Assignee: Goodrich Corp
•
Filing: 1983-01-24
•
Granted: 1984-05-29
•
Expires: 2003-01-24
Abstract
Abstract A heterogeneous rubber composition having improved flex crack growth resistance and heat buildup is made by blending together separate fractions of chemically similar rubber compounds and ingredients such as carbon black.
Inventors
- 👤 Biing-Lin Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:21
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/203; C08J2321/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
245 words
A process for making a crack growth resistant rubber composition, comprising the steps of: (a) forming a heterogeneous rubber composition comprising by weight approximately 100 total parts of a rubber, and from about 60 to about 95 total parts of a carbon black, said rubber composition formed by (b) separately forming a minor fraction comprising one or more rubber compounds, and carbon black, said rubber compound selected from the group consisting of nitrile rubber, a polymer made from a conjugated diene having from 4 to 12 carbon atoms, and a copolymer made from monomers selected from the group consisting of conjugated dienes having from 4 to 12 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, said minor fraction containing from about 10 to about 50 parts by weight of said rubber, and an amount of carbon black ranging from about 2.5 parts by weight to about 37.5 parts by weight; (c) separately forming a major fraction comprising an identical one or more rubber compounds and a similar carbon black as in said minor fraction, said major fraction having a range of said rubber ranging from about 50 to about 90 parts by weight and an amount of said carbon black ranging from about 22.5 to about 92.5 parts by weight; (d) separately mixing and heating at least one of said fractions; and (e) mixing together under heat said major fraction and said minor fraction to produce said heterogeneous rubber composition.
Claim 2
Dependent Claim
245 words
A process for making a crack growth resistant rubber composition, comprising the steps of: (a) forming a heterogeneous rubber composition comprising by weight approximately 100 total parts of a rubber, and from about 60 to about 95 total parts of a carbon black, said rubber composition formed by (b) separately forming a minor fraction comprising one or more rubber compounds, and carbon black, said rubber compound selected from the group consisting of nitrile rubber, a polymer made from a conjugated diene having from 4 to 12 carbon atoms, and a copolymer made from monomers selected from the group consisting of conjugated dienes having from 4 to 12 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, said minor fraction containing from about 10 to about 50 parts by weight of said rubber, and an amount of carbon black ranging from about 2.5 parts by weight to about 37.5 parts by weight; (c) separately forming a major fraction comprising an identical one or more rubber compounds and a similar carbon black as in said minor fraction, said major fraction having a range of said rubber ranging from about 50 to about 90 parts by weight and an amount of said carbon black ranging from about 22.5 to about 92.5 parts by weight; (d) separately mixing and heating at least one of said fractions; and (e) mixing together under heat said major fraction and said minor fraction to produce said heterogeneous rubber composition.
Claim 3
Dependent Claim
82 words
A process according to claim 1, wherein in said minor fraction the amount of said rubber ranges from about 20 to about 45 parts by weight, and wherein the amount of said carbon black ranges from about 5 to about 34 parts by weight, and wherein in said major fraction said amount of rubber ranges from about 55 to about 80 parts by weight and wherein the amount of said carbon black ranges from about 41 to about 85 parts by weight.
Claim 4
Dependent Claim
32 words
A process according to claim 2, wherein said rubber in said major fraction and said minor fraction is selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene, cis-polybutadiene, and styrene-butadiene rubber.
Claim 5
Dependent Claim
33 words
A process according to claim 3, including mixing under heat said major fraction components, adding said minor fraction components to said major fraction, and mixing under heat to produce said heterogeneous rubber composition.
Claim 6
Dependent Claim
38 words
A process according to claim 3, including separately mixing under heat said major fraction components, separately mixing under heat said minor fraction components, adding said mixed major fraction and said mixed minor fraction together and mixing under heat.
Claim 7
Dependent Claim
100 words
A process according to claim 4, and including at least another rubber in said major fraction and including at least a similar rubber in said minor fraction, wherein in said minor fraction said amount of rubber ranges from about 30 to about 40 parts by weight, and wherein said amount of carbon black ranges from about 7.5 to about 30 parts by weight, and wherein in said major fraction, said amount of rubber ranges from about 60 to about 70 parts by weight and wherein the amount of carbon black ranges from about 55 to about 77.5 parts by weight.
Claim 8
Dependent Claim
100 words
A process according to claim 5, and including at least another rubber in said major fraction and including at least a similar rubber in said minor fraction, wherein in said minor fraction said amount of rubber ranges from about 30 to about 40 parts by weight, and wherein said amount of carbon black ranges from about 7.5 to about 30 parts by weight, and wherein in said major fraction, said amount of rubber ranges from about 60 to about 70 parts by weight and wherein the amount of carbon black ranges from about 55 to about 77.5 parts by weight.
Claim 9
Dependent Claim
82 words
A process according to claim 4, including adding curing agents to said mixed major blend and said minor blend, and mixing, and including mixing said major fraction at a temperature of from about 180° F. to about 350° F., mixing said minor fraction at a temperature of from about 180° F. to about 350° F., and mixing said mixture containing said major blend, said minor blend, and said curing agents at a temperature of from about 130° F. to about 200° F.
