Method of making novel rubbery block copolymers and pressure-sensitive adhesives
Assignee: Phillips Petroleum Co
•
Filing: 1977-06-23
•
Granted: 1979-04-10
•
Expires: 1997-06-23
Abstract
Abstract Rubbery coupled conjugated diene/monovinyl-substituted aromatic hydrocarbon teleblock copolymers are prepared by incremental addition of both monovinyl-substituted aromatic hydrocarbon and initiator. The resulting copolymers can be used to produce improved pressure-sensitive adhesives.
Inventors
- 👤 Larry L. Nash
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:20
CPC Classifications
C; C08; C08G; C08G81/00; C08G81/02; C08G81/021; C08G81/022; C09; C09J; C09J153/00; C09J153/02; C08L; C08L2666/00; C08L2666/02; Y; Y10; Y10S; Y10S525/00; Y10S525/901
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
159 words
An adhesive composition comprising about 100 parts by weight of a rubbery teleblock copolymer, about 40 to 150 parts by weight of tackifier, about 0 to 100 parts by weight of plasticizer, and about 0.1 to 5 parts by weight of stabilizer, wherein said rubbery teleblock copolymer is prepared by: (a) polymerizing an initial portion of monovinyl-substituted aromatic hydrocarbon in the presence of an initial portion of an organomonolithium polymerization initiator to form an initial living polymer mixture, (b) adding sequentially to said initial living polymer mixture at least one further portion of monovinyl-substituted aromatic hydrocarbon and at least one further portion of organomonolithium initiator and letting each further portion of monovinyl-substituted aromatic hydrocarbon polymerize such as to form a further living polymer mixture, (c) adding conjugated diene to said further living polymer mixture and letting said conjugated diene polymerize such as to form a living polymer, and (d) coupling said living polymer to form said rubbery teleblock copolymer.
Claim 2
Dependent Claim
159 words
An adhesive composition comprising about 100 parts by weight of a rubbery teleblock copolymer, about 40 to 150 parts by weight of tackifier, about 0 to 100 parts by weight of plasticizer, and about 0.1 to 5 parts by weight of stabilizer, wherein said rubbery teleblock copolymer is prepared by: (a) polymerizing an initial portion of monovinyl-substituted aromatic hydrocarbon in the presence of an initial portion of an organomonolithium polymerization initiator to form an initial living polymer mixture, (b) adding sequentially to said initial living polymer mixture at least one further portion of monovinyl-substituted aromatic hydrocarbon and at least one further portion of organomonolithium initiator and letting each further portion of monovinyl-substituted aromatic hydrocarbon polymerize such as to form a further living polymer mixture, (c) adding conjugated diene to said further living polymer mixture and letting said conjugated diene polymerize such as to form a living polymer, and (d) coupling said living polymer to form said rubbery teleblock copolymer.
Claim 3
Dependent Claim
21 words
An adhesive composition according to claim 1 wherein said conjugated diene is butadiene and wherein said monovinyl-substituted aromatic hydrocarbon is styrene.
Claim 4
Dependent Claim
27 words
An adhesive composition according to claim 2 wherein the total number of portions of styrene is 2 and the total number of portions of initiator is 2.
Claim 5
Dependent Claim
53 words
An adhesive composition according to claim 3 wherein about 10 to about 90 percent of the total styrene in the rubbery teleblock copolymer is said initial portion of styrene and about 10 to about 90 percent of the total initiator used to form said rubbery teleblock copolymer is said initial portion of initiator.
Claim 6
Dependent Claim
53 words
An adhesive composition according to claim 3 wherein about 25 to about 75 percent of the total styrene in the rubbery teleblock copolymer is said initial portion of styrene and about 20 to about 45 percent of the total initiator used to form said rubbery teleblock copolymer is said initial portion of initiator.
Claim 7
Dependent Claim
18 words
An adhesive composition according to claim 1 wherein polymerization takes place in the presence of a hydrocarbon diluent.
Claim 8
Dependent Claim
22 words
An adhesive composition according to claim 6 wherein a small amount of a polar compound is initially added to said hydrocarbon diluent.
Claim 9
Dependent Claim
13 words
An adhesive composition according to claim 7 wherein said polar compound is tetrahydrofuran.
Claim 10
Dependent Claim
13 words
An adhesive composition according to claim 8 wherein said organomonolithium initiator is N-butyllithium.
Claim 11
Dependent Claim
22 words
An adhesive composition according to claim 1 wherein a coupling agent having 3 or more reactive sites is used in step (d).
Claim 12
Dependent Claim
17 words
An adhesive composition according to claim 2 wherein the weight ratio of butadiene:total styrene is about 80:20.
Claim 13
Dependent Claim
118 words
An adhesive composition comprising about 100 parts by weight of a rubbery teleblock copolymer, about 40 to 150 parts by weight of tackifier, about 0 to 100 parts by weight of plasticizer, and about 0.1 to 5 parts by weight of stabilizer, wherein said rubbery teleblock copolymer is represented by the general formula (S--D).sub.x Y wherein S represents a block of polymerized monovinyl-substituted aromatic hydrocarbon molecules, D represents a block of polymerized conjugated diene molecules, Y represents the residue of a polyfunctional coupling agent, x is an integer of at least 2, and wherein the heterogeneity index of the monovinyl-substituted aromatic hydrocarbon portion S of the copolymer is substantially larger than the heterogeneity index of the total copolymer.
Claim 14
Dependent Claim
118 words
An adhesive composition comprising about 100 parts by weight of a rubbery teleblock copolymer, about 40 to 150 parts by weight of tackifier, about 0 to 100 parts by weight of plasticizer, and about 0.1 to 5 parts by weight of stabilizer, wherein said rubbery teleblock copolymer is represented by the general formula (S--D).sub.x Y wherein S represents a block of polymerized monovinyl-substituted aromatic hydrocarbon molecules, D represents a block of polymerized conjugated diene molecules, Y represents the residue of a polyfunctional coupling agent, x is an integer of at least 2, and wherein the heterogeneity index of the monovinyl-substituted aromatic hydrocarbon portion S of the copolymer is substantially larger than the heterogeneity index of the total copolymer.
Claim 15
Dependent Claim
41 words
An adhesive composition according to claim 12 wherein the heterogeneity index of the monovinyl-substituted aromatic hydrocarbon portion S of the copolymer is in the range from about 1.4 to about 2.0, whereas the heterogeneity index of the total copolymer is regular.
Claim 16
Dependent Claim
19 words
An adhesive composition according to claim 13 wherein S is a styrene block and D is a butadiene block.
Claim 17
Dependent Claim
14 words
An article of manufacture to which the adhesive according to claim 1 is adhering.
Claim 18
Dependent Claim
14 words
An article of manufacture to which the adhesive according to claim 12 is adhering.
Claim 19
Dependent Claim
26 words
An adhesive composition according to claim 1 wherein the weight ratio of conjugated diene:monovinyl-substituted aromatic hydrocarbon is in the range from about 90:10 to about 60:40.
Claim 20
Dependent Claim
26 words
An adhesive composition according to claim 12 wherein the weight ratio of conjugated diene:monovinyl-substituted aromatic hydrocarbon is in the range from about 90:10 to about 60:40.
References Cited (Backward Citations)
US3281383A
Cited
US3637554A
Cited
US3639517A
Cited
US3658740A
Cited
US3753936A
Cited
CA997889A
Cited
US3950291A
Cited
US3993613A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-04-09 | 1982-10-09 | 1983-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-04-09 | 1986-10-09 | 1987-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-04-09 | 1990-10-09 | 1991-04-10 | $7700.00 | Window Closed / Lapsed |