Abstract
Abstract A method of making solid glass articles by the flame hydrolysis technique. A thin stratum of low viscosity glass soot is applied to the surface of a mandrel. First and second coatings of glass soot are deposited on the surface of the thin stratum to form a porous preform. The refractive index of the soot particles of the first coating is greater than that of the soot of the second coating, and the soot of the first coating has a viscosity lower than that of the second coating. The mandrel is removed, and the soot preform is subjected to a high temperature whereby it is consolidated to form a dense glass blank. The glass surface tension and the relative viscosities of the inner and outer portions of the preform cause the aperture to close during the consolidation process. The thin stratum, which preferably includes P 2 O 5 , smoothes over the damage caused by removing the mandrel and reduces or even eliminates seed formation at the axis of the resultant glass blank. The blank may be heated and drawn into a filament, or it may be sliced into optical windows, lenses or the like.
Inventors
- 👤 Alan C. Bailey
- 👤 Alan J. Morrow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 11:14
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/036; G02B6/03605; G02B6/03611; C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03B37/01446; G02B6/028; G02B6/0281; C03B2201/00; C03B2201/02; C03B2201/06; C03B2201/20; C03B2201/28; C03B2201/30; C03B2201/31; C03B2203/00; C03B2203/10; C03B2203/22; C03B2207/00; C03B2207/80; C03B2207/85; C03B2207/87; G02B6/0288
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
177 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying to said mandrel a stratum of low viscosity glass soot, applying a first coating of glass soot to the outside peripheral surface of said stratum, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, the viscosity of said second coating being greater than that of said first coating and the viscosity of said first coating being greater than that of said stratum at the consolidation temperature of said second coating, removing said mandrel to form a soot preform having an aperture therein, the thickness of said stratum being sufficiently great that a continuous layer of said low viscosity material remains on the inner surface of said first coating after the step of removing said mandrel has been completed, and forming the structure so formed into a desired glass article.
Claim 2
Independent Claim
177 words
A method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying to said mandrel a stratum of low viscosity glass soot, applying a first coating of glass soot to the outside peripheral surface of said stratum, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, the viscosity of said second coating being greater than that of said first coating and the viscosity of said first coating being greater than that of said stratum at the consolidation temperature of said second coating, removing said mandrel to form a soot preform having an aperture therein, the thickness of said stratum being sufficiently great that a continuous layer of said low viscosity material remains on the inner surface of said first coating after the step of removing said mandrel has been completed, and forming the structure so formed into a desired glass article.
Claim 3
Dependent Claim
64 words
A method in accordance with claim 1 wherein the step of forming comprises heating said preform to a sufficiently high temperature for a sufficient period of time to permit the soot at at least one end thereof to consolidate, and simultaneously drawing the consolidated portion of said preform to reduce the cross-sectional area thereof and close said aperture, thereby forming an optical waveguide filament.
Claim 4
Dependent Claim
48 words
A method in accordance with claim 1 wherein the step of forming comprises heating said preform to a sufficiently high temperature for a sufficient period of time to permit said stratum and said first and second soot coatings to consolidate and to permit said aperture to simultaneously close.
Claim 5
Dependent Claim
31 words
A method in accordance with claim 1 wherein the viscosity of said stratum is less than 1/10 the viscosity of said first coating at the consolidation temperature of said second coating.
Claim 6
Dependent Claim
184 words
In a method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, removing said mandrel to form a soot preform having an aperture therein, heating said preform to a sufficiently high temperature for a sufficient period of time to permit said first and second soot coatings to consolidate and to permit said aperture to close, and forming the structure so formed into a desired glass article, the improvement comprising: applying to said mandrel prior to the application of said first coating a stratum of low viscosity glass soot, the thickness of said stratum being sufficiently great that a continuous layer of said low viscosity material remains on the inner surface of said first coating after the step of removing said mandrel has been completed.
Claim 7
Dependent Claim
184 words
In a method of forming a high purity glass article comprising the steps of providing a substantially cylindrical mandrel, applying a first coating of glass soot to the outside peripheral surface of said mandrel, applying a second coating of glass soot over the outside peripheral surface of said first coating, the glass soot of said second coating having a refractive index less than that of the glass soot of the first coating, removing said mandrel to form a soot preform having an aperture therein, heating said preform to a sufficiently high temperature for a sufficient period of time to permit said first and second soot coatings to consolidate and to permit said aperture to close, and forming the structure so formed into a desired glass article, the improvement comprising: applying to said mandrel prior to the application of said first coating a stratum of low viscosity glass soot, the thickness of said stratum being sufficiently great that a continuous layer of said low viscosity material remains on the inner surface of said first coating after the step of removing said mandrel has been completed.
Claim 8
Dependent Claim
19 words
A method in accordance with claim 5 wherein the thickness of said soot stratum is at least 0.15 mm.
Claim 9
Dependent Claim
24 words
A method in accordance with claim 6 wherein said stratum contains at least 7 wt. % P 2 O 5 as the viscosity-depressing component.
Claim 10
Dependent Claim
27 words
A method in accordance with claim 7 wherein, prior to the step of applying said stratum, a coating of soft, release material is applied to said mandrel.
Claim 11
Dependent Claim
20 words
A method in accordance with claim 7 wherein said stratum is formed on a soot having a binary glass composition.
Claim 12
Dependent Claim
20 words
A method in accordance with claim 7 wherein said stratum is formed of a soot having a ternary glass composition.
Claim 13
Dependent Claim
35 words
A method in accordance with claim 6 wherein the step of heating said preform to permit said coatings to consolidate and to permit said aperture to close comprises heating said preform in a helium-rich atmosphere.
Claim 14
Dependent Claim
43 words
A method in accordance with claim 5 wherein the step of forming comprises heating the structure so formed to the drawing temperature of the materials thereof, and drawing the heated structure to reduce the cross-sectional area thereof, thereby forming an optical waveguide fiber.
Claim 15
Dependent Claim
46 words
A method in accordance with claim 5 wherein, during the step of heating said preform to permit said coatings to consolidate and to permit said aperture to close, a drying gas mixture is flowed into said preform aperture and outwardly through the interstices of said preform.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-02 | 1985-05-04 | 1985-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-02 | 1989-05-04 | 1989-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-02 | 1993-05-04 | 1993-11-03 | $7700.00 | Window Closed / Lapsed |