Abstract A ceramic cellular structure having a cell density of up to 1600 cells per square inch and wall thicknesses down to 2 mils is produced by a process which comprises: (1) forming a slurry consisting essentially of finely divided sinterable solid particles of ceramic raw materials and a controlled amount of a plastic supporting matrix containing thermoplastic resin, a thermosetting resin, a plasticizer, an organic solvent and a small amount of a deflocculant; (2) ball milling the slurry; (3) casting the slurry in the form of a film; (4) removing the solvent to produce a self-supporting green ceramic tape; (6) molding a portion of the tape to form a corrugated first member; (7) providing another portion of the tape to form a substantially flat second member; (8) forming a first bilayer by bonding the second member to the nodes of the first member; (9) mutually bonding a predetermined number of bilayers substantially identical to the first bilayer to form a cellular green structure of a desired shape; and (10) firing the green structure at a temperature sufficient to form a sinter-welded polycrystalline ceramic structure. The fired structures, after being subjected to various finishing operations, are useful as rotary heat regenerators, stationary heat recuperators and catalyst supports.
A cellular structure of green ceramic tape consisting essentially of finely divided sinterable solid particles of ceramic raw materials substantially uniformly distributed throughout a fugitive plastic supporting matrix, the cells of the structure being defined by alternate corrugated and flat ceramic tape members wherein said cells completely traverse the article from one face to the opposite face thereof, the weight ratio of said supporting matrix to said raw materials in said tape being from about 1:3 to about 1:6, said supporting matrix consisting essentially of from about 28.5 to about 74.5 weight percent of a two-part resin, the resin consisting essentially of polyvinyl butyral in the amount of from 50 to 95 weight percent, remainder an amine thermosetting resin selected from the group consisting of melamine formaldehyde and urea formaldehyde, and from about 25 to about 70 weight percent of a plasticizer selected from the group consisting of alkyl phthalate and dialkyl phthalate plasticizers and from about 0.5 to about 1.5 weight percent of a deflocculating agent, the structure bearing a surface layer containing a catalyst, the structure, after firing, defining a catalytic converter.
Claim 2
Dependent Claim
184 words
A cellular structure of green ceramic tape consisting essentially of finely divided sinterable solid particles of ceramic raw materials substantially uniformly distributed throughout a fugitive plastic supporting matrix, the cells of the structure being defined by alternate corrugated and flat ceramic tape members wherein said cells completely traverse the article from one face to the opposite face thereof, the weight ratio of said supporting matrix to said raw materials in said tape being from about 1:3 to about 1:6, said supporting matrix consisting essentially of from about 28.5 to about 74.5 weight percent of a two-part resin, the resin consisting essentially of polyvinyl butyral in the amount of from 50 to 95 weight percent, remainder an amine thermosetting resin selected from the group consisting of melamine formaldehyde and urea formaldehyde, and from about 25 to about 70 weight percent of a plasticizer selected from the group consisting of alkyl phthalate and dialkyl phthalate plasticizers and from about 0.5 to about 1.5 weight percent of a deflocculating agent, the structure bearing a surface layer containing a catalyst, the structure, after firing, defining a catalytic converter.