Cutting insert having unique cross section
Assignee: Carboloy Inc
•
Filing: 1981-12-16
•
Granted: 1984-05-15
•
Expires: 2001-12-16
Abstract
Abstract A blank adapted to be mounted on a substrate to form a cutting insert is formed by preparing a crystal dispersion of super-hard crystals, such as diamond or cubic boron nitride crystals, and carbon black in a temporary binder, and a core dispersion of carbon fiber, carbon black and filler in a temporary binder. The crystal dispersion and the core dispersion are placed in a mold to respectively form a core dispersion layer and a crystal dispersion layer which forms a ring about the periphery of the core dispersion layer on the upper surface thereof. The crystal and core dispersion layers are compacted with a chamfered plunger applied to the lower surface of the core layer to form an intermediate composite having a recess at the lower surface thereby compressing the dispersions to a substantially uniform compaction throughout the intermediate composite. The intermediate composite is then heated to allow for the removal of the temporary binder and the infiltration of liquified silicon. The intermediate composite is then sintered to produce the blank, the crystal and core layers being bonded internally and to each other by a matrix of β-silicon carbide and silicon.
Inventors
- 👤 John M. Ohno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:38
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/573; B; B23; B23B; B23B27/00; B23B27/14; B23B27/141; B23B27/145; B23B27/146; B23B27/148; B24; B24D; B24D3/00; B24D3/02; B24D3/04; B24D3/06; C04B35/58; C04B35/583; C04B35/5831; B23B2226/00; B23B2226/72; Y; Y10; Y10T; Y10T407/00; Y10T407/27
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
198 words
A process for producing a blank adapted to be mounted on a substrate to form a cutting insert, comprising the steps of: preparing at least one crystal dispersion of super-hard crystals selected from at least one member of the group consisting of diamond and cubic boron nitride crystals and carbon black in a temporary binder; preparing a core dispersion of carbon fiber, carbon black and filler in a temporary binder; placing said at least one crystal dispersion and said core dispersion in a mold to respectively form at least one crystal dispersion layer and a core dispersion layer, said at least one crystal dispersion layer forming a rim about the periphery of said core dispersion layer on the upper surface thereof; compacting said crystal and core dispersion layers with a chamfered plunger applied to the lower surface of said core layer to form an intermediate composite having a recess at said lower surface, thereby compressing said dispersions to a substantially uniform density throughout said intermediate composite; heating said intermediate composite to allow for the removal of said temporary binder and the infiltration of liquefied silicon into said intermediate composite; and sintering said intermediate composite to produce said blank.
Claim 2
Dependent Claim
198 words
A process for producing a blank adapted to be mounted on a substrate to form a cutting insert, comprising the steps of: preparing at least one crystal dispersion of super-hard crystals selected from at least one member of the group consisting of diamond and cubic boron nitride crystals and carbon black in a temporary binder; preparing a core dispersion of carbon fiber, carbon black and filler in a temporary binder; placing said at least one crystal dispersion and said core dispersion in a mold to respectively form at least one crystal dispersion layer and a core dispersion layer, said at least one crystal dispersion layer forming a rim about the periphery of said core dispersion layer on the upper surface thereof; compacting said crystal and core dispersion layers with a chamfered plunger applied to the lower surface of said core layer to form an intermediate composite having a recess at said lower surface, thereby compressing said dispersions to a substantially uniform density throughout said intermediate composite; heating said intermediate composite to allow for the removal of said temporary binder and the infiltration of liquefied silicon into said intermediate composite; and sintering said intermediate composite to produce said blank.
Claim 3
Dependent Claim
64 words
The process of claim 1 wherein said step of compacting is performed so as to impart a compressional force to at least a part of said at least one crystal dispersion layer having components in directions both parallel to and perpendicular to the direction of motion of said plunger, such that said part of said at least one crystal dispersion layer is tightly compacted.
Claim 4
Dependent Claim
13 words
The process of claim 2 wherein said filler is super fine β-silicon carbide.
Claim 5
Dependent Claim
17 words
The process of claim 2 wherein said intermediate composite is sintered from approximately 30 to 50 minutes.
Claim 6
Dependent Claim
122 words
A blank adapted to be mounted on a substrate to form a cutting insert, comprising; a core of carbon fiber and filler; at least one crystal dispersion of super-hard crystals selected from at least one member from the group consisting of diamond and cubic boron nitride crystals; wherein said core and said at least one crystal dispersion are respectively formed as adjacent layers bonded internally and to each other by a matrix of β-silicon carbide and silicon, said at least one crystal dispersion forming a rim about the periphery of said core on the upper surface thereof, and said core being formed with a chamfered indentation on the lower surface thereof which allows said blank to have a substantially uniform compaction throughout.
Claim 7
Dependent Claim
122 words
A blank adapted to be mounted on a substrate to form a cutting insert, comprising; a core of carbon fiber and filler; at least one crystal dispersion of super-hard crystals selected from at least one member from the group consisting of diamond and cubic boron nitride crystals; wherein said core and said at least one crystal dispersion are respectively formed as adjacent layers bonded internally and to each other by a matrix of β-silicon carbide and silicon, said at least one crystal dispersion forming a rim about the periphery of said core on the upper surface thereof, and said core being formed with a chamfered indentation on the lower surface thereof which allows said blank to have a substantially uniform compaction throughout.
Claim 8
Dependent Claim
219 words
A process for producing a blank adapted to be mounted on a substrate to form a cutting insert, comprising the steps of: preparing at least one crystal dispersion of super-hard crystals selected from at least one member of the group consisting of diamond and cubic boron nitride crystals and carbon black in a temporary binder; preparing a core dispersion of carbon fiber, carbon black and filler in a temporary binder; placing said at least one crystal dispersion and said core dispersion in a mold to respectively form at least one crystal dispersion layer and a core dispersion layer, said at least one crystal dispersion layer forming a rim about the periphery of said core dispersion layer on the upper surface thereof; compacting said crystal and core dispersion layers with a chamfered plunger applied to the lower surface of said core layer to form an intermediate composite having a recess at said lower surface, thereby compressing said dispersions to a substantially uniform density throughout said intermediate composite; heating said intermediate composite to allow for the removal of said temporary binder and the infiltration of liquefied silicon into said intermediate composite; sintering said intermediate composite to produce said blank; and bonding said blank onto a substrate by means of an adhesive disposed within said recess, whereby substantially no adhesive is visible.
Claim 9
Dependent Claim
219 words
A process for producing a blank adapted to be mounted on a substrate to form a cutting insert, comprising the steps of: preparing at least one crystal dispersion of super-hard crystals selected from at least one member of the group consisting of diamond and cubic boron nitride crystals and carbon black in a temporary binder; preparing a core dispersion of carbon fiber, carbon black and filler in a temporary binder; placing said at least one crystal dispersion and said core dispersion in a mold to respectively form at least one crystal dispersion layer and a core dispersion layer, said at least one crystal dispersion layer forming a rim about the periphery of said core dispersion layer on the upper surface thereof; compacting said crystal and core dispersion layers with a chamfered plunger applied to the lower surface of said core layer to form an intermediate composite having a recess at said lower surface, thereby compressing said dispersions to a substantially uniform density throughout said intermediate composite; heating said intermediate composite to allow for the removal of said temporary binder and the infiltration of liquefied silicon into said intermediate composite; sintering said intermediate composite to produce said blank; and bonding said blank onto a substrate by means of an adhesive disposed within said recess, whereby substantially no adhesive is visible.
Claim 10
Dependent Claim
21 words
The process of claim 6 wherein said adhesive is selected from one member of the group consisting of polyamide and polyimide.
Claim 11
Dependent Claim
19 words
The product produced in accordance with the process of any one of claims 1, 2, 3, 4 or 6.
References Cited (Backward Citations)
US2475565A
Cited
US2938807A
Cited
US3816081A
Cited
US4063909A
Cited
US4018631A
Cited
US4220677A
Cited
US4120731A
Cited
SU624796A1
Cited
US4219339A
Cited
US4171339A
Cited
US4167399A
Cited
US4168957A
Cited
GB2006733A
Cited
US4173614A
Cited
US4124401A
Cited
US4151686A
Cited
EP0010257A1
Cited
US4220455A
Cited
US4238433A
Cited
EP0012966A1
Cited
US4247304A
Cited
US4242106A
Cited
US4241135A
Cited
US4268582A
Cited
US4231195A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-15 | 1987-11-14 | 1988-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-15 | 1991-11-14 | 1992-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-15 | 1995-11-14 | 1996-05-15 | $7700.00 | Window Closed / Lapsed |