Process for making photoreceptors
Assignee: Xerox Corp
•
Filing: 1981-12-03
•
Granted: 1983-11-08
•
Expires: 2001-12-03
Abstract
Abstract A process for preparing a selenium alloy highly resistant to the development of persistant bulk space charge during prolonged, electrophotographic cycling comprising heating a mixture comprising selenium, arsenic and chlorine to a temperature between about 290° C. and about 330° C. to form a molten mixture, agitating the molten mixture to blend the components therein, discontinuing or substantially discontinuing all agitation of the mixture to achieve a quiescent state for the mixture, raising the temperature of the mixture to at least about 420° C. for at least about 30 minutes and cooling the mixture until it becomes a solid.
Inventors
- 👤 Susan L. Robinette
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:21
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08207
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
122 words
A process for preparing a photoconductive insulating alloy comprising selenium, about 0.3 percent by weight to about 0.5 percent by weight arsenic, based on the total weight of said alloy, and about 50 ppm to about 150 ppm chlorine, based on the total weight of said alloy comprising heating a mixture comprising sufficient selenium, arsenic and chlorine to a temperature between about 290° C. and about 330° C. to form a molten mixture, agitating said molten mixture to blend said selenium, arsenic and chlorine, discontinuing or substantially discontinuing all agitation of said molten mixture, heating said molten mixture to a temperature of at least about 420° C. for at least about 30 minutes, and cooling said mixture until it becomes a solid.
Claim 2
Dependent Claim
122 words
A process for preparing a photoconductive insulating alloy comprising selenium, about 0.3 percent by weight to about 0.5 percent by weight arsenic, based on the total weight of said alloy, and about 50 ppm to about 150 ppm chlorine, based on the total weight of said alloy comprising heating a mixture comprising sufficient selenium, arsenic and chlorine to a temperature between about 290° C. and about 330° C. to form a molten mixture, agitating said molten mixture to blend said selenium, arsenic and chlorine, discontinuing or substantially discontinuing all agitation of said molten mixture, heating said molten mixture to a temperature of at least about 420° C. for at least about 30 minutes, and cooling said mixture until it becomes a solid.
Claim 3
Dependent Claim
28 words
A process according to claim 1 including heating said mixture to said temperature between about 290° C. and about 330° C. in a vessel open to the atmosphere.
Claim 4
Dependent Claim
41 words
A process according to claim 1 comprising heating said molten mixture to a temperature between about 425° C. and about 500° C. for between about 30 minutes and about 3 hours after discontinuing or substantially discontinuing agitation of said molten mixture.
Claim 5
Dependent Claim
38 words
The process according to claim 3 wherein said molten mixture is heated to a temperature of about 450° C. for between about 1 hour to about 2 hours after discontinuing or substantially discontinuing agitation of said molten mixture.
Claim 6
Dependent Claim
31 words
The process according to claim 1 including agitating said molten mixture to blend said selenium, arsenic and chlorine for a period between about 30 minutes to about 1 hour, 30 minutes.
Claim 7
Dependent Claim
17 words
A process according to claim 1 including preparing said photoconductive insulating alloy in a substantially inert atmosphere.
Claim 8
Dependent Claim
36 words
A process according to claim 1 including cooling said molten mixture to a temperature between about 290° C. and about 310° C., forming said molten alloy into droplets and cooling said droplets to form solid shot.
Claim 9
Dependent Claim
42 words
A process according to claim 1 wherein said mixture heated to said temperature between about 290° C. and about 330° C. initially comprises up to about 10 percent by weight excess arsenic and up to about 10 percent by weight excess chlorine.
Claim 10
Dependent Claim
49 words
A process according to claim 1 wherein said mixture is premixed by stirring shot particles comprising high purity selenium, shot particles comprising selenium and arsenic, and shot particles comprising selenium and chlorine prior to heating said mixture to a temperature of between about 290° C. and about 300° C.
Claim 11
Dependent Claim
135 words
A process for preparing an photoconductive insulating alloy comprising selenium, about 0.3 percent by weight to about 0.5 percent by weight arsenic, based on the total weight of said alloy, and about 50 ppm to about 150 ppm chlorine, based on the total weight of said alloy comprising heating a mixture comprising sufficient selenium, arsenic, and chlorine to a temperature between about 290° C. and about 330° C. to form a molten mixture, agitating said molten mixture for between about 30 minutes and about 3 hours to blend the said selenium, arsenic and chlorine, discontinuing or substantially discontinuing all agitation of said molten mixture, heating said molten mixture to a temperature of at least about 420° C. for between about 30 minutes and about 3 hours and cooling said mixture until it becomes a solid.
Claim 12
Dependent Claim
135 words
A process for preparing an photoconductive insulating alloy comprising selenium, about 0.3 percent by weight to about 0.5 percent by weight arsenic, based on the total weight of said alloy, and about 50 ppm to about 150 ppm chlorine, based on the total weight of said alloy comprising heating a mixture comprising sufficient selenium, arsenic, and chlorine to a temperature between about 290° C. and about 330° C. to form a molten mixture, agitating said molten mixture for between about 30 minutes and about 3 hours to blend the said selenium, arsenic and chlorine, discontinuing or substantially discontinuing all agitation of said molten mixture, heating said molten mixture to a temperature of at least about 420° C. for between about 30 minutes and about 3 hours and cooling said mixture until it becomes a solid.
References Cited (Backward Citations)
US2803542A
Cited
GB1031864A
Cited
US3312548A
Cited
US3867143A
Cited
US3785806A
Cited
US3973960A
Cited
US4126457A
Cited
US4226929A
Cited
US4286035A
Cited
US4297424A
Cited
US4338387A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |