Low temperature process for depositing an oxide dielectric layer on a conductive surface and multilayer structures formed thereby
Assignee: Raytheon Co
•
Filing: 1981-09-24
•
Granted: 1983-12-06
•
Expires: 2001-09-24
Abstract
Abstract The specification discloses a low temperature process for forming an effective insulating layer of a selected oxide on the surface of a chosen conductive substrate. The oxide so formed has low pinhole density, good surface morphology, and good step coverage. In addition, the disclosed process simultaneously minimizes the deformation or restructuring of the surface of a temperature-sensitive conductive substrate, which would produce unwanted hillocks or spikes that degrade the insulating properties of the oxide. In accordance with the disclosed process, the substrate is exposed to a chosen vapor phase reactant in the presence of neutral, charge-free atomic oxygen to produce a reaction between the atomic oxygen and the vapor phase reactant to form the selected oxide, which deposits on the surface of the conductive substrate. Improved multilayer structures comprising multiple layers of conductive material separated by an oxide dielectric layer are formed by the disclosed process.
Inventors
- 👤 John W. Peters
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:55
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6338; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
118 words
A process for forming an effective insulating layer of an oxide of a chosen element on the surface of a substrate of a chosen conductive material comprising the step of exposing said surface to a chosen vapor phase reactant containing said chosen element in the presence of neutral atomic oxygen at a temperature sufficiently low to minimize deformation of said surface of said substrate to thereby produce a reaction between said atomic oxygen and said reactant to form said oxide which deposits as a layer on said surface of said substrate, whereby said layer of said oxide exhibits relatively low pinhole density, relatively good surface morphology, and relatively good step coverage to thereby provide said effective insulating layer.
Claim 2
Dependent Claim
118 words
A process for forming an effective insulating layer of an oxide of a chosen element on the surface of a substrate of a chosen conductive material comprising the step of exposing said surface to a chosen vapor phase reactant containing said chosen element in the presence of neutral atomic oxygen at a temperature sufficiently low to minimize deformation of said surface of said substrate to thereby produce a reaction between said atomic oxygen and said reactant to form said oxide which deposits as a layer on said surface of said substrate, whereby said layer of said oxide exhibits relatively low pinhole density, relatively good surface morphology, and relatively good step coverage to thereby provide said effective insulating layer.
Claim 3
Dependent Claim
27 words
The process as set forth in claim 1 wherein said atomic oxygen is photochemically generated by the mercury photosensitized dissociation of a chosen chemically unreactive oxygen-containing precursor.
Claim 4
Dependent Claim
44 words
The process as set forth in claim 1 wherein said atomic oxygen is photochemically generated by the exposure of a chosen chemically unreactive oxygen-containing precursor to radiation of a selected wavelength to cause the direct dissociation of said precursor to form said atomic oxygen.
Claim 5
Dependent Claim
38 words
The process as set forth in claim 2 or 3 wherein said chosen chemically unreactive oxygen-containing precursor is selected from the group consisting of: nitrous oxide, nitrogen dioxide, and molecular oxygen under selected pressure and flow rate conditions.
Claim 6
Dependent Claim
40 words
The process as set forth in claim 1 wherein said chosen conductive material is selected from the group consisting of aluminum, aluminum silicide, magnesium chromium, molybdenum, tungsten, titanium, vanadium, iron, copper, indium, tin, indium tin oxide, tin oxide, and polyacetylene.
Claim 7
Dependent Claim
50 words
The process as set forth in claim 1 wherein said substrate of said chosen conductive material is selected from the group consisting of a continuous layer of said chosen conductive material formed on a second substrate, and a patterned layer of said chosen conductive material formed on a second substrate.
Claim 8
Dependent Claim
104 words
A process for forming a low defect density layer of an oxide of a chosen element on the surface of a chosen temperature-sensitive conductive substrate while simultaneously minimizing deformation of said surface, comprising the step of exposing said surface to a chosen vapor phase reactant containing said chosen element in the presence of neutral, charge-free oxygen atoms to thereby produce a reaction between said neutral oxygen atoms and said reactant to form said oxide which deposits on said surface of said substrate, whereby the temperature of said reaction is sufficiently low to minimize said deformation of said surface of said chosen temperature-sensitive conductive substrate.
Claim 9
Dependent Claim
104 words
A process for forming a low defect density layer of an oxide of a chosen element on the surface of a chosen temperature-sensitive conductive substrate while simultaneously minimizing deformation of said surface, comprising the step of exposing said surface to a chosen vapor phase reactant containing said chosen element in the presence of neutral, charge-free oxygen atoms to thereby produce a reaction between said neutral oxygen atoms and said reactant to form said oxide which deposits on said surface of said substrate, whereby the temperature of said reaction is sufficiently low to minimize said deformation of said surface of said chosen temperature-sensitive conductive substrate.
Claim 10
Dependent Claim
92 words
A process for forming an effective insulating layer of silicon dioxide on the surface of a chosen temperature sensitive conductive substrate comprising the step of exposing said surface to a chosen silicon-containing vapor phase reactant in the presence of neutral, charge-free oxygen atoms to thereby react said oxygen atoms and said reactant to form said silicon dioxide on said surface, whereby the temperature of said process is sufficiently low to prevent the formation of unwanted hillocks or spikes on said surface which would penetrate said insulating layer to form unwanted pinholes therein.
Claim 11
Dependent Claim
92 words
A process for forming an effective insulating layer of silicon dioxide on the surface of a chosen temperature sensitive conductive substrate comprising the step of exposing said surface to a chosen silicon-containing vapor phase reactant in the presence of neutral, charge-free oxygen atoms to thereby react said oxygen atoms and said reactant to form said silicon dioxide on said surface, whereby the temperature of said process is sufficiently low to prevent the formation of unwanted hillocks or spikes on said surface which would penetrate said insulating layer to form unwanted pinholes therein.
Claim 12
Dependent Claim
37 words
The process as set forth in claim 8 wherein said chosen silicon-containing vapor phase reactant is silane (SiH 4 ) and said exposing takes place at a temperature within the range of 100° C. to 200° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |