24 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked styrene chains and another macrocyclic structure comprises crosslinked polyurethane chains.
Claim 16
Dependent Claim
25 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyesterstyrene adduct chains and another macrocyclic structure comprises crosslinked polyepoxide chains.
Claim 17
Dependent Claim
25 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyesterstyrene adduct chains and another macrocyclic structure comprises crosslinked polyurethane chains.
Claim 18
Dependent Claim
16 words
The synthetic resin in accordance with claim 1 wherein one macrocyclic structure comprises crosslinked polyurethane chains.
Claim 19
Independent Claim
117 words
A method for the production of synthetic resin of two or more polymers having an interpenetrating polymeric network of polymeric chains characterized by a single glass transition temperature which comprises providing at least two types of chemically dissimilar polymers which do not contain ionizable groups and which are crosslinkable by different crosslinking mechanisms using polymer specific crosslinking agents, forming an intimate admixture of said types of chemically dissimilar polymers, and simultaneously crosslinking with polymer specific crosslinking agents polymers of the same type to each other while in intimate admixture, thereby producing separate macrocyclic structures of said chemically dissimilar polymers having substantially no intermolecular chemical bonding therebetween but being threaded through each other in an interpenetrating polymeric network.
Claim 20
Independent Claim
117 words
A method for the production of synthetic resin of two or more polymers having an interpenetrating polymeric network of polymeric chains characterized by a single glass transition temperature which comprises providing at least two types of chemically dissimilar polymers which do not contain ionizable groups and which are crosslinkable by different crosslinking mechanisms using polymer specific crosslinking agents, forming an intimate admixture of said types of chemically dissimilar polymers, and simultaneously crosslinking with polymer specific crosslinking agents polymers of the same type to each other while in intimate admixture, thereby producing separate macrocyclic structures of said chemically dissimilar polymers having substantially no intermolecular chemical bonding therebetween but being threaded through each other in an interpenetrating polymeric network.
Claim 21
Dependent Claim
16 words
The method in accordance with claim 14 wherein emulsions of said types of polymers are admixed.
Claim 22
Independent Claim
82 words
A method for the production of a synthetic resin of two or more polymers having an interpenetrating network of polymeric chains which comprises providing a macrocyclic structure of crosslinked polymer containing no ionizable groups, sorbing within the macrocyclic structure of the crosslinked polymer, a liquid, crosslinkable polymer which contains no ionizable groups and which is chemically dissimilar to said macrocyclic crosslinked polymer and does not chemically inter-react therewith, and thereafter crosslinking the sorbed polymer in situ with a polymer specific crosslinking agent.
Claim 23
Independent Claim
82 words
A method for the production of a synthetic resin of two or more polymers having an interpenetrating network of polymeric chains which comprises providing a macrocyclic structure of crosslinked polymer containing no ionizable groups, sorbing within the macrocyclic structure of the crosslinked polymer, a liquid, crosslinkable polymer which contains no ionizable groups and which is chemically dissimilar to said macrocyclic crosslinked polymer and does not chemically inter-react therewith, and thereafter crosslinking the sorbed polymer in situ with a polymer specific crosslinking agent.
Claim 24
Independent Claim
126 words
A method for the production of synthetic resin of two or more polymers having an interpenetrating polymeric network of polymeric chains characterized by a single glass transition temperature which comprises providing at least two types of chemically dissimilar polymers which do not contain ionizable groups and which are crosslinkable by different crosslinking mechanisms using polymer specific crosslinking agents, forming an intimate admixture of said types of chemically dissimilar polymers, and crosslinking with polymer specific crosslinking agents polymers of the same type to each other, at least one of which is crosslinked while in intimate admixture with the other, thereby producing separate macrocyclic structures of said chemically dissimilar polymers having substantially no intermolecular chemical bonding therebetween but being threaded through each other in an interpenetrating polymeric network.
Claim 25
Independent Claim
126 words
A method for the production of synthetic resin of two or more polymers having an interpenetrating polymeric network of polymeric chains characterized by a single glass transition temperature which comprises providing at least two types of chemically dissimilar polymers which do not contain ionizable groups and which are crosslinkable by different crosslinking mechanisms using polymer specific crosslinking agents, forming an intimate admixture of said types of chemically dissimilar polymers, and crosslinking with polymer specific crosslinking agents polymers of the same type to each other, at least one of which is crosslinked while in intimate admixture with the other, thereby producing separate macrocyclic structures of said chemically dissimilar polymers having substantially no intermolecular chemical bonding therebetween but being threaded through each other in an interpenetrating polymeric network.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-23 | 1985-05-25 | 1985-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-23 | 1989-05-25 | 1989-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-23 | 1993-05-25 | 1993-11-24 | $7700.00 | Window Closed / Lapsed |