Photoluminescence method of testing double heterostructure wafers
Assignee: AT&T Inc
•
Filing: 1982-09-10
•
Granted: 1984-04-10
•
Expires: 2002-09-10
Abstract
Abstract Under photoluminescence (PL) excitation, the lateral spreading of photo-excited carriers can suppress the photoluminescence signal from double heterostructure (DH) wafers containing a p-n junction. In any DH with a p-n junction in the active layer, PL is suppressed if the power of the excitation source does not exceed a threshold value. This effect can be advantageously used for a nondestructive optical determination of the top cladding layer sheet conductance as well as p-n junction misplacement, important parameters for injection lasers and LEDs.
Inventors
- 👤 Paul R. Besomi
- 👤 Joshua Degani
- 👤 Daniel P. Wilt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:24
CPC Classifications
G; G01; G01N; G01N21/00; G01N21/62; G01N21/63; G01N21/64; G01N21/6489; G01R; G01R31/00; G01R31/28; G01R31/302; G01R31/308
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
152 words
A manufacturing process including a method of testing a double heterostructure wafer having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at the wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, (e) selecting the wafer if the characteristic exhibits a photoluminescence threshold P th which indicates that the wafer has a p-n junction in the active layer, and rejecting the wafer if the characteristic exhibits no such threshold which indicates that the wafer has a p-n junction outside the active layer.
Claim 2
Dependent Claim
152 words
A manufacturing process including a method of testing a double heterostructure wafer having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at the wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, (e) selecting the wafer if the characteristic exhibits a photoluminescence threshold P th which indicates that the wafer has a p-n junction in the active layer, and rejecting the wafer if the characteristic exhibits no such threshold which indicates that the wafer has a p-n junction outside the active layer.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein the active layer comprises InGaAsP and the cladding layers comprise InP, and in step (a) the excitation beam is generated by a Nd:YAG laser which emits radiation at a wavelength absorbed in the active layer.
Claim 4
Independent Claim
56 words
The method of claims 1 or 2 wherein the wafer should have a total sheet conductance Σ t within a predetermined range, and after step (e) performing on the selected wafers the additional step of calculating Σ t from P th and rejecting those wafers in which the calculated Σ t falls outside the predetermined range.
Claim 5
Dependent Claim
65 words
The method of claim 3 wherein Σ t is calculated from P th using the equation: ##EQU3## where hν is the photon energy of the radiation , kT is the thermal energy, g is the electron charge, α is the absorption coefficient of the active layer to radiation at hν, d a of the active layer, and e is the base of the natural logarithm.
Claim 6
Dependent Claim
145 words
A manufacturing process including a method of testing a double heterostructure wafer having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at the wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, exhibits a photoluminescence threshold P th which indicates that the wafer has a p-n junction in the active layer, and selecting the wafer if the characteristic exhibits no such threshold which indicates that the wafer has a p-n junction outside the active layer.
Claim 7
Dependent Claim
145 words
A manufacturing process including a method of testing a double heterostructure wafer having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at the wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, exhibits a photoluminescence threshold P th which indicates that the wafer has a p-n junction in the active layer, and selecting the wafer if the characteristic exhibits no such threshold which indicates that the wafer has a p-n junction outside the active layer.
Claim 8
Dependent Claim
157 words
A manufacturing process including a method of testing a plurality of double heterostructure wafers each having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at a wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, (e) distinguishing between one wafer if the characteristic exhibits a photoluminescence threshold P th which indicates that the one wafer has a p-n junction in the active layer, and another wafer if the characteristic exhibits no such threshold which indicates that the other wafer has a p-n junction outside the active layer.
Claim 9
Dependent Claim
157 words
A manufacturing process including a method of testing a plurality of double heterostructure wafers each having a narrow bandgap active layer between a pair of wider bandgap cladding layers, the method including the steps of: (a) directing an excitation beam of optical radiation at a wafer, the radiation energy being chosen so that it is absorbed in the active layer, but not in the cladding layers, thereby to generate photoluminescence from the active layer, (b) varying the intensity of the excitation beam so as to vary the intensity of the photoluminescence, (c) detecting the photoluminescence, (d) generating a photoluminescence intensity versus excitation beam intensity characteristic, (e) distinguishing between one wafer if the characteristic exhibits a photoluminescence threshold P th which indicates that the one wafer has a p-n junction in the active layer, and another wafer if the characteristic exhibits no such threshold which indicates that the other wafer has a p-n junction outside the active layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |