Ceramic seal between spaced members such as a terminal pin and a ferrule
Assignee: PACIFIC COAST TECHNOLOGIES Inc A WA CORP
•
Filing: 1982-04-27
•
Granted: 1983-10-25
•
Expires: 2002-04-27
Abstract
Abstract Acid and alkali oxides are smelted for an extended period of time at a first elevated temperature above their melting temperatures. The smelted mixture is then quenched in water and fritted. The fritted mixture is then disposed between a pair of members which are to be hermetically sealed relative to each other. The fritted mixture is then at least partially fused in an oxygen atmosphere at a second temperature below the first temperature for a relatively short period of time. The at least partially fused mixture is then rapidly cooled in air. In this way, the mixture is provided with a partially amorphous state and a partially crystalline state. The crystals in the mixture are disposed primarily at the borders of at least a particular one of the members to be sealed. The mixture hermetically seals the two members, is resistant to acids and alkalis and inhibits the propagation of cracks. The mixture is particularly adapted to seal steels such as stainless steels and steel alloys including cobalt and molybdenum or including nickel and chromium. The mixture is also adapted to seal noble metals such as platinum and also alloys such as those including nickel.
Inventors
- 👤 James C. Kyle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:35
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/24; H; H01; H01B; H01B17/00; H01B17/26; H01B17/30; H01B17/303; H01B17/305
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
186 words
A method of providing a hermetic seal between a first member which is a steel and a second member, including the following steps: providing a mixture of acid and alkali oxides, at least one of the oxides in the mixture having properties of forming a glass, smelting the mixture at a first elevated temperature above the melting point of the oxides for an extended period of time to melt the oxides and to provide a partially amorphous and partially crystalline state in the mixture, quenching the smelted fixture in water to produce a frit, fusing the fritted mixture to the first and second members in an oxygen atmosphere at a second elevated temperature below the first elevated temperature for a minimal period of time, and rapidly cooling the fused mixture and the first and second members directly to air, thereby providing said first and said second members sealed together by a fused vitreous mixture having a partially crystalline and partially amorphous structure, with the relative amount of the crystalline structure being greater at positions adjacent the first member than at positions displaced from the first member.
Claim 2
Independent Claim
186 words
A method of providing a hermetic seal between a first member which is a steel and a second member, including the following steps: providing a mixture of acid and alkali oxides, at least one of the oxides in the mixture having properties of forming a glass, smelting the mixture at a first elevated temperature above the melting point of the oxides for an extended period of time to melt the oxides and to provide a partially amorphous and partially crystalline state in the mixture, quenching the smelted fixture in water to produce a frit, fusing the fritted mixture to the first and second members in an oxygen atmosphere at a second elevated temperature below the first elevated temperature for a minimal period of time, and rapidly cooling the fused mixture and the first and second members directly to air, thereby providing said first and said second members sealed together by a fused vitreous mixture having a partially crystalline and partially amorphous structure, with the relative amount of the crystalline structure being greater at positions adjacent the first member than at positions displaced from the first member.
Claim 3
Dependent Claim
53 words
A method as set forth in claim 1 wherein the quenching of the smelted mixture in water causes the mixture to become partially crystalline, and the subsequent fusing of the fritted mixture and the rapid cooling of the fused mixture in air causes an additional portion of the mixture to become partially crystalline.
Claim 4
Dependent Claim
22 words
A method as set forth in claim 2 wherein the partially amorphous mixture has properties of being resistant to acids and bases.
Claim 5
Dependent Claim
84 words
A method as set forth in claim 2 wherein the fusing of the fritted mixture in an oxygen atmosphere and the rapid cooling of the fused mixture in air causes the mixture to become crystalline at the surface adjacent a particular one of the first and second members and an oxygen coating to be formed on the surface of at least the particular member and a common valence bond to be formed between the fritted mixture and the oxygen coating on the particular member.
