Assignee: Corning Glass Works
•
Filing: 1982-07-26
•
Granted: 1984-06-12
•
Expires: 2002-07-26
Abstract
Abstract A glass optical waveguide preform is formed by depositing first and second coatings of glass soot on a mandrel. The characteristics of the first coating are such that it can ultimately form the core of an optical fiber. The core-clad diameter ratio of the preform is greater than that necessary to provide the desired core-clad diameter ratio of the resultant fiber. The mandrel is removed and the porous preform is consolidated. The preform aperture is etched, rinsed and dried. One end of the preform is heated and pinched to close the aperture. The aperture is evacuated, and the remaining end of the preform is heated, the corresponding end of the aperture being caused to close. An intermediate fiber is drawn from the resultant consolidated preform, the entire aperture being closed during drawing due to the low pressure within the aperture. The intermediate fiber is severed into sections, each of which functions as a mandrel for the deposition of a further coating of cladding soot. The resultant composite article is consolidated and drawn into an optical fiber.
Inventors
- 👤 George E. Berkey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:03
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01486; C03B37/01493; C03B37/01466; C03B37/01473; C03B2203/00; C03B2203/10; C03B2203/18; C03B2203/20
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
97 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying at least one coating of particulate glass to the outside peripheral surface of said mandrel, removing said mandrel to form a porous preform having an aperture therein, heating said porous preform to form an elongated, consolidated glass preform having a longitudinal aperture therethrough, closing one end of said aperture, evacuating said aperture, and closing the remaining end of said aperture, the entire expanse of said aperture between said ends remaining open to form the high purity glass article.
Claim 2
Independent Claim
97 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying at least one coating of particulate glass to the outside peripheral surface of said mandrel, removing said mandrel to form a porous preform having an aperture therein, heating said porous preform to form an elongated, consolidated glass preform having a longitudinal aperture therethrough, closing one end of said aperture, evacuating said aperture, and closing the remaining end of said aperture, the entire expanse of said aperture between said ends remaining open to form the high purity glass article.
Claim 3
Dependent Claim
36 words
The method of claim 1 wherein, prior to the step of closing one end of said aperture, said method includes the step of removing the surface portion of the aperture forming wall of said consolidated preform.
Claim 4
Dependent Claim
28 words
The method of claim 2 wherein the step of removing comprises etching and rinsing the surface of said aperture-forming wall, and flowing a drying gas through said aperture.
Claim 5
Dependent Claim
35 words
The method of claim 3 further comprising the steps of heating at least one end of said formed glass article and drawing to close said aperture and reduce the diameter of said formed glass article.
Claim 6
Dependent Claim
48 words
The method of claim 4 wherein the step of drawing is characterized in that it comprises drawing an intermediate, large diameter fiber, said method further comprising the step of adding cladding material to said intermediate fiber and drawing the resultant composite article to form an optical waveguide fiber.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein the step of adding cladding material comprises inserting said intermediate fiber into a tube of cladding glass.
Claim 8
Dependent Claim
62 words
The method of claim 4 wherein the step of drawing comprises drawing said formed glass articles to an intermediate fiber having a thickness sufficient that it can be employed as a mandrel upon which particulate glass can be deposited, said method further comprising the steps of depositing a layer of particulate cladding glass on at least a portion of said intermediate fiber.
Claim 9
Dependent Claim
61 words
The method of claim 7 wherein the step of drawing to form an optical waveguide fiber comprises heating the composite article comprising at least a portion of said intermediate fiber and said layer of particulate cladding glass to simultaneously consolidate said particulate cladding glass and reduce the diameter of the combination of said intermediate fiber and the consolidated cladding glass thereon.
Claim 10
Dependent Claim
52 words
The method of claim 1 wherein, during the step of heating, said one end becomes closed, said method further comprising the steps of severing said closed end and removing the surface portion of the aperture forming wall of said consolidated preform prior to the step of closing one end of said aperture.
Claim 11
Dependent Claim
46 words
The method of claim 1 wherein, prior to the step of heating, said method comprises inserting a capilliary tube into one end of said aperture and flowing a drying gas into the remaining end of said aperture, said capilliary tube closing during the step of heating.
Claim 12
Dependent Claim
37 words
The method of claim 10 further comprising the step of severing the end of said preform containing said closed capilliary tube, etching and rinsing the surface of said aperture-forming wall and flowing drying gas through said aperture.
Claim 13
Independent Claim
217 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying to said mandrel a stratum of particulate glass having a relatively low coefficient of expansion, applying a first coating of particulate glass to the outside peripheral surface of said stratum, the coefficient of expansion of said first coating being greater than that of said stratum, applying a second coating of particulate glass over the outside peripheral surface of said first coating, said second coating having a refractive index less than that of said first coating, removing said mandrel to form a porous preform having an aperture therein, heating said porous preform to form an elongated, consolidated glass preform having a longitudinal aperture therethrough, etching a surface portion of said stratum glass from the aperture-forming wall of said consolidated preform, rinsing the aperture-forming wall of said preform, flowing a drying gas through said aperture, closing one end of said aperture, evacuating said aperture, closing the remaining end of said aperture, heating at least one end of said consolidated preform and drawing to close said aperture and reduce the diameter of said consolidated preform, thereby forming a large diameter, intermediate fiber, adding cladding material to said intermediate fiber, and drawing the composite article so formed into an optical waveguide fiber.
Claim 14
Independent Claim
217 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying to said mandrel a stratum of particulate glass having a relatively low coefficient of expansion, applying a first coating of particulate glass to the outside peripheral surface of said stratum, the coefficient of expansion of said first coating being greater than that of said stratum, applying a second coating of particulate glass over the outside peripheral surface of said first coating, said second coating having a refractive index less than that of said first coating, removing said mandrel to form a porous preform having an aperture therein, heating said porous preform to form an elongated, consolidated glass preform having a longitudinal aperture therethrough, etching a surface portion of said stratum glass from the aperture-forming wall of said consolidated preform, rinsing the aperture-forming wall of said preform, flowing a drying gas through said aperture, closing one end of said aperture, evacuating said aperture, closing the remaining end of said aperture, heating at least one end of said consolidated preform and drawing to close said aperture and reduce the diameter of said consolidated preform, thereby forming a large diameter, intermediate fiber, adding cladding material to said intermediate fiber, and drawing the composite article so formed into an optical waveguide fiber.
Claim 15
Dependent Claim
44 words
The method of claim 12 wherein the step of adding cladding material comprises depositing a layer of particulate cladding glass on at least a portion of said intermediate fiber, and consolidating said layer of particulate cladding glass on the surface of said intermediate fiber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |