Glass optical fibres and glass compositions therefor
Assignee: Post Office
•
Filing: 1980-04-01
•
Granted: 1984-05-01
•
Expires: 2000-04-01
Abstract
Abstract A glass suitable for use as the core glass in a high numerical aperture optical fibre has a composition selected from the range of glasses which comprise (i) from 15 to 25 mole percent of soda, (ii) from 25 to 65 mole percent of silica and germania, taken together, the content of germania not exceeding 42 mole percent, (iii) up to 22.5 mole percent of boric oxide and barium oxide, taken together, the content of boric oxide not exceeding 20 mole percent, and the content of barium oxide not exceeding 12 mole percent, and (iv) from 0.01 to 1 weight percent of a redox buffering agent. The glass can be prepared by controlling the partial oxygen pressure of the melt so that it is approximately 10-5 atmospheres. An optical fibre can be produced, by using a soda-boro-silicate clad glass, and a core glass having the composition in the above range.
Inventors
- 👤 Keith J. Beales
- 👤 Sally Partington
- 👤 Anthony G. Dunn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:41
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C3/076; C03C3/089
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
184 words
A high numerical aperture optical fibre core glass comprising soda, silica, germania, boric oxide, optionally barium oxide, and a redox buffering agent, and having a composition selected from the range of glasses which comprise (i) from 15 to 25 mole percent soda, (ii) from 25 to 65 mole percent silica and germania, taken together, the content of germania not exceeding 42 mole percent, (iii) up to 22.5 mole percent of boric oxide and barium oxide, taken together, the content of boric oxide not exceeding 20 mole percent and the content of barium oxide not exceeding 12 mole percent, and (iv) from 0.01 to 1 weight percent of a redox buffering agent, said composition being selected such that the glass is not subject to devitrification or phase separation and such that the glass has a refractive index greater than 1.54, said glass being characterized by having a fictive partial oxygen pressure of 10 -5 atmospheres produced by melting appropriate materials from which the glass is formed and controlling the partial oxygen pressure of the melt by bubbling pure dry carbon dioxide through the molten glass.
Claim 2
Dependent Claim
184 words
A high numerical aperture optical fibre core glass comprising soda, silica, germania, boric oxide, optionally barium oxide, and a redox buffering agent, and having a composition selected from the range of glasses which comprise (i) from 15 to 25 mole percent soda, (ii) from 25 to 65 mole percent silica and germania, taken together, the content of germania not exceeding 42 mole percent, (iii) up to 22.5 mole percent of boric oxide and barium oxide, taken together, the content of boric oxide not exceeding 20 mole percent and the content of barium oxide not exceeding 12 mole percent, and (iv) from 0.01 to 1 weight percent of a redox buffering agent, said composition being selected such that the glass is not subject to devitrification or phase separation and such that the glass has a refractive index greater than 1.54, said glass being characterized by having a fictive partial oxygen pressure of 10 -5 atmospheres produced by melting appropriate materials from which the glass is formed and controlling the partial oxygen pressure of the melt by bubbling pure dry carbon dioxide through the molten glass.
Claim 3
Dependent Claim
14 words
A glass according to claim 1, wherein said redox buffering agent is arsenic trioxide.
Claim 4
Dependent Claim
44 words
A glass according to claim 2, having the following composition: 20 mole percent of soda, 8.3 mole percent of boric oxide, 11.7 mole percent of barium oxide, 8 mole percent of germania, 52 mole percent of silica and 0.01-1 weight percent of arsenic trioxide.
Claim 5
Dependent Claim
44 words
A high numerical aperture optical fibre having a core made from a glass according to any of claims 1 to 3 and a cladding made from a soda-boro-silicate glass having a composition so chosen that it is not subject to devitrification or phase separation.
Claim 6
Dependent Claim
35 words
A high numerical aperture optical fibre according to claim 4, wherein said cladding has substantially the following composition: 15.1 mole percent of soda, 23.4 mole percent of boric oxide, and 61.5 mole percent of silica.
Claim 7
Independent Claim
181 words
A method of making a high numerical aperture optical fibre core glass comprising soda, silica, germania, boric oxide, optionally barium oxide, and a redox buffering agent and having a composition chosen from the range of glasses which comprise (i) from 15 to 25 mole percent of soda, (ii) from 25 to 65 mole percent of silica and germania, taken together, the content of germania not exceeding 42 mole percent, (iii) up to 22.5 mole percent of boric oxide and barium oxide, taken together, the content of boric oxide not exceeding 20 mole percent and the content of barium oxide not exceeding 12 mole percent, and (iv) from 0.01 to 1 weight percent of a redox buffering agent, said composition being selected such that the glass is not subject to devitrification or phase separation and such that the glass has a refractive index greater than 1.54, comprising the steps of melting appropriate materials from which the glass is formed and controlling the partial oxygen pressure at 10 -5 atmosphere of the melt by bubbling pure dry carbon dioxide through the molten glass.
Claim 8
Independent Claim
181 words
A method of making a high numerical aperture optical fibre core glass comprising soda, silica, germania, boric oxide, optionally barium oxide, and a redox buffering agent and having a composition chosen from the range of glasses which comprise (i) from 15 to 25 mole percent of soda, (ii) from 25 to 65 mole percent of silica and germania, taken together, the content of germania not exceeding 42 mole percent, (iii) up to 22.5 mole percent of boric oxide and barium oxide, taken together, the content of boric oxide not exceeding 20 mole percent and the content of barium oxide not exceeding 12 mole percent, and (iv) from 0.01 to 1 weight percent of a redox buffering agent, said composition being selected such that the glass is not subject to devitrification or phase separation and such that the glass has a refractive index greater than 1.54, comprising the steps of melting appropriate materials from which the glass is formed and controlling the partial oxygen pressure at 10 -5 atmosphere of the melt by bubbling pure dry carbon dioxide through the molten glass.
Claim 9
Dependent Claim
14 words
A method according to claim 6, wherein said redox buffering agent is arsenic trioxide.
Claim 10
Dependent Claim
47 words
A method according to claim 6, wherein the core glass has the following composition: 20 mole percent soda, 8.3 mole percent of boric oxide, 11.7 mole percent of barium oxide, 8 mole percent of germania, 52 mole percent of silica and 0.01-1 weight percent of arsenic trioxide.
References Cited (Backward Citations)
SU451646A1
Cited
US4097258A
Cited
US3957342A
Cited
US4023952A
Cited
GB1507711A
Cited
SU583104A1
Cited
DE2551158A1
Cited
US4094689A
Cited
FR2368444A1
Cited
GB2002341A
Cited
US4275951A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |