Carbide coated composite modified silicon aluminum oxynitride cutting tools
Assignee: Verizon Laboratories Inc
•
Filing: 1982-05-20
•
Granted: 1984-01-17
•
Expires: 2002-05-20
Abstract
Abstract Coated abrasion resistant composite ceramic cutting tools comprise a composite substrate body consisting essentially of a particulate material selected from the group consisting of the refractory metal carbides, nitrides, carbonitrides and combinations thereof uniformly distributed in a matrix, coated with at least one adherent coating layer comprising a refractory metal carbide. The particulate material is of an average particle size ranging between about 0.5 microns to about 20 microns and comprises from about 5 to about 60 volume percent of the composite cutting tool. The matrix consists essentially of a modified silicon aluminum oxynitride having about 2 to about 25 volume percent of a modifier selected from the oxides of silicon, yttrium, magnesium, hafnium, zirconium, beryllium, the lanthanides and combinations thereof.
Inventors
- 👤 Vinod K. Sarin
- 👤 Sergej-Tomislav Buljan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 08:56
CPC Classifications
B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597; C04B41/00; C04B41/45; C04B41/50; C04B41/5025; C04B41/5053; C04B41/80; C04B41/81; C04B41/85; C04B41/87; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
118 words
A coated abrasion resistant composite ceramic cutting tool comprising a substrate body and at least one adherent refractory metal carbide coating layer; said substrate body consisting essentially of a particulate material selected from the group consisting of the refractory metal carbides, nitrides, carbonitrides and mixtures thereof uniformly distributed in a matrix comprising a modified silicon aluminum oxynitride, said particulate material comprising from about 5 volume percent to about 60 volume percent of said cutting tool and having an average particle size of between about 0.5 microns and about 20 microns; said modified silicon aluminum oxynitride having a modifier selected from the group consisting of the oxides of silicon, ytrrium, magnesium, hafnium, zirconium, beryllium, the lanthanides and combinations thereof.
Claim 2
Dependent Claim
118 words
A coated abrasion resistant composite ceramic cutting tool comprising a substrate body and at least one adherent refractory metal carbide coating layer; said substrate body consisting essentially of a particulate material selected from the group consisting of the refractory metal carbides, nitrides, carbonitrides and mixtures thereof uniformly distributed in a matrix comprising a modified silicon aluminum oxynitride, said particulate material comprising from about 5 volume percent to about 60 volume percent of said cutting tool and having an average particle size of between about 0.5 microns and about 20 microns; said modified silicon aluminum oxynitride having a modifier selected from the group consisting of the oxides of silicon, ytrrium, magnesium, hafnium, zirconium, beryllium, the lanthanides and combinations thereof.
Claim 3
Dependent Claim
45 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said refractory metal carbide coating is selected from the group consisting of titanium carbide, vanadium carbide, chromium carbide, zirconium carbide, niobium carbide, molybdenum carbide, hafnium carbide, tantalum carbide, and tungsten carbide.
Claim 4
Dependent Claim
33 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 2 wherein said refractory metal carbide coating is selected from the group consisting of titanium carbide, hafnium carbide, and combinations thereof.
Claim 5
Dependent Claim
31 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said refractory metal carbide coating layer is of a thickness between about 0.1 microns and 10 microns.
Claim 6
Dependent Claim
30 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 4 wherein said refractory metal carbide coating is of a thickness between about 1.0 and about 10 microns.
Claim 7
Dependent Claim
53 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said modified silicon aluminum oxynitride is formed from about 2 to about 20 volume percent of said modifier, from about 20 to about 90 volume percent silicon nitride, and from about 5 to about 60 volume percent aluminum oxide.
Claim 8
Dependent Claim
30 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein the average particle size of said particulate material ranges between about 0.5 microns and 5 microns.
Claim 9
Dependent Claim
30 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said particulate material comprises from about 20 to about 40 volume percent of said cutting tool.
Claim 10
Dependent Claim
28 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 6 wherein said modifier comprises from about 2 to about 10 volume percent of said matrix.
Claim 11
Dependent Claim
32 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said particulate material is selected from the carbides of titanium, tungsten, hafnium, niobium, tantalum, vanadium, and combinations thereof.
Claim 12
Dependent Claim
31 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said particulate material is selected from the group consisting of titanium nitride, hafnium nitride, and combinations thereof.
Claim 13
Dependent Claim
31 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said particulate material is selected from the group consisting of titanium carbonitride, hafnium carbonitride, and combinations thereof.
Claim 14
Dependent Claim
20 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 10 wherein said particulate material is titanium carbide.
Claim 15
Dependent Claim
19 words
A coated abrasion resistant composite ceramic cutting tool in accordance with claim 1 wherein said modifier is yttrium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |