Process for the preparation of silver catalysts for the production of ethylene oxide
Assignee: Huels AG
•
Filing: 1980-03-31
•
Granted: 1981-12-15
•
Expires: 2000-03-31
Abstract
Abstract A process for preparing silver catalysts containing alkaline earth metals and alkali metals as promoters for the production of ethylene oxide by oxidizing ethylene with oxygen or oxygen-containing gases. The silver catalysts are prepared by: (a) depositing a suspension consisting of silver oxide and an aqueous solution of an organic silver salt on a porous substrate, the molar ratio of the silver in the silver oxide to the silver in the silver salt being from about 35 to 65%, and periodically increasing the pressure (decreasing the vacuum) being used during the absorption; (b) carrying out an interim drying as a thin moving bed in an inert gas atmosphere at temperatures between about 50° and 150° C. to prepare an interim product; (c) depositing a further layer of the silver-containing suspension on the interim product in the manner described in step (a), this suspension additionally containing compounds of barium and cesium, rubidium or a mixture of cesium and rubidium in sufficient amounts that the finished catalyst contains from about 0.01 to 0.25% by weight of barium and from about 0.001 to 0.05% by weight of cesium, rubidium, or a mixture of cesium and rubidium, calculated as metals; and (d) heating to temperatures from about 160° to 270° C. as a thin moving bed.
Inventors
- 👤 Erwin Vangermain
- 👤 Willi Brauckmann
- 👤 Hans-Jurgen Erberich
- 👤 Horst Ueberschaer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:14
CPC Classifications
C; C07; C07D; C07D301/00; C07D301/02; C07D301/03; C07D301/04; C07D301/08; C07D301/10; B; B01; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/66; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
283 words
In a process for the preparation of a supported silver catalyst containing alkaline earth metals and alkali metals as promoters suitable for the production of ethylene oxide by the oxidation of ethylene with gaseous oxygen or oxygen containing gases, the improvement comprising said catalyst preparation process comprising the following steps: (a) depositing in an evacuated container a suspension of silver oxide and an aqueous solution of an organic silver salt on a porous refractory substrate, the molar ratio of the silver in the silver oxide to the silver in the silver salt being from about 35 to 65% while periodically decreasing the vacuum; (b) drying the deposited silver compounds and porous refractory of (a) in a thin moving bed in an inert gas atmosphere at temperatures between about 50° and 150° C. to form an interim product; (c) depositing in said evacuated container a second suspension of silver oxide and a second aqueous solution of an organic silver salt on said interim product, the molar ratio of the silver in the silver oxide to the silver in the silver salt being from about 35 to 65%, said second suspension and said second aqueous solution suspension additionally containing compounds of barium and cesium or rubidium or a mixture of cesium and rubidium in sufficient amounts that the finished catalyst contains from about 0.01 to 0.25% by weight of barium and from about 0.001 to 0.05% by weight of cesium or rubidium or a mixture of cesium and rubidium, calculated as metals; and (d) activating the twice deposited silver compounds at temperatures of about 160° C. to 270° C. in a thin moving bed and in the presence of not more than about 8% oxygen.
Claim 2
Dependent Claim
283 words
In a process for the preparation of a supported silver catalyst containing alkaline earth metals and alkali metals as promoters suitable for the production of ethylene oxide by the oxidation of ethylene with gaseous oxygen or oxygen containing gases, the improvement comprising said catalyst preparation process comprising the following steps: (a) depositing in an evacuated container a suspension of silver oxide and an aqueous solution of an organic silver salt on a porous refractory substrate, the molar ratio of the silver in the silver oxide to the silver in the silver salt being from about 35 to 65% while periodically decreasing the vacuum; (b) drying the deposited silver compounds and porous refractory of (a) in a thin moving bed in an inert gas atmosphere at temperatures between about 50° and 150° C. to form an interim product; (c) depositing in said evacuated container a second suspension of silver oxide and a second aqueous solution of an organic silver salt on said interim product, the molar ratio of the silver in the silver oxide to the silver in the silver salt being from about 35 to 65%, said second suspension and said second aqueous solution suspension additionally containing compounds of barium and cesium or rubidium or a mixture of cesium and rubidium in sufficient amounts that the finished catalyst contains from about 0.01 to 0.25% by weight of barium and from about 0.001 to 0.05% by weight of cesium or rubidium or a mixture of cesium and rubidium, calculated as metals; and (d) activating the twice deposited silver compounds at temperatures of about 160° C. to 270° C. in a thin moving bed and in the presence of not more than about 8% oxygen.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein said drying step (b) is carried out a second time after step (c).
Claim 4
Dependent Claim
21 words
The process of claim 1, wherein the temperature difference across said thin moving bed is not more than about 10° C.
Claim 5
Dependent Claim
24 words
The process of claim 1, wherein said thin moving bed has a thickness not more than about twice the diameter of the catalyst grain.
Claim 6
Dependent Claim
26 words
The process of claim 1, wherein said periodically decreasing the vacuum is carried out once per minute with a 25 to 55 mbars reduction in vacuum.
Claim 7
Dependent Claim
42 words
The process of claim 1, wherein said porous refractory substrate is selected from the group consisting of alpha-aluminum oxide, alpha-aluminum oxide containing up to 20 percent by weight silicon dioxide and alpha-aluminum oxide containing up to 20 percent by weight silicon carbide.
References Cited (Backward Citations)
US3793231A
Cited
US4066575A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |