US4426443A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Preparation of hydrolyzed collagen-containing products from non-gelled, liquid hydrolyzed collagen concentrate and gelled products prepared therefrom
Assignee: DYNAGEL INCORPORATED A CORP OF
•
Filing: 1981-08-27
•
Granted: 1984-01-17
•
Expires: 2001-08-27
Abstract
Abstract A method of preparing a gelled product from an ungelled aqueous hydrolyzed collagen, such as gelatin or glue, concentrate containing 10-60 weight percent hydrolyzed collagen and a lyotropic agent is disclosed. The concentrate has a hydrolyzed collagen-to-lyotropic agent weight ratio of 1:0 of 1:0.1 to about 1:4.5, a pH value of 2.5-7 and gels at less than 20° C. On dilution with water to a hydrolyzed collagen concentration of about 2 weight percent while substantially maintaining the pH value of the concentrate, the diluted composition gels at a temperature above that of the concentrate. Specific concentrates, food products, industrial applications and methods for using the concentrates are disclosed.
Inventors
- 👤 Joseph L. Shank
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:32
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/22; A; A23; A23L; A23L29/00; A23L29/20; A23L29/275; A23L29/281; A23L29/284; C09H; C09H5/00; D; D21; D21H; D21H17/00; D21H17/20; D21H17/21; D21H17/22; G; G03; G03C; G03C1/00; G03C1/005; G03C1/04; G03C1/047; G03C1/76; G03C1/91; G03C1/93
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
180 words
A method for coating a substrate with a hydrolyzed collagen gel comprising the steps of: providing first volume of an aqueous hydrolyzed collagen concentrate comprising water, from about 10 to about 60 weight percent hydrolyzed collagen and a non-acid lyotropic agent, the weight ratio of hydrolyzed collagen-to-non-acid lyotropic agent being about 1:0.1 to about 1:4.5, said concentrate having a gel-set temperature of less than about 20° C. and a pH value between about 2.5 and about 7; diluting said first volume of hydrolyzed collagen concentrate to from about 2 to about 300 times said first volume to a hydrolyzed collagen concentration of between about 0.5 and about 25 weight percent to provide a diluted composition having a gel-set temperature higher than that of said hydrolyzed collagen concentrate; applying said diluted composition, prior to gelation, to contact the surface of a substrate and form a coating thereon; and maintaining said applied, diluted composition in contact with said substrate surface at a temperature below the gel-set temperature of said diluted composition for a time sufficient to form a gel on said surface.
Claim 2
Independent Claim
180 words
A method for coating a substrate with a hydrolyzed collagen gel comprising the steps of: providing first volume of an aqueous hydrolyzed collagen concentrate comprising water, from about 10 to about 60 weight percent hydrolyzed collagen and a non-acid lyotropic agent, the weight ratio of hydrolyzed collagen-to-non-acid lyotropic agent being about 1:0.1 to about 1:4.5, said concentrate having a gel-set temperature of less than about 20° C. and a pH value between about 2.5 and about 7; diluting said first volume of hydrolyzed collagen concentrate to from about 2 to about 300 times said first volume to a hydrolyzed collagen concentration of between about 0.5 and about 25 weight percent to provide a diluted composition having a gel-set temperature higher than that of said hydrolyzed collagen concentrate; applying said diluted composition, prior to gelation, to contact the surface of a substrate and form a coating thereon; and maintaining said applied, diluted composition in contact with said substrate surface at a temperature below the gel-set temperature of said diluted composition for a time sufficient to form a gel on said surface.
Claim 3
Dependent Claim
14 words
The method according to claim 1 wherein said non-acid lyotropic agent includes calcium chloride.
Claim 4
Dependent Claim
31 words
The method according to claim 2 wherein said substrate is a pile of coal or ore having a dust laden surface, and said method controls the escape of said dust therefrom.
Claim 5
Dependent Claim
24 words
The method according to claim 2 wherein said substrate is a photographic film precursor sheet and said method provides a subbing for photographic film.
Claim 6
Dependent Claim
21 words
The method according to claim 4 wherein said diluted composition comprises about 10 to about 25 percent by weight hydrolyzed collagen.
Claim 7
Dependent Claim
20 words
The method according to claim 2 wherein said substrate is paper and said method provides a sizing for said paper.
Claim 8
Dependent Claim
20 words
The method according to claim 6 wherein said diluted composition comprises about 0.5 to about 3.5 weight percent hydrolyzed collagen.
Claim 9
Dependent Claim
27 words
The method according to claim 1 wherein said lyotropic agent is calcium chloride and said hydrolyzed collagen-to-calcium chloride weight ratio is from about 1:0.3 to about 1:1.5.
Claim 10
Dependent Claim
29 words
The method according to claim 2 wherein said non-acid lyotropic agent additionally includes urea and said hydrolyzed collagen-to-non-acid lyotropic agent weight ratio is from about 1:1 to about 1:4.5
Claim 11
Independent Claim
160 words
A method for controlling the escape of dust from a dust laden surface comprising the steps of: providing an aqueous hydrolyzed collagen concentrate comprising water, from about 10 to about 40 weight percent hydrolyzed collagen and a lyotropic agent, the weight ratio of hydrolyzed collagen-to-lyotropic agent being about 1:0.3 to about 1:4.5, said concentrate having a gel-set temperature of less than about 0° C. and a pH value between about 4 and about 6; diluting said hydrolyzed collagen concentrate to a hydrolyzed collagen concentration of between about 0.5 and about 3.5 weight percent to provie a diluted composition having a gel-set temperature higher than that of said hydrolyzed collagen concentrate; applying said diluted composition, prior to gelation, to contact the surface of a dust laden substrate; and maintaining said applied, diluted composition in contact with said substrate surface at a temperature below the gel-set temperature of said diluted composition for a time sufficient to form a gel on said surface.
Claim 12
Independent Claim
160 words
A method for controlling the escape of dust from a dust laden surface comprising the steps of: providing an aqueous hydrolyzed collagen concentrate comprising water, from about 10 to about 40 weight percent hydrolyzed collagen and a lyotropic agent, the weight ratio of hydrolyzed collagen-to-lyotropic agent being about 1:0.3 to about 1:4.5, said concentrate having a gel-set temperature of less than about 0° C. and a pH value between about 4 and about 6; diluting said hydrolyzed collagen concentrate to a hydrolyzed collagen concentration of between about 0.5 and about 3.5 weight percent to provie a diluted composition having a gel-set temperature higher than that of said hydrolyzed collagen concentrate; applying said diluted composition, prior to gelation, to contact the surface of a dust laden substrate; and maintaining said applied, diluted composition in contact with said substrate surface at a temperature below the gel-set temperature of said diluted composition for a time sufficient to form a gel on said surface.
Claim 13
Dependent Claim
16 words
The method according to claim 10 wherein said substrate is a pile of coal or ore.
Claim 14
Dependent Claim
19 words
The method according to claim 11 wherein said diluted composition is applied to said dust laden surface by spraying.
Claim 15
Dependent Claim
22 words
The method according to claim 10 including the additional step of dehydrating said gel on said dust laden surface into a film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |