Silver-containing supported catalysts and catalyst intermediate products, processes for their preparation and their use

Claim 2

A supported catalyst containing silver characterized in that: (a) It has a BET specific surface area of 0.4 to 0.5 square meters per gram; (b) has a uniform continuous particle structure with spherical silver crystallites thereon which have an average diameter of 0.3 to 0.4 μm.

Claim 3

A supported catalyst according to claim 1, containing between 7 and about 30 percent by weight silver.

Claim 4

A supported catalyst according to claim 1, wherein said support comprises an alumina support.

Claim 5

A supported catalyst according to claim 3, wherein said alumina is α-alumina.

Claim 6

A supported catalyst according to claim 3, containing 0.05 to 0.5 percent by weight of an alkaline earth metal compound.

Claim 7

A supported catalyst according to claim 5, containing 0.07 to 0.3 percent by weight of an alkaline earth metal compound.

Claim 8

A supported catalyst according to claim 3, containing 0.001 to 0.03 percent by weight of alkali metal.

Claim 9

A supported catalyst according to claim 7, containing 0.003 to 0.002 percent by weight alkali metal.

Claim 10

A supported catalyst according to claim 3, wherein said support itself is a porous heat stable catalyst support.

Claim 11

A supported catalyst containing silver prepared by a process comprising: (a) impregnating a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver ions; (b) in a virtually oxygen-free atmosphere, drying the so-impregnated support and preliminarily decomposing lactic acid present in ionic or free form by heating the same at a temperature of about 50° to about 120° C., the preliminary decomposition being carried out successively in two temperature ranges from about 140° to 220° C. and from about 400° to 500° C., employing a heating up rate of 70° to 150° C. per hour for the heat-up rate between the two temperature ranges; and (c) activating the intermediate product of step (b) by heating the same in an oxygen-containing atmosphere at a temperature of at least 130° C. to at most 300° C. at a heating up rate of about 3° to about 8° C. per hour, the oxygen content being increased from about 0.4 to about 21% by volume in such a manner that the CO 2 content of the off-gas from the activation does not exceed 1% by volume.

Claim 12

A supported catalyst containing silver prepared by a process comprising: (a) impregnating a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver ions; (b) in a virtually oxygen-free atmosphere, drying the so-impregnated support and preliminarily decomposing lactic acid present in ionic or free form by heating the same at a temperature of about 50° to about 120° C., the preliminary decomposition being carried out successively in two temperature ranges from about 140° to 220° C. and from about 400° to 500° C., employing a heating up rate of 70° to 150° C. per hour for the heat-up rate between the two temperature ranges; and (c) activating the intermediate product of step (b) by heating the same in an oxygen-containing atmosphere at a temperature of at least 130° C. to at most 300° C. at a heating up rate of about 3° to about 8° C. per hour, the oxygen content being increased from about 0.4 to about 21% by volume in such a manner that the CO 2 content of the off-gas from the activation does not exceed 1% by volume.

Claim 13

A supported catalyst according to claim 10, wherein said support comprises alumina.

Claim 14

A supported catalyst according to claim 11, wherein said lactic acid contains barium and cesium as promoters.

Claim 15

A supported catalyst according to claim 11, wherein said lactic acid contains a soluble readily decomposable non-reducing compound.

Claim 16

A supported catalyst according to claim 13, wherein said soluble readily decomposable non-reducing organic compound is a sugar alcohol, or polyhydroxy acid.

Claim 17

A supported catalyst according to claim 14, wherein said sugar alcohol or polyhydroxy acid is present in said lactic acid in an amount of 30 to about 45 grams per 100 grams based upon 100% strength lactic acid.

Claim 18

A supported catalyst according to claim 11, wherein said preliminary combustion is effected until the carbon content of the preliminary decomposed product is between 0.5 to 8 percent by weight relative to the total weight of the catalyst intermediate product.

Claim 19

A supported catalyst according to claim 11, wherein a heating at a temperature from 140° to about 220° C. is effected for a period of time between 1/2 hour and 2 hours and a heating at a temperture in the range of 400° to 500° C. is effected for between 1/2 to about 2 hours.

Claim 20

An intermediate product for the preparation of a supported catalyst containing silver prepared by a process comprising the steps of: (a) impregnating a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver ions; and (b) drying the so-impregnated support in a virtually oxygen-free atmosphere at a temperature of 50° to about 120° C. to preliminarily decompose the lactic acid present in ionic form or in the free form and thereafter continuing preliminary decomposition by subjecting the so-dried composition to temperatures in two temperature ranges, from 140° to 200° C. and from 400° to about 500° C., the heating up range between the 140°-220° C. and 400° to 500° C. range being at a rate of 70° to 150° C. per hour and thereafter cooling the intermediate product in a virtually oxygen free atmosphere to about 70° to about 80° C. or below.

Claim 21

An intermediate product for the preparation of a supported catalyst containing silver prepared by a process comprising the steps of: (a) impregnating a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver ions; and (b) drying the so-impregnated support in a virtually oxygen-free atmosphere at a temperature of 50° to about 120° C. to preliminarily decompose the lactic acid present in ionic form or in the free form and thereafter continuing preliminary decomposition by subjecting the so-dried composition to temperatures in two temperature ranges, from 140° to 200° C. and from 400° to about 500° C., the heating up range between the 140°-220° C. and 400° to 500° C. range being at a rate of 70° to 150° C. per hour and thereafter cooling the intermediate product in a virtually oxygen free atmosphere to about 70° to about 80° C. or below.

Claim 22

The intermediate product of claim 18, whose carbon content is 0.5 to 8 percent by weight.

Claim 23

A process for the preparation of a supported catalyst containig silver which comprises the steps of: (a) contacting a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver; (b) drying the so-impregnated support in a virtually oxygen-free atmosphere at about 50° to about 120° C. and preliminarily decomposing the lactic acid present in ionic form or in free form by subjecting the same successively to two temperature ranges, one from about 140° to 220° C. and a second from 400° to 500° C., in a virtually oxygen-free atmosphere, the heating up rate from the temperature range of 140°-220° C. to the temperature range of 400° to 500° C. being 70° to 150° C. per hour; (c) activating the product obtained by step (b) by heating the same in an oxygen-containing atmosphere, the temperature being increased from at least 130° C. to at most 300° C. employing a heating-up rate of about 3° to about 8° C. per hour with increasing oxygen concentration from 0.4 to about 21 percent by volume in such a manner that the CO 2 content of the off-gas from the activation does not exceed 1% by volume.

Claim 24

A process for the preparation of a supported catalyst containig silver which comprises the steps of: (a) contacting a support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver; (b) drying the so-impregnated support in a virtually oxygen-free atmosphere at about 50° to about 120° C. and preliminarily decomposing the lactic acid present in ionic form or in free form by subjecting the same successively to two temperature ranges, one from about 140° to 220° C. and a second from 400° to 500° C., in a virtually oxygen-free atmosphere, the heating up rate from the temperature range of 140°-220° C. to the temperature range of 400° to 500° C. being 70° to 150° C. per hour; (c) activating the product obtained by step (b) by heating the same in an oxygen-containing atmosphere, the temperature being increased from at least 130° C. to at most 300° C. employing a heating-up rate of about 3° to about 8° C. per hour with increasing oxygen concentration from 0.4 to about 21 percent by volume in such a manner that the CO 2 content of the off-gas from the activation does not exceed 1% by volume.

Claim 25

A process according to claim 20, wherein said support comprises alumina.

Claim 26

A process according to claim 11, wherein the lactic acid contains barium and cesium.

Claim 27

A process according to claim 21, wherein the lactic acid employed is an optically active form of lactic acid.

Claim 28

A process according to claim 21, wherein at least 50% of the lactic acid employed consists of the L (+) form while the remainder is in the form of the racemate.

Claim 29

A process according to claim 21, wherein the activation is effected under pressure in a reactor employed for the preparation of an alkaline oxide.

Claim 30

A process according to claim 25, wherein the pressure within the reactor is 10-15 bars.

Claim 31

A process according to claim 21, wherein the lactic acid contains a soluble readily decomposible non-reducing organic compound.

Claim 32

A process for the preparation of catalyst intermediate product which comprises: (a) impregnating an alumina support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver; (b) drying the so-impregnated product in a virtually oxygen-free atmosphere at about 50° to about 120° C. and preliminarily decomposing the lactic acid, present in ionic form or in the free form, by subjecting it successively to temperatures in two different ranges, one of which is 140° to 220° C. and the second of which is 400° to 500° C., in a virtually oxygen-free atmosphere, employing a heat up rate from the 140°-220° C. range to the 400°-500° C. range of 70° to 150° C. per hour and thereafter cooling the so-heated support in a virtually oxygen-free atmosphere to about 70° to 80° C. or below.

Claim 33

A process for the preparation of catalyst intermediate product which comprises: (a) impregnating an alumina support whose specific surface area is at most 1 square meter per gram with lactic acid containing silver; (b) drying the so-impregnated product in a virtually oxygen-free atmosphere at about 50° to about 120° C. and preliminarily decomposing the lactic acid, present in ionic form or in the free form, by subjecting it successively to temperatures in two different ranges, one of which is 140° to 220° C. and the second of which is 400° to 500° C., in a virtually oxygen-free atmosphere, employing a heat up rate from the 140°-220° C. range to the 400°-500° C. range of 70° to 150° C. per hour and thereafter cooling the so-heated support in a virtually oxygen-free atmosphere to about 70° to 80° C. or below.