Claim 10
Dependent Claim
116 words
A process according to claim 5, including adding curing agents to said mixed major fraction and mixing, including adding curing agents to said mixed minor fraction and mixing, and including separately mixing said major fraction and said minor fraction at a temperature ranging from about 180° F. to about 350° F., separately mixing said curing agents with said major fraction and separately mixing said curing agents with said minor fraction at a temperature of from about 130° F. to about 200° F., and mixing said mixed major fraction having curing agents therein and said mixed minor fraction having curing agents therein with each other at a temperature of from about 130° F. to about 200° F.
Claim 11
Dependent Claim
14 words
A process according to claim 9, including forming an item and curing said item.
Claim 12
Dependent Claim
219 words
A crack growth resistant heterogeneous rubber composition, comprising: a mixed blend of a major fraction and a minor fraction forming said heterogeneous rubber composition, said major fraction and said minor fraction having chemically similar rubber and carbon black therein, said heterogeneous composition comprising by weight approximately 100 total parts of rubber, and from about 60 to about 95 total parts of a carbon black, said minor fraction comprising from about 10 to about 50 parts by weight of one or more rubber compounds and an amount by weight of carbon black ranging from about 2.5 parts to about 37.5 parts by weight, said rubber compound selected from the group consisting of nitrile rubber, a polymer made from a conjugated diene having from 4 to 12 carbon atoms, and a copolymer made from monomers selected from the group consisting of conjugated dienes having from 4 to 12 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, and said major fraction comprising an identical one or more rubber compounds and a similar carbon black as in said minor fraction, said major fraction having an amount of said rubber ranging from about 50 parts to about 90 parts by weight, and said major fraction having a carbon black range by weight of from about 22.5 to about 92.5.
Claim 13
Dependent Claim
219 words
A crack growth resistant heterogeneous rubber composition, comprising: a mixed blend of a major fraction and a minor fraction forming said heterogeneous rubber composition, said major fraction and said minor fraction having chemically similar rubber and carbon black therein, said heterogeneous composition comprising by weight approximately 100 total parts of rubber, and from about 60 to about 95 total parts of a carbon black, said minor fraction comprising from about 10 to about 50 parts by weight of one or more rubber compounds and an amount by weight of carbon black ranging from about 2.5 parts to about 37.5 parts by weight, said rubber compound selected from the group consisting of nitrile rubber, a polymer made from a conjugated diene having from 4 to 12 carbon atoms, and a copolymer made from monomers selected from the group consisting of conjugated dienes having from 4 to 12 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, and said major fraction comprising an identical one or more rubber compounds and a similar carbon black as in said minor fraction, said major fraction having an amount of said rubber ranging from about 50 parts to about 90 parts by weight, and said major fraction having a carbon black range by weight of from about 22.5 to about 92.5.
Claim 14
Dependent Claim
81 words
A crack growth resistant heterogeneous rubber composition according to claim 11, wherein in said major fraction the amount of said rubber is from about 55 to about 80 parts by weight and wherein said carbon black is from about 41 to about 85 parts by weight, and wherein in said minor fraction said amount of rubber is from about 20 to about 45 parts by weight and wherein said carbon black is from about 5 to about 34 parts by weight.
Claim 15
Dependent Claim
38 words
A crack growth resistant heterogeneous rubber composition according to claim 12, wherein said rubber in said major fraction and said minor fraction is selected from the group consisting of natural rubber, synthetic cis-1,4-polyisoprene, cis-polybutadiene, styrene-butadiene rubber, nitrile rubber.
Claim 16
Dependent Claim
101 words
A crack growth resistant heterogeneous rubber composition according to claim 13, and including at least another rubber in said major fraction and including at least a similar rubber in said minor fraction, wherein in said major fraction an amount of rubber is from about 60 to about 70 parts by weight and wherein said carbon black is from about 55 to about 77.5 parts by weight, and wherein in said minor fraction said amount of rubber is from about 30 to about 40 parts by weight and wherein said carbon black is from about 7.5 to about 30 parts by weight.
Claim 17
Dependent Claim
30 words
A crack growth resistant heterogeneous rubber composition according to claim 12, wherein said major fraction is mixed, wherein said minor fraction is added to said major fraction and mixed therewith.
Claim 18
Dependent Claim
36 words
A crack growth resistant heterogeneous rubber composition according to claim 12, wherein said major fraction is separately mixed, wherein said minor fraction is separately mixed, and wherein said fractions are added to each other and mixed.
Claim 19
Dependent Claim
30 words
A crack growth resistant heterogeneous rubber composition according to claim 14, wherein said major fraction is mixed, wherein said minor fraction is added to said major fraction and mixed therewith.
Claim 20
Dependent Claim
36 words
A crack growth resistant heterogeneous rubber composition according to claim 14, wherein said major fraction is separately mixed, wherein said minor fraction is separately mixed, and wherein said fractions are added to each other and mixed.
Claim 21
Dependent Claim
48 words
A crack growth resistant heterogeneous rubber composition according to claim 15, wherein said rubber in said minor fraction is identical to said rubber in said major fraction, and including curing agents in said rubber composition and wherein said rubber composition is in the form of a cured article.
Claim 22
Dependent Claim
48 words
A crack growth resistant heterogeneous rubber composition according to claim 17, wherein said rubber in said minor fraction is identical to said rubber in said major fraction, and including curing agents in said rubber composition and wherein said rubber composition is in the form of a cured article.
References Cited (Backward Citations)
US3294720A
Cited
US3872036A
Cited
US3846371A
Cited
US4222906A
Cited
US4321168A
Cited
US4342670A
Cited
EP0051450A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |