Novel polymer composition

Assignee: Mitsubishi Chemical Corp
•
Filing: 1981-12-31
•
Granted: 1984-03-06
•
Expires: 2001-12-31
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A polymer composition wherein an inorganic substance and an organic polymer are firmly consolidated, which is characterized by being produced by polymerizing a vinyl monomer susceptible to radical polymerization in a polymerization system containing a dispersed inorganic substance in the presence of at least one monomer selected from sulfonic acid monomers, sulfonate monomers, or carboxylic acid monomers represented by the general formula [I] <IMAGE> [I] wherein R1 is a hydrogen atom, alkyl group having 1 to 20 carbon atoms, phenyl group, derivative of phenyl group, or halogen atom, X is CONH, <IMAGE> COO(CH2)m or (CH2)n (wherein R2 and R3 are each a hydrogen atom or alkyl group having 1 to 15 carbon atoms, R4 is an alkylene group having 1 to 15 carbon atoms, m is an integer of 1 to 20, and n is an integer of 0 to 20), and Y is a hydrogen atom, ammonium radical, or an alkali metal atom, or by the general formula [II] <IMAGE> [II] wherein R5 is a hydrogen atom, alkyl group having 1 to 15 carbon atoms, COOZ, halogen atom, phenyl group, or derivative of phenyl group, R6 is a hydrogen atom, alkyl group having 1 to 15 carbon atoms, COOZ, halogen atom, phenyl group, or derivative of phenyl group, R7 is a hydrogen atom, alkyl group having 1 to 15 carbon atoms, halogen atom, phenyl group, or derivative of phenyl group, and Z is a hydrogen atom, ammonium radical, or alkali metal atom, or by the general formula [III] <IMAGE> [III] wherein R8 and R9 are each a hydrogen atom, alkyl group having 1 to 15 carbon atoms, halogen atom, phenyl group, or derivative of phenyl group.

Inventors

  • 👤 Kazuo Kishida
  • 👤 Isao Sasaki
  • 👤 Nobuhiro Mukai

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-05 15:02
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/44

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 187 words
A method of preparing a polymeric composition in which an inorganic substance is firmly consolidiated in an organic polymer, comprising: heterogeneously polymerizing methylmethacrylate or a vinyl monomer mixture comprising methylmethacrylate as the major component without initiating the reaction with a radical polymerization initiator at a temperature such that substantially no thermal polymerization occurs in a polymerization system containing said inorganic substance dispersed in an aqueous medium in the presence of at least one monomer selected from the group consisting of sulfonic acid monomers and sulfonate monomers of formula [I] ##STR9## wherein R 1 is hydrogen, alkyl of 1 to 20 carbon atoms, phenyl, a derivative of a phenyl group, or a halogen atom; X is CONH, ##STR10## COO(CH 2 ) m or (CH 2 ) n wherein R 2 and R 3 are each hydrogen or alkyl of 1 to 15 carbon atoms, R 4 is an alkylene group of 1 to 15 carbon atoms, m is an integer of 1 to 20, and n is 0 or an integer of 1 to 20; and U is a hydrogen atom, ammonium radical or an alkali metal atom.
Claim 2
Independent Claim 187 words
A method of preparing a polymeric composition in which an inorganic substance is firmly consolidiated in an organic polymer, comprising: heterogeneously polymerizing methylmethacrylate or a vinyl monomer mixture comprising methylmethacrylate as the major component without initiating the reaction with a radical polymerization initiator at a temperature such that substantially no thermal polymerization occurs in a polymerization system containing said inorganic substance dispersed in an aqueous medium in the presence of at least one monomer selected from the group consisting of sulfonic acid monomers and sulfonate monomers of formula [I] ##STR9## wherein R 1 is hydrogen, alkyl of 1 to 20 carbon atoms, phenyl, a derivative of a phenyl group, or a halogen atom; X is CONH, ##STR10## COO(CH 2 ) m or (CH 2 ) n wherein R 2 and R 3 are each hydrogen or alkyl of 1 to 15 carbon atoms, R 4 is an alkylene group of 1 to 15 carbon atoms, m is an integer of 1 to 20, and n is 0 or an integer of 1 to 20; and U is a hydrogen atom, ammonium radical or an alkali metal atom.
Claim 3
Dependent Claim 21 words
The method of claim 1, wherein the sulfonic acid monomer or sulfonate monomer is 2-acrylamido-2-methylpropanesulfonic acid, sodium 2-methacryloylethanesulfonate, or sodium 3-methacryloylpropanesulfonate.
Claim 4
Dependent Claim 58 words
The method of claim 1, wherein the inorganic substance is at least one member selected from the group consisting of calcium sulfite, calcium sulfate, silicon dioxide, titanium oxide, antimony trioxide, talc, clay, aluminum oxide, calcium carbonate, carbon black, carbon fiber, glass fiber, graphite, nickel powder, iron powder, zinc powder, copper powder, iron oxide, zinc oxide and aluminum hydroxide.
Claim 5
Dependent Claim 21 words
The method of claim 1, wherein the weight ratio of monomer mixture to the inorganic substance ranges from 250:1 to 1:5.
Claim 6
Dependent Claim 24 words
The method of claim 1, wherein said polymerization reaction is conducted under an inert gas atmosphere at a temperature from 10° to 100° C.
Claim 7
Dependent Claim 41 words
The method of claim 1, wherein the amount of said sulfonic acid monomer or sulfonate monomer in the reaction medium ranges from 0.05 to 100% by weight based on the total amount of inorganic substance and monomer in the polymerization medium.

References Cited (Backward Citations)

US3935340A Cited
US4130512A Cited
US3884871A Cited
US4048136A Cited
US3946139A Cited
US4070334A Cited
US4015991A Cited
US4060511A Cited
US4147681A Cited
US4194920A Cited
US4102856A Cited
US4230810A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1987-03-06 1987-09-05 1988-03-06 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1991-03-06 1991-09-05 1992-03-06 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1995-03-06 1995-09-05 1996-03-06 $7700.00 Window Closed / Lapsed