Closed cell polyimide foams and methods of making same
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1982-09-27
•
Granted: 1983-10-04
•
Expires: 2002-09-27
Abstract
Abstract A high temperature and flame resistant closed cell polyimide foam material and methods of making the foam. An aromatic tetracarboxylic acid dianhydride is reacted with an oxomine to produce an N-substituted imide, which is then esterfied with a suitable alcohol. The resulting liquid is dried and the dry residue is reduced to a uniform powder having particles with diameters generally in the 0.5 to 10 mm. range. The powder is preferably further dried, either before or after final size reduction, in a moderate vacuum at moderate temperature to remove any excess residual alcohol. The powder spontaneously expands to form a closed cell foam when heated to a temperature in the range of about 90° to 150° C. for a suitable period. When the powder is expanded in a closed mold, a well consolidated, uniform, closed cell foam product results. When expanded in an unrestricted manner, closed cell "macroballoons" having average diameters between about 0.4 and 15 mm. result. The closed cell foam produced has excellent flexibility and resistance to heat and flame, and does not shrink appreciably when exposed to flame.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 08:00
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/18; B32B5/20; B32B3/00; B32B3/10; B32B3/12; C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08J; C08J9/00; C08J9/02; C08J9/16; C08J9/22; C08J9/228; C08J9/236; B32B2266/00; B32B2266/08; B32B2305/00; B32B2305/02; B32B2305/024; B32B2305/30; B32B2307/00; B32B2307/30; B32B2307/306; B32B2307/3065; C08J2379/00; C08J2379/04; C08J2379/08; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/1234
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
137 words
A process for producing high temperature and flame resistant closed cell foam which comprises the steps of: reacting an oxoimine having the general formula: CH.sub.2 --(CH.sub.2).sub.x --NHCO where "X" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio thereof between about 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles into a mold; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a closed cell foam of substantial uniform density throughout the mold.
Claim 2
Dependent Claim
137 words
A process for producing high temperature and flame resistant closed cell foam which comprises the steps of: reacting an oxoimine having the general formula: CH.sub.2 --(CH.sub.2).sub.x --NHCO where "X" is a positive integer from 2 to 4, with an aromatic tetracarboxylic acid dianhydride in a mole ratio thereof between about 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; placing a suitable quantity of said particles into a mold; and heating said particles to a temperature in the range of about 90° to 150° C.; whereby said particles expand producing a closed cell foam of substantial uniform density throughout the mold.
Claim 3
Dependent Claim
64 words
The process according to claim 1 wherein said drying step is accomplished by heating the liquid at a temperature of from about 65° to 96° C. until a non-tacky solid results and further including the step of heating the dry material for about 30 to 120 min. at about 50° to 80° C. at a pressure of from about 25 to 29 in. Hg.
Claim 4
Dependent Claim
27 words
The process according to claim 1 wherein said heating to foam step is accomplished with the particles unrestrained whereby a plurality of closed cell macroballoons are produced.
Claim 5
Dependent Claim
29 words
The process according to claim 1 wherein said aromatic tetracarboxylic acid dianhydride is selected from the group consisting of 3,3', 4,4'-benzophenone tetracarboxylic acid dianhydride, pyromellitic dianhydride, and mixtures thereof.
Claim 6
Dependent Claim
23 words
The process according to claim 1 wherein said oxoimine is selected from the group consisting of caprolactam, 2-pyrrolidone or 2-piperidone and mixtures thereof.
Claim 7
Dependent Claim
11 words
The process according to claim 1 wherein said oxomine is caprolactam.
Claim 8
Dependent Claim
56 words
The process according to claim 1 wherein said reactive solvent esterifying agent is selected from the group consisting of aliphatic and aromatic alcohols, amino substituted aliphatic and aromatic alcohols, halogen substituted aliphatic and aromatic alcohols and mixtures thereof, said alcohols having up to 7 carbon atoms and having boiling points between about 75° and 100° C.
Claim 9
Dependent Claim
13 words
The process according to claim 1 wherein said reactive solvent is isopropyl alcohol.
