Abstract The invention relates to a blend, based on polystyrene and/or impact resistant polystyrene, which is stress-corrosion, impact and cold resistant and flame retardant. The blend according to the invention contains 50 to 98 mass % of polystyrene or impact resistant polystyrene, 0.01 to 15 mass % of zeolites with a pore size above 0.43 nm, 2 to 18 mass % of a styrene/butadiene block copolymer, 0 to 15 mass % of a flame retardant and 0 to 2 mass % of a surface-active agent. The properties of the blend can be adjusted between wide limits by a suitable selection of the quality and quantity of the components. The blend can be prepared by the processors themselves, whereby the selection of the available polystyrene types can be considerably increased.
A freon-corrosion, impact and cold resistant and flame-retardant polystyrene blend, comprising 50 to 98 mass % of polystyrene or impact resistant polystyrene, 0.01 to 15 mass % of zeolites with a pore size above 0.43 nm, 2 to 18 mass % of a styrene/butadiene block copolymer, 0 to 15 mass % of a flame retardant and 0 to 2 mass % of a surface-active agent, wherein the zeolites contain a cation of Mg--, Co--, Sb-- or Mo--, such cation being introduced into the zeolite by ion exchange.
Claim 2
Dependent Claim
87 words
A freon-corrosion, impact and cold resistant and flame-retardant polystyrene blend, comprising 50 to 98 mass % of polystyrene or impact resistant polystyrene, 0.01 to 15 mass % of zeolites with a pore size above 0.43 nm, 2 to 18 mass % of a styrene/butadiene block copolymer, 0 to 15 mass % of a flame retardant and 0 to 2 mass % of a surface-active agent, wherein the zeolites contain a cation of Mg--, Co--, Sb-- or Mo--, such cation being introduced into the zeolite by ion exchange.
Claim 3
Dependent Claim
40 words
A blend as claimed in claim 1, comprising 80 to 97 mass % of polystyrene, 0.02 to 10 mass % of zeolites of a pore size above 0.43 nm and 2.5 to 10 mass % of a styrene/butadiene block copolymer.
Claim 4
Dependent Claim
33 words
A composition as claimed in claim 1, comprising 86 to 96 mass % of polystyrene, 0.05 to 5 mass % of zeolites and 3 to 9 mass % of a styrene/butadiene block copolymer.
Claim 5
Dependent Claim
26 words
A blend as claimed in claim 1, wherein the styrene content in block form of the styrene/butadiene block copolymer amounts to at least 25 mass %.