Claim 6
Dependent Claim
63 words
A method as set forth in claim 3 wherein lead oxide, boric oxide and silicon dioxide are included in the mixture to define a flux and particular oxides are included in the mixture to enhance the bond between the particular member and the partially amorphous mixture and to inhibit cracking of the partially amorphous mixture when subjected to considerable mechanical and temperature stresses.
Claim 7
Dependent Claim
40 words
A method as set forth in claim 5, wherein the particular oxides constitute manganese oxide, aluminum oxide and at least one particular oxide selected from a group consisting of cobalt oxide, nickel oxide, chromium oxide, copper oxide and vanadium oxide.
Claim 8
Dependent Claim
57 words
A method as set forth in claim 1 wherein the mixture of acid and alkali and oxides constitute the following materials a range of percentages by weight as set forth below: ______________________________________
Chemical Range of Percentage by Weight
______________________________________
Lead oxide 28-32
Silicon dioxide
38-42
Boric oxide 2-4
Aluminum oxide
1-2
Manganese oxide
Sodium oxide 13-16
______________________________________
Claim 9
Dependent Claim
51 words
A method as set forth in claim 6, wherein the particular oxides also include at least one particular oxide selected from a group consisting of zinc zirconium silicate, zirconium spinel and zirconium silicate and having a percentage by weight in the range of approximately three percent (3%) to twelve percent (12%).
Claim 10
Dependent Claim
61 words
A method as set forth in claim 6, wherein the particular oxides also include the following chemical in a range of percentages by weight as set forth below: ______________________________________
Range of Relative Percentages
Chemical by Weight
______________________________________
At least one oxide
1.5-3
selected from a group con-
sisting of cobalt oxide,
nickel oxide, chromium
oxide, copper oxide and
vanadium oxide.
______________________________________
Claim 11
Dependent Claim
42 words
A method as set forth in claim 6, wherein the particular oxides also include the following chemical in a range of percentages by weight as set forth below: ______________________________________
Range of Relative Percentages
Material by Weight
______________________________________
Molybdic oxide (MoO)
0.5-3
______________________________________
Claim 12
Dependent Claim
51 words
A method as set forth in claim 7 wherein the particular oxides also include at least one particular oxide selected from a group consisting of zinc zirconium silicate, zirconium spinel and zirconium silicate and having a percentage by weight in the range of approximately three percent (3%) to twelve percent (12%).
Claim 13
Dependent Claim
61 words
A method as set forth in claim 11 wherein the particular oxides also include the following chemical in a range of percentages by weight as set forth below: ______________________________________
Range of Relative Percentages
Chemical by Weight
______________________________________
At least one oxide
1.5-3
selected from a group con-
sisting of cobalt oxide,
nickel oxide, chromium
oxide, copper oxide and
vanadium oxide.
______________________________________
Claim 14
Dependent Claim
42 words
A method as set forth in claim 11 wherein the particular oxides also include the following chemical in a range of percentages by weight as set forth below: ______________________________________
Range of Relative Percentages
Material by Weight
______________________________________
Molybdic oxide (MoO)
0.5-3
______________________________________
Claim 15
Independent Claim
204 words
A method of forming a hermetic seal between first and second members, including the following steps: providing a mixture of acid and alkali oxides, at least one of the oxides in the mixture having properties of forming a glass and at least another one of the oxides in the mixture having properties of forming crystals, smelting the mixture at an elevated temperature of approximately 1800° F. to 1900° F. for an extended period to approximately four (4) or five (5) hours to melt the oxides and to provide a partially amorphous and partially crystalline state in the mixture, quenching the smelted mixture to produce a fit, fusing the fritted mixture to the first and second members in an oxygen atmosphere at a reduced temperature between approximately 1500° F. and 1600° F. for a reduced period of time to approximately twenty (20) to thirty (30) minutes, and rapidly cooling the first and second members and the fused mixture, thereby providing said first and said second members sealed together by a fused vitreous mixture having a partially crystalline and partially amorphous structure, with the relative amount of the crystalline structure being greater at positions adjacent the first member than at positions displaced from the first member.
Claim 16
Independent Claim
204 words
A method of forming a hermetic seal between first and second members, including the following steps: providing a mixture of acid and alkali oxides, at least one of the oxides in the mixture having properties of forming a glass and at least another one of the oxides in the mixture having properties of forming crystals, smelting the mixture at an elevated temperature of approximately 1800° F. to 1900° F. for an extended period to approximately four (4) or five (5) hours to melt the oxides and to provide a partially amorphous and partially crystalline state in the mixture, quenching the smelted mixture to produce a fit, fusing the fritted mixture to the first and second members in an oxygen atmosphere at a reduced temperature between approximately 1500° F. and 1600° F. for a reduced period of time to approximately twenty (20) to thirty (30) minutes, and rapidly cooling the first and second members and the fused mixture, thereby providing said first and said second members sealed together by a fused vitreous mixture having a partially crystalline and partially amorphous structure, with the relative amount of the crystalline structure being greater at positions adjacent the first member than at positions displaced from the first member.
Claim 17
Dependent Claim
84 words
A method as set forth in claim 14 wherein the fusing of the fritted mixture in an oxygen atmosphere and the rapid cooling of the fused mixture in air causes the mixture to become crystalline at the surface adjacent a particular one of the first and second members and an oxygen coating to be formed on the surface of at least the particular member and a common valence bond to be formed between the fritted mixture and the oxygen coating on the particular member.
Claim 18
Dependent Claim
61 words
A method as set forth in claim 15 wherein lead oxide, boric oxide and silicon dioxide are included in the mixture to define a flux and manganese oxide is included in the mixture to enhance the resistance of the fused mixture to acids and to inhibit the cracking of the fused mixture with stresses from mechanical forces or changes in temperature.
Claim 19
Dependent Claim
30 words
A method as set forth in claim 16 wherein the fused mixture has a coefficient of thermal expansion slightly greater than the coefficient of thermal expansion of the particular member.
Claim 20
Dependent Claim
35 words
A method as set forth in claim 17 wherein the particular member is oxidized at its surface and a common valence bond is produced between the surface of the particular member and the fused mixture.
Claim 21
Dependent Claim
42 words
A method as set forth in claim 18 wherein the particular member is made from a material selected from a group consisting of stainless steel or an alloy of steel and a metal selected from a group consisting of cobalt and aluminum.
Claim 22
Dependent Claim
22 words
A method as set forth in claim 16 wherein the fused mixture has an electrical resistance as high as 10 18 ohms.
Claim 23
Dependent Claim
33 words
A method as set forth as set forth in claim 16 wherein the other one of the first and second members is selected from a group consisting of noble metals and nickel alloys.
Claim 24
Dependent Claim
31 words
A method as set forth in claim 21 wherein the other member is etched at its surface and the fused mixture becomes locked in the etched surface of the other member.
Claim 25
Dependent Claim
90 words
A method as set forth in claim 14, including the additional steps of: fusing the fritted mixture again to the first and second members in an oxygen atmosphere at a reduced temperature between approximately 1500° F. and 1600° F. for an additional period of time to approximately twenty (20) to thirty (30) minutes when a hermetic seal is not produced between the first and second members and the fused mixture in the previous fusing, and rapidly cooling the first and second members and the fused mixture after such additional fusing.
References Cited (Backward Citations)
US2889952A
Cited
US2949376A
Cited
US3225132A
Cited
US3199967A
Cited
US3346357A
Cited
US3370991A
Cited
US3258350A
Cited
US3467509A
Cited
US3734702A
Cited
US3907535A
Cited
US4002799A
Cited
US3920888A
Cited
US3920172A
Cited
US4047292A
Cited
US4128697A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-24 | 1987-04-25 | 1987-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-24 | 1991-04-25 | 1991-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-24 | 1995-04-25 | 1995-10-25 | $7700.00 | Window Closed / Lapsed |