Abstract
Abstract A method for manufacturing a semiconductor device of a type in which a semiconductor element is formed on an insulating substrate. After ions which break the regularity of the crystal lattice of a monocrystalline semiconductor layer formed on the insulating substrate are implanted to form an amorphous semiconductor layer in part of the monocrystalline semiconductor layer, and after an impurity is doped in the semiconductor layer, a single annealing process is performed to recrystallize the amorphous semiconductor layer and at the same time to activate the doped impurity.
Inventors
- 👤 Kenji Maeguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:31
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2921; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/38; H10P14/3802; H10P14/3822; H10P30/208; H10P30/21; H10P30/212; H10P30/28; H10P95/00; H10P95/90; Y; Y10; Y10S; Y10S148/00; Y10S148/091; Y10S148/093
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
112 words
A method for manufacturing a semiconductor device, comprising the steps of: forming a monocrystalline semiconductor layer on an insulating substrate; implanting ions for breaking the regularity of the crystal lattice of said monocrystalline semiconductor layer into said monocrystalline semiconductor layer to form an amorphous layer in part of said monocrystalline semiconductor layer along a direction of thickness thereof; doping an impurity in said amorphous layer and a remaining portion of said monocrystalline semiconductor layer; and annealing the structure thus obtained, whereby activation of said first impurity and recrystallization of said amorphous layer by solid phase growth using said remaining portion of said monocrystalline semiconductor layer as a seed crystal are simultaneously performed.
Claim 2
Independent Claim
112 words
A method for manufacturing a semiconductor device, comprising the steps of: forming a monocrystalline semiconductor layer on an insulating substrate; implanting ions for breaking the regularity of the crystal lattice of said monocrystalline semiconductor layer into said monocrystalline semiconductor layer to form an amorphous layer in part of said monocrystalline semiconductor layer along a direction of thickness thereof; doping an impurity in said amorphous layer and a remaining portion of said monocrystalline semiconductor layer; and annealing the structure thus obtained, whereby activation of said first impurity and recrystallization of said amorphous layer by solid phase growth using said remaining portion of said monocrystalline semiconductor layer as a seed crystal are simultaneously performed.
Claim 3
Dependent Claim
26 words
The method according to claim 1, wherein said amorphous layer is formed in a portion of said monocrystalline semiconductor layer except for the surface portion thereof.
Claim 4
Dependent Claim
22 words
The method according to claim 1, wherein said amorphous semiconductor layer is formed in the surface portion of said monocrystalline semiconductor layer.
Claim 5
Dependent Claim
16 words
The method according to claim 1, wherein said impurity is doped by means of ion implantation.
Claim 6
Dependent Claim
13 words
The method according to claim 4, wherein said impurity is As + ions.
Claim 7
Independent Claim
23 words
The method according to one of claims 1 to 5, wherein said annealing is performed at a temperature of 700° to 1,000° C.
Claim 8
Independent Claim
181 words
A method for manufacturing a metal oxide semiconductor device, comprising the steps of: forming a monocrystalline semiconductor layer on an insulating substrate; forming an oxide layer on said monocrystalline semiconductor layer; doping ions for breaking the regularity of the crystal lattice of said monocrystalline semiconductor layer through said oxide layer into said monocrystalline semiconductor layer to form an amorphous semiconductor layer in part of said monocrystalline semiconductor layer along a direction of thickness thereof; forming a gate electrode on part of said oxide layer; doping a first impurity in said amorphous semiconductor layer and a remaining portion of said monocrystalline semiconductor layer using said gate electrode as a mask; annealing the structure thus obtained, whereby activation of said first impurity and recrystallization of said amorphous semiconductor layer by solid phase growth using said remaining portion of said monocrystalline semiconductor layer as a seed crystal are simultaneously performed; and selectively removing said oxide layer which contacts an impurity region formed by said activation of said first impurity to expose the impurity region, and forming an electrode which contacts said exposed impurity region.
Claim 9
Independent Claim
181 words
A method for manufacturing a metal oxide semiconductor device, comprising the steps of: forming a monocrystalline semiconductor layer on an insulating substrate; forming an oxide layer on said monocrystalline semiconductor layer; doping ions for breaking the regularity of the crystal lattice of said monocrystalline semiconductor layer through said oxide layer into said monocrystalline semiconductor layer to form an amorphous semiconductor layer in part of said monocrystalline semiconductor layer along a direction of thickness thereof; forming a gate electrode on part of said oxide layer; doping a first impurity in said amorphous semiconductor layer and a remaining portion of said monocrystalline semiconductor layer using said gate electrode as a mask; annealing the structure thus obtained, whereby activation of said first impurity and recrystallization of said amorphous semiconductor layer by solid phase growth using said remaining portion of said monocrystalline semiconductor layer as a seed crystal are simultaneously performed; and selectively removing said oxide layer which contacts an impurity region formed by said activation of said first impurity to expose the impurity region, and forming an electrode which contacts said exposed impurity region.
Claim 10
Dependent Claim
49 words
The method according to claim 7, further comprising the step of implanting a second impurity which has a conductivity type opposite to the conductivity type of said first impurity into said amorphous semiconductor layer and said remaining portion of said monocrystalline semiconductor layer, before said gate electrode is formed.
Claim 11
Dependent Claim
22 words
The method according to claim 8, wherein said first impurity is As + ions, and said second impurity is B + ions.
Claim 12
Dependent Claim
25 words
The method according to claim 9, wherein said B + ions are doped to have a concentration peak in the vicinity of said insulating substrate.
Claim 13
Dependent Claim
27 words
The method according to claim 7, wherein said amorphous semiconductor layer is formed in a portion of said monocrystalline semiconductor layer except for the surface portion thereof.
Claim 14
Dependent Claim
22 words
The method according to claim 7, wherein said amorphous semiconductor layer is formed in the surface portion of said monocrystalline semiconductor layer.
Claim 15
Independent Claim
23 words
The method according to one of claims 7 to 12, wherein said annealing is performed at a temperature of 700° to 1,000° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-07 | 1988-02-06 | 1988-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-07 | 1992-02-06 | 1992-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-07 | 1996-02-06 | 1996-08-07 | $7700.00 | Window Closed / Lapsed |