Sodium borosilicate glasses for dielectric optical waveguides
Assignee: Post Office
•
Filing: 1975-04-25
•
Granted: 1976-05-18
•
Expires: 1995-04-25
Abstract
Abstract A particular range of glass compositions in the soda-boro-silicate glass system has been found to be particularly suitable for ultra-low loss dielectric optical waveguides. The composition range is indicated in FIG. 1 of the specification. By preparing such glasses in a reducing atmosphere (0-20% CO in CO2) and adding about 1% As2 O3 to the melt attenuation coefficients due to copper and iron can be minimised. The water content of the glass can be reduced by bubbling dry CO in CO2 through the molten glass. Glasses containing less than 30% Na2O by weight have the lowest losses. Using glasses of this type dielectric optical waveguides having an insertion loss of less than 14 dBKm<->1 have been made.
Inventors
- 👤 George Reginald Newns
- 👤 Keith John Beales
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:16
CPC Classifications
C; C03; C03C; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C3/076; C03C3/089
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
98 words
A reduced soda-boro-silicate glass for use in fabricating dielectric optical waveguides having a total insertion loss of less than 20 dB/km, said glass having an OH content less than 20 ppm, a composition lying within the range of compositions defined by Region A of FIG. 1, and lying outside the region of phase separation of soda-boro-silicate glasses, said glass containing between 0.1% and 5% by weight of a redox buffering oxide to minimize absorption due to presence of transition metal ion impurities, said oxide being selected from the group consisting of arsenic trioxide, antimony trioxide and cerium oxide.
Claim 2
Dependent Claim
98 words
A reduced soda-boro-silicate glass for use in fabricating dielectric optical waveguides having a total insertion loss of less than 20 dB/km, said glass having an OH content less than 20 ppm, a composition lying within the range of compositions defined by Region A of FIG. 1, and lying outside the region of phase separation of soda-boro-silicate glasses, said glass containing between 0.1% and 5% by weight of a redox buffering oxide to minimize absorption due to presence of transition metal ion impurities, said oxide being selected from the group consisting of arsenic trioxide, antimony trioxide and cerium oxide.
Claim 3
Dependent Claim
16 words
A soda-boro-silicate glass as claimed in claim 1 wherein said redox buffering oxide is arsenic trioxide.
Claim 4
Dependent Claim
20 words
A soda-boro-silicate glass as claimed in claim 2, said glass containing less than 30% by weight of Na 2 O.
Claim 5
Dependent Claim
66 words
A dielectric optical waveguide having a core and cladding both consisting of soda-boro-sillicate glass compositions in accordance with claim 1, in which the refractive index of the glasses differs by at least 1%, the cladding glass refractive index being lower than that of the core glass, and the total insertion loss being lower than 20 dB/km at a wavelength of between 750 mm - 850 mm.
Claim 6
Dependent Claim
21 words
A dielectric optical waveguide as claimed in claim 4 wherein said soda-boro-silicate glasses contain less than 30% by weight of soda.
References Cited (Backward Citations)
US3020165A
Cited
US3531306A
Cited
US3858964A
Cited
US3779733A
Cited
US3791714A
Cited
US3868170A
Cited
US3879207A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-18 | 1979-11-17 | 1980-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-18 | 1983-11-17 | 1984-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-18 | 1987-11-17 | 1988-05-18 | $7700.00 | Window Closed / Lapsed |