Claim 10
Dependent Claim
28 words
The process according to claim 1 wherein from about 8 to 15 moles reactive solvent is used per mole imide and said esterification takes place at reflux temperature.
Claim 11
Dependent Claim
35 words
The process according to claim 1 wherein said diamine is selected from the group consisting of 4,4'-diaminodiphenyl methane, meta-phenylene diamine, paraphenylene diamine, 4,4'-diaminodiphenyl ether, 4-4'-diaminodiphenyl sulfone, 3,3'-diaminodiphenyl sulfone, 4-4'-diaminodiphenyl sulfide, 3,3'-diaminodiphenyl methane and mixtures thereof.
Claim 12
Dependent Claim
38 words
The process according to claim 10 wherein up to 30 mole percent of said diamine is an aliphatic diamine selected from the group consisting of 1,3-diamino propane, 1,4-diamino butane, 1,6-diamino hexane, 1-8-diamino octane, 1,12-diamono dodecane and mixtures thereof.
Claim 13
Dependent Claim
12 words
The process according to claim 1 wherein said diamine is 4,4'-diaminodiphenyl methane.
Claim 14
Dependent Claim
21 words
The process according to claim 1 further including the step of adding a surfactant to the liquid immediately prior to drying.
Claim 15
Dependent Claim
20 words
The process according to claim 1 wherein said particles have average diameters in the about 1.0 to 5.0 mm. range.
Claim 16
Dependent Claim
24 words
The process according to claim 1 wherein from about 2 to 3 volume percent powder is placed in the mold, based on mold volume.
Claim 17
Dependent Claim
43 words
The process according to claim 1 further including the step of adding a filler to said liquid composition prior to said dry drying step; wherein said filler comprising aramid fibers, graphite fibers, glass fibers, carbon fibers, graphite powders, flurocarbon powders and mixtures thereof.
Claim 18
Dependent Claim
49 words
The process according to claim 1 further including the step of adding from about 2 to 50 weight percent, based on the foamed resin, of a fire retardant to said liquid composition prior to said drying step; wherein said fire retardant comprises aluminum trihydrate, antimony oxide and mixtures thereof.
Claim 19
Dependent Claim
127 words
The process for producing a polyimide product which comprises reacting an aromatic tetracarboxylic acid dianhydride with an oxoimine having the general formula: CH.sub.2 --(CH.sub.2).sub.x --NHCO where "X" is a positive integer from 2 to 4, esterfying the resulting N-substituted imide, adding a diamine, drying the resulting solution to a non-tacky dry material and heating the dry material to polymerization temperature; the improvement wherein the material after drying is reduced to a powder having an average particle diameter of from about 0.5 to 10 mm. and further drying the powder at a temperature of from about 50° to 80° C. at a reduced pressure of about 25 to 29 in Hg.; whereby upon completion of heating said material to polymerization temperature a uniform closed cell foam is produced.
Claim 20
Dependent Claim
127 words
The process for producing a polyimide product which comprises reacting an aromatic tetracarboxylic acid dianhydride with an oxoimine having the general formula: CH.sub.2 --(CH.sub.2).sub.x --NHCO where "X" is a positive integer from 2 to 4, esterfying the resulting N-substituted imide, adding a diamine, drying the resulting solution to a non-tacky dry material and heating the dry material to polymerization temperature; the improvement wherein the material after drying is reduced to a powder having an average particle diameter of from about 0.5 to 10 mm. and further drying the powder at a temperature of from about 50° to 80° C. at a reduced pressure of about 25 to 29 in Hg.; whereby upon completion of heating said material to polymerization temperature a uniform closed cell foam is produced.
Claim 21
Dependent Claim
11 words
The foamed product prepared according to the process of claim 1.
Claim 22
Dependent Claim
11 words
The foamed product prepared according to the process of claim 14.
Claim 23
Dependent Claim
11 words
The foamed product prepared according to the process of claim 17.
Claim 24
Dependent Claim
11 words
The foamed product prepared according to the process of claim 18.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-03 | 1987-04-04 | 1987-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-03 | 1991-04-04 | 1991-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-03 | 1995-04-04 | 1995-10-04 | $7700.00 | Window Closed / Lapsed |