US4421702A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ceramic recuperative heat exchangers and a method for producing the same
Assignee: NGK Insulators Ltd
•
Filing: 1981-03-16
•
Granted: 1983-12-20
•
Expires: 2001-03-16
Abstract
Abstract Ceramic honeycomb type recuperative heat exchangers having a large number of parallel channels formed of partition walls are disclosed, in which fluids to be heat-exchanged are passed through respective channels that are produced by extruding a ceramic raw batch material into a honeycomb structural body, drying the shaped honeycomb structural body, prior to or after firing step cutting off partition walls in the given rows of the honeycomb structural body in the axial direction of the channels to a given depth from the end surface of the honeycomb structural body and sealing only the end surfaces of said rows.
Inventors
- 👤 Isao Oda
- 👤 Tadaaki Matsuhisa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:11
CPC Classifications
F; F28; F28F; F28F7/00; F28F7/02; F28F21/00; F28F21/04; Y; Y10; Y10S; Y10S165/00; Y10S165/355; Y10S165/395; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
244 words
A method for producing ceramic recuperative heat exchangers having a large number of parallel channels formed of partition walls such that flowing fluids are capable of being heat-exchanged through respective channels, in which the sectional shape of the channels and thickness of the partition walls are substantially uniform, the open frontal area of the heat transmitting portion where the fluids are heat-exchanged being more than 60% and the porosity of the ceramic material forming the partition walls simultaneously being not more than 10%, which comprises: adding to ceramic material at least some water, an organic solvent, and a forming aid, kneading thoroughly the resulting mixture to prepare a raw batch material; extruding the raw batch material into a honeycomb structural body having a large number of axially extended channels in which the sectional shape of the channels and the thickness of the partition walls are substantially uniform, the channels being arranged generally into rows; drying the shaped honeycomb structural body; prior to or after firing, cutting off partition walls in particular rows of the honeycomb structural body in the axial direction of the channels to a given depth from the end surface of the honeycomb structural body; and sealing only the end surfaces of said rows with a suitable sealing means, such that the open frontal area of the heat transmitting portion is at least 60%, and the porosity of the ceramic is no more than 10% after the conclusion of said sealing step.
Claim 2
Independent Claim
244 words
A method for producing ceramic recuperative heat exchangers having a large number of parallel channels formed of partition walls such that flowing fluids are capable of being heat-exchanged through respective channels, in which the sectional shape of the channels and thickness of the partition walls are substantially uniform, the open frontal area of the heat transmitting portion where the fluids are heat-exchanged being more than 60% and the porosity of the ceramic material forming the partition walls simultaneously being not more than 10%, which comprises: adding to ceramic material at least some water, an organic solvent, and a forming aid, kneading thoroughly the resulting mixture to prepare a raw batch material; extruding the raw batch material into a honeycomb structural body having a large number of axially extended channels in which the sectional shape of the channels and the thickness of the partition walls are substantially uniform, the channels being arranged generally into rows; drying the shaped honeycomb structural body; prior to or after firing, cutting off partition walls in particular rows of the honeycomb structural body in the axial direction of the channels to a given depth from the end surface of the honeycomb structural body; and sealing only the end surfaces of said rows with a suitable sealing means, such that the open frontal area of the heat transmitting portion is at least 60%, and the porosity of the ceramic is no more than 10% after the conclusion of said sealing step.
Claim 3
Dependent Claim
39 words
The method as claimed in claim 1 wherein the step of sealing the end surfaces of said rows when the partition walls have been cut off, comprises applying a paste of the same material as the honeycomb structural body.
Claim 4
Independent Claim
21 words
The method as claimed in claims 1 or 2, wherein the sectional shape of the channels is triangular, quadrilateral or hexagonal.
Claim 5
Dependent Claim
24 words
The method as claimed in claim 1 or 2 wherein the ceramic material is cordierite, mullite, magnesium aluminum titanate, silicon carbide or silicon nitride.
Claim 6
Dependent Claim
19 words
The method as claimed in claim 3, wherein the ceramic material is cordierite mullite, magnesium aluminum titanate, silicon nitride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-19 | 1987-06-20 | 1987-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-19 | 1991-06-20 | 1991-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-19 | 1995-06-20 | 1995-12-20 | $7700.00 | Window Closed / Lapsed |