US4415602A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Reactive plating method and product
Assignee: Canadian Industrial Innovation Centre
•
Filing: 1982-04-05
•
Granted: 1983-11-15
•
Expires: 2002-04-05
Abstract
Abstract A method is disclosed for the reactive plating of substrates to produce transparent conducting films and photoactive coatings. Reactive gases at low pressures are introduced into a vacuum chamber having a partial vacuum therein. A substrate located in the vacuum chamber is subjected to a glow discharge in the partial vacuum. A coating material, such as zinc or silicon is vaporized in the vacuum chamber to react with the gases, with the resulting compound being deposited on the substrate by the effect of the glow discharge. The power in the glow discharge and the partial pressures of the vaporized coating material and gases introduced into the vacuum chamber can all be controlled separately to vary the stoichiometric ratios and the properties of the coatings. The electrode geometry is arranged and the operation maintained such that the power density distribution in the discharge is fixed and controlled.
Inventors
- 👤 Don E. Brodie
- 👤 John H. Morgan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:50
CPC Classifications
H; H01; H01J; H01J37/00; H01J37/32; H01J37/32009; H01J37/32018; C; C23; C23C; C23C14/00; C23C14/0021; C23C14/22; C23C14/24; C23C14/32
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
69 words
A method of coating a substrate comprising: providing a vacuum chamber communicating with a surface of the substrate to be coated; producing a glow discharge in the vacuum chamber in contact with said substrate surface; vaporizing coating material in said chamber; and introducing a gas into the vacuum chamber to react with said vaporized coating material forming a compound to be deposited on the substrate by the glow discharge.
Claim 2
Independent Claim
69 words
A method of coating a substrate comprising: providing a vacuum chamber communicating with a surface of the substrate to be coated; producing a glow discharge in the vacuum chamber in contact with said substrate surface; vaporizing coating material in said chamber; and introducing a gas into the vacuum chamber to react with said vaporized coating material forming a compound to be deposited on the substrate by the glow discharge.
Claim 3
Dependent Claim
34 words
A method of coating a substrate as claimed in claim 1 wherein the production of the glow discharge, the vaporization of the coating material and the introduction of the gas are all done simultaneously.
Claim 4
Dependent Claim
37 words
A method of coating a substrate as claimed in claim 2 and further comprising the step of terminating the glow discharge after at least a continuous molecular layer of coating compound has been coated on the substrate.
Claim 5
Dependent Claim
35 words
A method of coating a substrate as claimed in claim 3 wherein the glow discharge is produced having a discharge power just above the threshold power required to maintain the discharge in the vacuum chamber.
Claim 6
Dependent Claim
45 words
A method of coating a substrate as claimed in claim 3 wherein the gas is introduced at a constant rate and the coating material is vaporized at a rate such that its reaction with the gas produces a non-stoichiometric compound being deposited on the substrate.
Claim 7
Dependent Claim
47 words
A method of coating a substrate as claimed in claim 3 wherein the coating material is vaporized at a constant rate and the gas is introduced at a rate such that its reaction with the vaporized coating material produces a non-stiochiometric compound being deposited on the substrate.
Claim 8
Dependent Claim
32 words
A method of coating a substrate as claimed in claim 1 wherein the production of the glow discharge and the introduction of the gas are done before the coating material is vaporized.
Claim 9
Dependent Claim
35 words
A method of coating a substrate as claimed in claim 7 and further comprising the step of terminating the glow discharge after the introduction of the gas and during the vaporization of the coating material.
Claim 10
Dependent Claim
35 words
A method of coating a substrate as claimed in claim 7 wherein the glow discharge is produced having a discharge power just above the threshold power required to maintain the discharge in the vacuum chamber.
Claim 11
Dependent Claim
45 words
A method of coating a substrate as claimed in claim 7 wherein the gas is introduced at a constant rate and the coating material is vaporized at a rate such that its reaction with the gas produces a non-stoichiometric compound being deposited on the substrate.
