Poly(arylene sulfide) composition suitable for molding

Claim 1

A composition suitable for molding comprising: (a) from about 25 to about 50 weight percent poly(arylene sulfide), (b) from about 10 to about 30 weight percent reinforcing agent, (c) from about 30 to about 60 weight percent filler, (d) from about 0.5 to about 2 weight percent of processing aid, (e) from zero to about 3 weight percent colorant, and (f) from about 0.5 to about 2 weight percent of an oil-soluble organonitrogen compound grafted hydrogenated conjugated diene/monovinylarene copolymer having (1) a polymerized monovinylarene content of about 20 to 70 weight percent with the proviso that when said copolymer contains a random block, the block polymonovinylarene content is in the range of about 15 to 35 weight percent, (2) a number average molecular weight suitable for oil solubility, (3) the extent of hydrogenation of said copolymer such that about at least 95 weight percent of olefinic double bonds having been saturated and (4) less than about 5 weight percent of aromatic double bonds having been saturated, said copolymer characterized as having been prepared by the process which comprises metalating a hydrogenated conjugated diene hydrocarbon/monovinylarene hydrocarbon copolymer, and reacting the resulting metalated hydrogenated copolymer with effective amounts of at least one nitrogen-containing organic compound represented by the general formulae X-Q-(NR 2 3 ) n or Y[Q-(NR 2 3 ) n ] m wherein each R 3 is the same or different alkyl, cycloalkyl, aryl, or combination radical, Q is a hydrocarbon radical having a valence of n+1 and is a saturated aliphatic, saturated cycloaliphatic, aromatic or combination radical, X is a functional group capable of reaction on a one-to-one basis with one equivalent of polymer metal, Y is or contains a functional group capable of reacting on a one-to-one basis with one equivalent of polymer metal, n is at least one, and m is 2 or 3, thereby preparing said grafted copolymer.

Claim 6

A method for improving processability of a composition comprising from about 25 to about 50 weight percent poly(arylene sulfide), from about 10 to about 30 weight percent reinforcing agent, from about 30 to about 50 weight percent filler, from about 0.5 to about 2 weight percent of a processing aid and from zero to about 3 weight percent colorant and said method comprising the addition to said composition of from about 0.5 to about 2 weight percent of an oil-soluble organonitrogen compound grafted hydrogenated conjugated diene/monovinylarene copolymer having (1) a polymerized monovinylarene content of about 20 to 70 weight percent with the proviso that when said copolymer contains a random block, the block polymonovinylarene content is in the range of about 15 to 35 weight percent, (2) a number average molecular weight suitable for oil solubility, (3) the extent of hydrogenation of said copolymer such that about at least 95 weight percent of olefinic double bonds having been saturated and (4) less than about 5 weight percent of aromatic double bonds having been saturated, said copolymer characterized as having been prepared by the process which comprises metalating a hydrogenated conjugated diene hydrocarbon/monovinylarene hydrocarbon copolymer, and reacting the resulting metalated hydrogenated copolymer with effective amounts of at least one nitrogen-containing organic compound represented by the general formulae X-Q-(NR 2 3 ) n or Y[Q-(NR 2 3 ) n ] m wherein each R 3 is the same or different alkyl, cycloalkyl, aryl, or combination radical, Q is a hydrocarbon radical having a valence of n+1 and is a saturated aliphatic, saturated cycloaliphatic, aromatic or combination radical, X is a functional group capable of reaction on a one-to-one basis with one equivalent of polymer metal, Y is or contains a functional group capable of reacting on a one-to-one basis with one equivalent of polymer metal, n is at least one, and m is 2 or 3, thereby preparing said grafted copolymer.

Claim 7

A method for improving processability of a composition comprising from about 25 to about 50 weight percent poly(arylene sulfide), from about 10 to about 30 weight percent reinforcing agent, from about 30 to about 50 weight percent filler, from about 0.5 to about 2 weight percent of a processing aid and from zero to about 3 weight percent colorant and said method comprising the addition to said composition of from about 0.5 to about 2 weight percent of an oil-soluble organonitrogen compound grafted hydrogenated conjugated diene/monovinylarene copolymer having (1) a polymerized monovinylarene content of about 20 to 70 weight percent with the proviso that when said copolymer contains a random block, the block polymonovinylarene content is in the range of about 15 to 35 weight percent, (2) a number average molecular weight suitable for oil solubility, (3) the extent of hydrogenation of said copolymer such that about at least 95 weight percent of olefinic double bonds having been saturated and (4) less than about 5 weight percent of aromatic double bonds having been saturated, said copolymer characterized as having been prepared by the process which comprises metalating a hydrogenated conjugated diene hydrocarbon/monovinylarene hydrocarbon copolymer, and reacting the resulting metalated hydrogenated copolymer with effective amounts of at least one nitrogen-containing organic compound represented by the general formulae X-Q-(NR 2 3 ) n or Y[Q-(NR 2 3 ) n ] m wherein each R 3 is the same or different alkyl, cycloalkyl, aryl, or combination radical, Q is a hydrocarbon radical having a valence of n+1 and is a saturated aliphatic, saturated cycloaliphatic, aromatic or combination radical, X is a functional group capable of reaction on a one-to-one basis with one equivalent of polymer metal, Y is or contains a functional group capable of reacting on a one-to-one basis with one equivalent of polymer metal, n is at least one, and m is 2 or 3, thereby preparing said grafted copolymer.