Method for manufacturing a field isolation structure for a semiconductor device
Assignee: Fujitsu Ltd
•
Filing: 1981-05-13
•
Granted: 1983-09-20
•
Expires: 2001-05-13
Abstract
Abstract A method for forming a field isolation structure for a semiconductor device, in which a groove is formed in a semiconductor substrate, an insulating layer is formed on the substrate at least in the groove, a glass layer or a silicon layer is formed thereon, and thereafter a high energy beam such as a laser beam is irradiated onto the glass or silicon layer to selectively heat the same thereby to melt or fluidify the layer and let the same flow into the groove is disclosed. A smooth and flat surface is obtained through the above melting process, which also prevents electrical breaks in wiring layers formed thereon. The method is particularly suited to producing small field isolation structures thus improving the integration density of the device.
Inventors
- 👤 Junji Sakurai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:29
CPC Classifications
H; H10; H10P; H10P34/00; H10P34/40; H10P34/42; H10P95/00; H10P95/04; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
117 words
A method for manufacturing a semiconductor device having a semiconductor substrate, a plurality of active elements formed in said substrate and an isolation region formed in said substrate for isolating said active elements from one another, the method comprising the steps of; forming a groove in said substrate defining said isolation region, covering said groove with an insulating layer, forming on said insulating layer at least in said groove a layer of a material capable of being fluidified when heated, and irradiating said layer of said material with an energy beam to selectively heat said layer of said material and permit the same to flow into said groove, thereby to fill up said groove with said material.
Claim 2
Independent Claim
117 words
A method for manufacturing a semiconductor device having a semiconductor substrate, a plurality of active elements formed in said substrate and an isolation region formed in said substrate for isolating said active elements from one another, the method comprising the steps of; forming a groove in said substrate defining said isolation region, covering said groove with an insulating layer, forming on said insulating layer at least in said groove a layer of a material capable of being fluidified when heated, and irradiating said layer of said material with an energy beam to selectively heat said layer of said material and permit the same to flow into said groove, thereby to fill up said groove with said material.
Claim 3
Dependent Claim
14 words
The method according to claim 1, wherein said energy beam is a laser beam.
Claim 4
Dependent Claim
13 words
The method according to claim 1, wherein said material consists of a glass.
Claim 5
Independent Claim
13 words
The method according to clalim 1, wherein said material consists of phosopho-silicate glass.
Claim 6
Independent Claim
13 words
The method according to clalim 1, wherein said material consists of phosopho-silicate glass.
Claim 7
Dependent Claim
17 words
The method according to claim 4, wherein said energy beam is a carbon dioxide gas laser beam.
Claim 8
Dependent Claim
12 words
The method according to claim 1, wheren said material consists of silicon.
Claim 9
Dependent Claim
14 words
The method according to claim 1, wherein said insulating layer consists of silicon dioxide.
Claim 10
Dependent Claim
23 words
The method according to claim 1, wherein the thickness of said layer of said material is less than the depth of said groove.
Claim 11
Dependent Claim
24 words
The method according to claim 1, wherein the thickness of said layer of said material is less than half the width of said groove.
References Cited (Backward Citations)
JPS5422168A
Cited
US4204894A
Cited
US4233091A
Cited
JPS5572052A
Cited
US4269636A
Cited
US4284659A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-09-19 | 1987-03-21 | 1987-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-09-19 | 1991-03-21 | 1991-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-09-19 | 1995-03-21 | 1995-09-20 | $7700.00 | Window Closed / Lapsed |