Claim 12
Dependent Claim
47 words
A method of coating a substrate as claimed in claim 7 wherein the coating material is vaporized at a constant rate and the gas is introduced at a rate such that its reaction with the vaporized coating material produces a non-stoichiometric compound being deposited on the substrate.
Claim 13
Dependent Claim
35 words
A method of coating a substrate as claimed in claim 1 wherein the glow discharge is produced having a discharge power just above the threshold power required to maintain the discharge in the vacuum chamber.
Claim 14
Dependent Claim
45 words
A method of coating a substrate as claimed in claim 1 wherein the gas is introduced at a constant rate and the coating material is vaporized at a rate such that its reaction with the gas produces a non-stoichiometric compound being deposited on the substrate.
Claim 15
Dependent Claim
47 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is vaporized at a constant rate and the gas is introduced at a rate such that its reaction with the vaporized coating material produces a non-stoichiometric compound being deposited on the substrate.
Claim 16
Dependent Claim
22 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is zinc and the gas is oxygen.
Claim 17
Dependent Claim
45 words
A method of coating a substrate as claimed in claim 15 wherein the zinc is vaporized by providing a heated zinc source having a discharge orifice between 0.024 and 0.030 inches in diameter, the zinc being heated between 430 degrees Centigrade and 600 degrees Centigrade.
Claim 18
Dependent Claim
41 words
A method of coating a substrate as claimed in claim 15 wherein the zinc is vaporized by providing a heated zinc source having a discharge orifice of 0.024 inches in diameter, the zinc being heated between 550 and 600 degrees Centigrade.
Claim 19
Dependent Claim
39 words
A method of coating a substrate as claimed in claim 15 wherein the oxygen is introduced into the vacuum chamber and the chamber is evacuated to produce an oxygen pressure between 0.010 and 0.070 torr. in the vacuum chamber.
Claim 20
Dependent Claim
35 words
A method of coating a substrate as claimed in claim 15 wherein the oxygen is introduced into the vacuum chamber and the chamber is evacuated to produce an oxygen pressure between 0.035 and 0.055 torr.
Claim 21
Dependent Claim
27 words
A method of coating a substrate as claimed in claim 15 wherein the glow discharge is produced having a discharge power between 0.1 watts and 20 watts.
Claim 22
Dependent Claim
20 words
A method of coating a substrate as claimed in claim 20 wherein the glow discharge power is substantially 0.5 watts.
Claim 23
Dependent Claim
69 words
A method of coating a substrate as claimed in claim 15 wherein the zinc is vaporized by providing a heated zinc source having a discharge orifice of 0.024 inches, the zinc being heated to 585 degrees Centigrade, wherein the oxygen is introduced into the vacuum chamber and the chamber is evacuated to produce an oxygen pressure. substantially about 0.050 torr., and wherein the glow discharge power is 0.5 watts.
Claim 24
Dependent Claim
22 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is silicon and the gas is hydrogen.
Claim 25
Dependent Claim
22 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is silicon and the gas is nitrogen.
Claim 26
Dependent Claim
22 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is silicon and the gas is oxygen.
Claim 27
Dependent Claim
27 words
A method of coating a substrate as claimed in claim 1 wherein the coating material is silicon and the gas is a mixture of nitrogen and oxygen.
References Cited (Backward Citations)
CA770566A
Cited
CA643527A
Cited
CA884480A
Cited
CA855193A
Cited
US2501563A
Cited
US2539149A
Cited
US2904452A
Cited
US2996418A
Cited
US3108900A
Cited
US3068510A
Cited
US3208873A
Cited
US3165405A
Cited
US3318790A
Cited
US3473959A
Cited
US3549411A
Cited
US3655438A
Cited
CA962225A
Cited
US3788894A
Cited
CA977306A
Cited
US3847658A
Cited
CA1006847A
Cited
US3900592A
Cited
CA1031720A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |