Abstract A low or zero magnetostriction ferromagnetic alloy is used for a magnetic recording medium. The alloy is (Fe y Co 1-y ) 1-x Cr x where y (Fe) is preferably 15-23 atomic percent of the FeCo part of the alloy. The value of x (Cr) is 7-20 atomic percent of the alloy and the remainder 1-x (FeCo) is 83-92 atomic percent of the alloy. The maximum ranges of the composition of the alloy are about as follows: Fe - 8-24 atomic percent Co - 56-83 atomic percent Cr - 7-20 atomic percent The material is adapted for use at room temperature below the Curie temperature of the specific alloy employed. When y (Fe) is 13 at. % and x (Cr) is 7 at. % the magnetostriction remains at zero, but the material is not corrosion resistant and thus it is useful for magnetic recording applications only where corrosion is not a problem. Thus the percentage of Cr must be within the range from 7-17 atomic percent. Above about 17 atomic percent of Cr, the saturation magnetization of the films falls off rather precipitously and it reaches zero at about 20 atomic percent of Cr. This has been shown for Fe 48 Co 52 in combination with percentages of Cr added to that FeCo mixture. These alloys are useful for magnetic recording media because of their low magnetostriction which increases the capacity to have assurance as to the location of a bit of information on a medium.
A thin film magnetic recording medium for storing magnetic transistions representative of data information, said medium comprising a thin film layer consisting essentially of Fe, Co, and Cr, said film having substantially zero magnetostriction in accordance with the formula (FeCo) Cr with atomic percentage ranges of about ______________________________________
element atomic percent
______________________________________
Fe 8-24
Co 56-83
Cr 7-20
______________________________________ whereby magnetic recordings can be made without altering the magnetic state of the medium in response to extraneous mechanical forces.
Claim 2
Dependent Claim
79 words
A thin film magnetic recording medium for storing magnetic transistions representative of data information, said medium comprising a thin film layer consisting essentially of Fe, Co, and Cr, said film having substantially zero magnetostriction in accordance with the formula (FeCo) Cr with atomic percentage ranges of about ______________________________________
element atomic percent
______________________________________
Fe 8-24
Co 56-83
Cr 7-20
______________________________________ whereby magnetic recordings can be made without altering the magnetic state of the medium in response to extraneous mechanical forces.
Claim 3
Dependent Claim
61 words
A medium in accordance with claim 1 wherein said alloy comprises (Co x Fe y ) 93 Cr 7 with about 7 atomic percent Cr and about 93 atomic percent of (Co x Fe y ) where x is about 85 atomic percent for an overall percentage of about ______________________________________
element atomic percent
______________________________________
Co 79
Fe 14
Cr 7
______________________________________
Claim 4
Dependent Claim
72 words
A medium in accordance with claim 1 wherein said alloy comprises (Co x Fe y ) 90 Cr 10 with about 10 atomic percent Cr and about 90 atomic percent of (Co x Fe y ) where x is about 78 atomic percent of Co and y is about 22 atomic percent of Fe, for an overall percentage of about ______________________________________
element atomic percent
______________________________________
Co 70
Fe 20
Cr 10
______________________________________
Claim 5
Dependent Claim
59 words
A medium in accordance with claim 1 wherein said alloy comprises (Co x Fe y ) 86 Cr 14 with about 14 atomic percent Cr and about 77 atomic percent of Co and y is about 23 atomic percent of Fe, for an overall percentage of about ______________________________________
element atomic percent
______________________________________
Co 66
Fe 20
Cr 14
______________________________________
Claim 6
Dependent Claim
35 words
A medium in accordance with claim 1 having between about 8 and 17 atomic percent Cr, between about 12.5 and 21 atomic percent Fe, and with the remainder between 64 and 78 atomic percent Co.