US4412980A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing a diamond sintered compact
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1982-02-25
•
Granted: 1983-11-01
•
Expires: 2002-02-25
Abstract
Abstract The invention relates to a diamond sintered compact wherein diamond crystal particles are uniformly oriented in a particular direction and the method for producing the same, and has for an object to provide a diamond sintered compact having a high thermal conductivity particularly suitable for heat sink for use in the field of electronics. According to the invention, graphite is used as carbonaceous raw material, diamond crystal particles having such elongated shape that the ratio of the length of the long axis to that of the short axis is more than 2 being synthesized in such state that the greater part of the crystal particles have their long axes uniformly oriented in a particular direction, the crystal particles being sintered in the direction of the long axes thereof so that transformation of the graphite into diamond and sintering thereof may be accomplished synchronously. The invention has for an object to obtain a diamond sintered compact suitable for the aforesaid use by degassing reaction system raw material plugged into an air permeable container by heating it in vacuum in order to intercept gaseous components causing a decrease of thermal conductivity at the time of synthesizing diamond from carbonaceous material and a catalytic metal and sintering thereof, subsequently the air permeable part of the said container being sealed by means of soldering material preliminarily placed in contact with the said container.
Inventors
- 👤 Kazuo Tsuji
- 👤 Shuji Yazu
- 👤 Akio Hara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:34
CPC Classifications
B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; H; H10; H10W; H10W99/00; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/062; B01J2203/065; B01J2203/0655; B01J2203/0675; B01J2203/0685; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
202 words
A method for producing a diamond sintered compact having diamond crystal particles uniformly oriented in a particular direction, which comprises placing a carbonaceous material as a raw material for producing diamond, and a catalytic metal for crystallizing diamond, in layered or concentric relationship to each other the catalytic metal comprising between 5 to 50 weight % of the total weight of the carbonaceous material and catalytic metal, a metal inert to synthesis of diamond or a metal having a higher melting point than the catalytic metal being interposed at the interface between the carbonaceous material and catalytic metal, subjecting the resultant assembly to temperature and pressure under conditions of a pressure higher than 65 kb, and a temperature higher by 200° C. than the eutectic temperature of the catalytic metal and carbon and lower by 100° C. than the thermodynamic equilibrium line of diamond versus graphite, the rate of temperature rise beyond the eutectic temperature being at least 100° C./min. predetermined pressure and temperature conditions within these limits being maintained for a time sufficient for formation and growth of diamond crystals and sintering of each diamond particle, thereby enabling synchronous transformation of the carbonaceous material into diamond and sintering of the diamond.
Claim 2
Independent Claim
202 words
A method for producing a diamond sintered compact having diamond crystal particles uniformly oriented in a particular direction, which comprises placing a carbonaceous material as a raw material for producing diamond, and a catalytic metal for crystallizing diamond, in layered or concentric relationship to each other the catalytic metal comprising between 5 to 50 weight % of the total weight of the carbonaceous material and catalytic metal, a metal inert to synthesis of diamond or a metal having a higher melting point than the catalytic metal being interposed at the interface between the carbonaceous material and catalytic metal, subjecting the resultant assembly to temperature and pressure under conditions of a pressure higher than 65 kb, and a temperature higher by 200° C. than the eutectic temperature of the catalytic metal and carbon and lower by 100° C. than the thermodynamic equilibrium line of diamond versus graphite, the rate of temperature rise beyond the eutectic temperature being at least 100° C./min. predetermined pressure and temperature conditions within these limits being maintained for a time sufficient for formation and growth of diamond crystals and sintering of each diamond particle, thereby enabling synchronous transformation of the carbonaceous material into diamond and sintering of the diamond.
Claim 3
Dependent Claim
36 words
The method for producing a diamond sintered compact as defined in claim 1, wherein the metal inert to synthesis of diamond is selected from the group consisting of Au, Ag, Cu, Al, Zn, Sn and Pb.
Claim 4
Dependent Claim
42 words
The method for producing a diamond sintered compact as defined in claim 1, wherein the metal having a higher melting point than the catalytic metal is selected from the group consisting of Pt, Ti, Zr, Hf, V, Ta, Nb, Mo and W.
Claim 5
Dependent Claim
36 words
The method for producing a diamond sintered compact as defined in claim 1, wherein said resultant assembly is heated, under said pressure, at a rate of 100°-1200° C./min from said eutectic temperature to said predetermined temperature.
Claim 6
Dependent Claim
103 words
The method for producing a diamond sintered compact as defined in claim 1, wherein said diamond sintered compact contains 5-30 weight % of said catalytic metal and is constituted by individual crystal particles each of which has a long axis more than 2 times the length of its short axis, the long axes of more than 50% of said crystal particles being uniformly oriented in the direction of the thickness of said sintered compact or in the direction normal thereto, said crystal particles forming a substantially continuous diamond phase by being bonded to each other in the direction of the long axes thereof.
Claim 7
Dependent Claim
31 words
The method for producing a diamond sintered compact as defined in claim 5, wherein said long axis has a length of 50-400μ, and said short axis has a length of 20-80μ.
Claim 8
Dependent Claim
32 words
The method for producing a diamond sintered compact as defined in claim 1, wherein said catalytic metal is selected from the group consisting of Fe, Ni, Co, Cr, Mn and alloys thereof.
Claim 9
Dependent Claim
34 words
The method for producing a diamond sintered compact as defined in claim 7, wherein one or two metals selected from the group consisting of Al, Ti and Zr are mixed with said catalytic metal.
Claim 10
Dependent Claim
42 words
The method for producing a diamond sintered compact as defined in claim 1, wherein the metal inert to synthesis of diamond is Au, and the weight ratio of Au is within the range of 0.1-5 wt % relative to the catalytic metal.
Claim 11
Dependent Claim
67 words
The method for producing a diamond sintered compact as defined in claim 1, wherein the metal inert to synthesis of diamond or the metal having a higher melting point than the catalytic metal is interposed between the carbonaceous material and catalytic metal by a method which comprises electroplating, vacuum evaporating, powder coating or ion sputtering said inert metal or higher melting point metal on said catalytic metal.
Claim 12
Dependent Claim
29 words
The method for producing a diamond sintered compact as defined in claim 10, wherein said inert metal or higher melting point metal is vacuum evaporated on said catalytic metal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |