Superconducting circuit fabrication
Assignee: Unisys Corp
•
Filing: 1982-01-28
•
Granted: 1984-06-26
•
Expires: 2002-01-28
Abstract
Abstract An improved method of anodization of thin films for the fabrication of superconducting devices. An electrically conducting contact layer is formed over a substrate between an electrically conducting object layer and the substrate. Also, an electrically insulating layer is formed between the object layer and the contact layer. The contact layer is connected to a power supply and at least a preselected portion of the object layer is anodized to a predetermined thickness. This may include anodizing all of some preselected portions through the complete thickness of the object layer. A pattern of hardened photoresist on the object layer provides portions not protected by the pattern. When anodization of the electrically conducting object layer takes place, the resulting anodized portion is thicker than the thickness of the portion of the object layer that it replaces. The present invention further includes reducing the preselected portion of the object layer to be anodized by a predetermined amount before anodizing so that when anodization is complete, the resulting partially anodized partially conducting object layer is substantially planar. Alternatively, the thickness of the anodized preselected portions can be reduced after anodizing by a predetermined amount to cause the layer to be substantially planar. The same pattern of hardened photoresist can be used when reducing the thickness of portions of the object layer or anodized preselected portions.
Inventors
- 👤 Barry F. Stein
- 👤 Peter L. Young
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:39
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/022; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0912
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
76 words
A method of anodizing at least a preselected portion of at least one electrically conducting layer disposed over a substrate comprising: forming an electrically conducting contact layer over said substrate; forming an electrically insulating layer over said contact layer; forming said at least one electrically conducting layer over said insulating layer; electrically coupling said contact layer to the positive terminal of an anodizing power source; anodizing said at least one conducting layer to a predetermined thickness.
Claim 2
Independent Claim
76 words
A method of anodizing at least a preselected portion of at least one electrically conducting layer disposed over a substrate comprising: forming an electrically conducting contact layer over said substrate; forming an electrically insulating layer over said contact layer; forming said at least one electrically conducting layer over said insulating layer; electrically coupling said contact layer to the positive terminal of an anodizing power source; anodizing said at least one conducting layer to a predetermined thickness.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the step of anodizing comprises anodizing said at least one conducting layer through the entire thickness of said conducting layer.
Claim 4
Dependent Claim
56 words
The method of claim 2 wherein: the step of forming said contact layer comprises vacuum deposition of said contact layer on said substrate; the step of forming an electrical insulation layer comprises uniformly anodizing said contact layer to a predetermined thickness of said contact layer; and said conducting layer is vacuum deposited on said insulation layer.
Claim 5
Dependent Claim
66 words
The method of claim 1 wherein said method further comprises, after the step of forming said at least one electrically conducting layer, the step of forming a pattern of protective material on said at least one electrically conducting layer whereby only a preselected portion of said at least one electrically conducting layer not protected by said pattern of protective material is anodized during said anodizing step.
Claim 6
Dependent Claim
47 words
The method of claim 4 wherein said method further comprises the step of: reducing the thickness of said at least a preselected portion of said at least one conducting layer before the step of anodizing whereby a substantially planar partially anodized conducting layer is formed after anodization.
Claim 7
Dependent Claim
45 words
The method of claim 2,3 or 4 wherein said method further comprises the step of: reducing the thickness of the anodized preselected portion of said at least one conducting layer after the step of anodizing whereby a substantially planar partially anodized conducting layer is formed.
Claim 8
Dependent Claim
17 words
The method of claim 5 wherein the step of reducing comprises the step of ion beam etching.
Claim 9
Dependent Claim
17 words
The method of claim 6 wherein the step of reducing comprises the step of ion beam etching.
Claim 10
Dependent Claim
40 words
The method of claim 1 or 2 wherein there are more than one electrically conducting layer formed over said substrate and said method further comprises anodizing at least a preselected portion of each of said conducting layers to be anodized.
Claim 11
Dependent Claim
22 words
The method of claim 1 wherein said contact layer and said at least one conducting layer comprises a material having superconducting properties.
Claim 12
Dependent Claim
10 words
The method of claim 9 wherein said material is niobium.
Claim 13
Independent Claim
76 words
A method of obtaining a planar surface comprising: adding photoresist to a planar conductor whereby an area of said conductor is protected from action by further steps; etching part of the thickness of said conductor in unprotected areas to a predetermined thickness; anodizing said etched and unprotected areas of said conductor throughout the thickness thereof and until the thickness of the anodized areas substantially equal the thickness of the protected conducting areas; and removing said photoresist.
Claim 14
Independent Claim
76 words
A method of obtaining a planar surface comprising: adding photoresist to a planar conductor whereby an area of said conductor is protected from action by further steps; etching part of the thickness of said conductor in unprotected areas to a predetermined thickness; anodizing said etched and unprotected areas of said conductor throughout the thickness thereof and until the thickness of the anodized areas substantially equal the thickness of the protected conducting areas; and removing said photoresist.
Claim 15
Independent Claim
68 words
A method of obtaining a planar surface comprising: adding photoresist to a planar conductor whereby an area of said conductor is protected from the action of further steps; anodizing the unprotected area of said conductor throughout the entire thickness thereof; etching part of said anodized areas until the thickness of said anodized area substantially equals the area of the protected area of said conductor; and removing said photoresist.
Claim 16
Independent Claim
68 words
A method of obtaining a planar surface comprising: adding photoresist to a planar conductor whereby an area of said conductor is protected from the action of further steps; anodizing the unprotected area of said conductor throughout the entire thickness thereof; etching part of said anodized areas until the thickness of said anodized area substantially equals the area of the protected area of said conductor; and removing said photoresist.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |