Porous electrode preparation method
Assignee: United States Department of Energy
•
Filing: 1981-09-17
•
Granted: 1983-10-18
•
Expires: 2001-09-17
Abstract
Abstract A porous sintered plaque is provided with a bimodal porosity that is especially well suited for use as an electrode within a molten carbonate fuel cell. The coarse porosity is sufficient for admitting gases into contact with the reaction surfaces while the fine porosity is wetted with and retains molten electrolyte on the reaction sites. The electrode structure is prepared by providing a very fine powder of such as nickel oxide and blending the powder with a suitable decomposable binder to form a solid mass. The mass is comminuted into agglomerate size particles substantially larger than the fine oxide particles and formed into a cohesive compact for subsequent sintering. Sintering is carried out at sufficient conditions to bind the agglomerates together into a porous structure having both coarse and fine porosity. Where lithiated nickel oxide cathodes are prepared, the sintering conditions can be moderate enough to retain substantial quantities of lithium within the electrode for adequate conductivity.
Inventors
- 👤 Richard M. Arons
- 👤 Joseph T. Dusek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:08
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9016; C; C01; C01B; C01B4/00; C04; C04B; C04B38/00; C04B38/0051; H01M4/8663; H01M4/8668; H01M4/88; H01M4/8875; H01M4/8878; H01M4/8882; H01M4/8885; C04B2111/00; C04B2111/00474; C04B2111/00853; H01M2004/8678; H01M2004/8689; H01M8/00; H01M8/14; H01M2008/147; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M2300/0051; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
134 words
A method of preparing a sintered oxide plaque having bimodal porosity for use as a substrate having large pores for a gas flow and small pores for providing a large surface area comprising: providing particulate oxide material of a first particle size; blending said particulate material with a decomposable, resinous binder to form a solid mass; comminuting the solid mass into agglomerates of a second particle size larger than said first particle size; compacting said agglomerates into a porous cohesive plaque having a coarse porosity among said agglomerates; and sintering said compacted plaque at a sufficient temperature for a sufficient time to sinter bind the particles of first size into a structure of fine porosity within said agglomerates while driving off said decomposable resinous binder but substantially maintaining said course porosity among said agglomerates.
Claim 2
Independent Claim
134 words
A method of preparing a sintered oxide plaque having bimodal porosity for use as a substrate having large pores for a gas flow and small pores for providing a large surface area comprising: providing particulate oxide material of a first particle size; blending said particulate material with a decomposable, resinous binder to form a solid mass; comminuting the solid mass into agglomerates of a second particle size larger than said first particle size; compacting said agglomerates into a porous cohesive plaque having a coarse porosity among said agglomerates; and sintering said compacted plaque at a sufficient temperature for a sufficient time to sinter bind the particles of first size into a structure of fine porosity within said agglomerates while driving off said decomposable resinous binder but substantially maintaining said course porosity among said agglomerates.
Claim 3
Dependent Claim
65 words
The method of claim 1 wherein said particulate material includes an oxide of nickel and said sintered plaque is for use as an electrode in a fuel cell employing molten carbonate electrolyte and a reactant gas, said bimodal porosity includes a first pore size sufficiently small to wettingly retain said molten carbonate and a second pore size sufficiently large to permit passage of the reactant.
Claim 4
Dependent Claim
41 words
The method of claim 2 wherein said particulate oxide of nickel is blended with a resinous binder selected from the group consisting of polyvinyl alcohol in aqueous solution and a mixture of stearic acid and acrylic ester polymers in organic solution.
Claim 5
Dependent Claim
27 words
The method of claim 2 wherein prior to blending with said binder, said particulate oxide of nickel is calcined at about 1000° C. for about one hour.
Claim 6
Dependent Claim
22 words
The method of claim 4 wherein said cohesive plaque is sintered at about 1000° C. to 1200° C. for about one hour.
Claim 7
Dependent Claim
19 words
The method of claim 5 wherein said cohesive plaque is sintered at about 1000°-1100° C. for about one hour.
Claim 8
Dependent Claim
29 words
The method of claim 2 wherein said particulate oxide of nickel has particle sizes of about 0.5 to 1 μm and said agglomerates are of about 30-50 μm size.
Claim 9
Dependent Claim
44 words
The method of claim 7 wherein about 10-30% of the void volume of said sinter and plaque has a first pore size of about 0.05 to 0.2 μm and about 25-75% of the void volume has a second pore size of about 2-20 μm.
Claim 10
Dependent Claim
22 words
The method of claim 2 wherein said agglomerates are pressed at about 7 to 14 KPa to form a porous cohesive plaque.
Claim 11
Dependent Claim
23 words
The method of claim 2 wherein a minor proportion of lithium as oxide or carbonate is incorporated into said oxide of nickel material.
Claim 12
Dependent Claim
21 words
The method of claim 10 wherein about 3-6 parts lithium are included per 100 parts of nickel in said sintered plaque.
Claim 13
Dependent Claim
82 words
An electrode prepared by the method of claim 1 for a fuel cell including molten carbonate salt as electrolyte, said electrode comprising a porous sintered plaque of NiO having a porosity of about 40-70% with a bimodal pore size, said bimodal pore size characterized by about 10-30% of the pore volume having a fine pore size in the range of 0.05 to 0.2 μm and about 25-75% of the pore volume having a coarse pore size in the range of 2-20 μm.
Claim 14
Independent Claim
137 words
A method of preparing a sintered oxide plaque of bimodal porosity comprising: forming a particulate mixture of a first particle size including a major proportion of nickel oxide and a minor proportion of lithium oxide; blending a decomposable resinous binder into said particulate mixture to form a solid mass; comminuting the solid mass into agglomerates of a second particle size larger than said first particle size; compacting said agglomerates to form a plaque having a coarse porosity among said agglomerates and a fine porosity within individual agglomerates; and heating said plaque to a sufficient sintering temperature for a sufficient time to drive off said resinous binder and to sinter bind said particles of first size while substantially maintaining said coarse porosity among said agglomerates and while substantially maintaining said minor proportion of lithium oxide within said plaque.
Claim 15
Independent Claim
137 words
A method of preparing a sintered oxide plaque of bimodal porosity comprising: forming a particulate mixture of a first particle size including a major proportion of nickel oxide and a minor proportion of lithium oxide; blending a decomposable resinous binder into said particulate mixture to form a solid mass; comminuting the solid mass into agglomerates of a second particle size larger than said first particle size; compacting said agglomerates to form a plaque having a coarse porosity among said agglomerates and a fine porosity within individual agglomerates; and heating said plaque to a sufficient sintering temperature for a sufficient time to drive off said resinous binder and to sinter bind said particles of first size while substantially maintaining said coarse porosity among said agglomerates and while substantially maintaining said minor proportion of lithium oxide within said plaque.
Claim 16
Dependent Claim
50 words
The method of claim 13 wherein said particulate mixture is formed by calcining nickel oxide particles at a temperature of 700°-1000° C. for about 1 hour but less than 6 hours followed by blending a minor proportion of particulate lithium as particulate oxide or carbonate with the nickel oxide particles.
Claim 17
Dependent Claim
22 words
The method of claim 14 wherein lithium is blended into the nickel oxide at about 3-6 parts lithium per 100 parts nickel.
Claim 18
Dependent Claim
25 words
The method of claim 15 wherein said plaque is heated to a sintering temperature of about 1000° C. to 1200° C. for about 1 hour.
References Cited (Backward Citations)
US2928891A
Cited
US3282737A
Cited
US3423247A
Cited
US3323951A
Cited
US3367801A
Cited
US3480538A
Cited
US3981749A
Cited
US3451810A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-17 | 1987-04-18 | 1987-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-17 | 1991-04-18 | 1991-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-17 | 1995-04-18 | 1995-10-18 | $7700.00 | Window Closed / Lapsed |