Process for manufacturing boride dispersion copper alloys
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1982-06-11
•
Granted: 1984-03-13
•
Expires: 2002-06-11
Abstract
Abstract A process for manufacturing a boride dispersion copper alloy by preparing a metallic material having a surface portion comprising at least one of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium, and copper or an alloy thereof, and diffusing boron into the surface portion. The resulting material includes fine boride particles uniformly dispersed in the surface portion and is useful as a material for electrical contacts or sliding parts due to its high resistance to adhesion, wear and arc, and excellent electrical conductivity and sliding properties.
Inventors
- 👤 Hironori Fujita
- 👤 Tohru Arai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:03
CPC Classifications
C; C23; C23C; C23C8/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
86 words
A process for manufacturing a boride dispersed copper alloy, which comprises: preparing a metallic material having a surface portion comprising a copper alloy containing at least one metal selected from the group consisting of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium, and copper or an alloy thereof; and diffusing boron into said metallic material to form in said surface portion thereof fine particles of a boride of at least one metal selected from the group consisting of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium.
Claim 2
Dependent Claim
86 words
A process for manufacturing a boride dispersed copper alloy, which comprises: preparing a metallic material having a surface portion comprising a copper alloy containing at least one metal selected from the group consisting of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium, and copper or an alloy thereof; and diffusing boron into said metallic material to form in said surface portion thereof fine particles of a boride of at least one metal selected from the group consisting of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium.
Claim 3
Dependent Claim
55 words
A process according to claim 1, wherein said metallic material is prepared by coating said at least one metal selected from the group consisting of beryllium, gallium, manganese, nickel, palladium, silicon and vanadium on the surface of copper or an alloy thereof, and heating said coated metal to diffuse the same into said surface portion.
Claim 4
Dependent Claim
23 words
A process according to claim 1, wherein said surface portion of said metallic material has a depth of from 0.01 to 1 mm.
Claim 5
Dependent Claim
23 words
A process according to claim 3, wherein said surface portion of said metallic material has a depth of from 0.03 to 0.2 mm.
Claim 6
Dependent Claim
26 words
A process according to claim 1, wherein said surface portion of said metallic material comprises 5 to 75 atom % of said at least one metal.
Claim 7
Dependent Claim
41 words
A process according to claim 1, wherein said surface portion of said metallic material during the preparing step further comprises at least one of manganese, titanium, silicon and chromium, thereby promoting the formation of fine boride particles during the diffusing step.
Claim 8
Dependent Claim
28 words
A process according to claim 6, wherein said at least one of manganese, titanium, silicon and chromium is incorporated in the range of 0.1 to 3 atom %.
Claim 9
Dependent Claim
19 words
A process according to claim 1, wherein said boride has an average particle diameter of 0.1 to 20 microns.
Claim 10
Dependent Claim
20 words
A process according to claim 1, wherein said boride occupies about 5 to 80% by volume of said surface portion.
Claim 11
Dependent Claim
33 words
A process according to claim 1, wherein said boron is diffused by one method selected from the group consisting of a molten salt method, a powder method and a physical vapor deposition method.
Claim 12
Dependent Claim
50 words
A process according to claim 1, wherein nickel and copper are melted to prepare said metallic material having the surface portion of a copper-nickel alloy, and said metallic material is immersed in a molten salt bath containing boron to form fine nickel boride particles uniformly dispersed in said surface portion.
Claim 13
Dependent Claim
51 words
A process according to claim 6, wherein nickel, silicon and copper are melted to prepare said metallic material having the surface portion of a copper-nickel-silicon alloy, and said metallic material is immersed in a molten salt bath containing boron to form fine nickel boride particles uniformly dispersed in said surface portion.
Claim 14
Dependent Claim
51 words
A process according to claim 6, wherein nickel, titanium and copper are melted to prepare said metallic material having the surface portion of a copper-nickel-titanium alloy, and said metallic material is immersed in a molten salt bath containing boron to form fine nickel boride particles uniformly dispersed in said surface portion.
Claim 15
Dependent Claim
55 words
A process according to claim 2, wherein a nickel layer is electroplated on pure copper and heated to prepare said metallic material having the surface portion of a copper-nickel alloy, and said metallic material is immersed in a molten salt bath containing boron to form fine nickel boride particles uniformly dispersed in said surface portion.
Claim 16
Dependent Claim
50 words
A process according to claim 1, wherein manganese and copper are melted to prepare said metallic material having the surface portion of a copper-manganese alloy, and said metallic material is buried and heated in a powder mixture containing boron to form fine manganese boride uniformly dispersed in said surface portion.
Claim 17
Dependent Claim
50 words
A process according to claim 1, wherein silicon and copper are melted to prepare said metallic material having the surface portion of a copper-silicon alloy, and said metallic material is buried and heated in a powder mixture containing boron to form fine silicon boride uniformly dispersed in said surface portion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-13 | 1987-09-12 | 1988-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-13 | 1991-09-12 | 1992-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-13 | 1995-09-12 | 1996-03-13 | $7700.00 | Window Closed / Lapsed |