Methods of piercing and enlarging elongate metal members such as seamless tubes
Assignee: Columbiana Foundry Co
•
Filing: 1976-07-06
•
Granted: 1977-07-12
•
Expires: 1996-07-06
Abstract
Abstract A method is provided for piercing and enlarging metal members at high temperatures, particularly members containing slag inclusion, by the steps of urging said member, over a piercer or enlarger point by rolling whereby said point passes through and forms an axial opening in the ingot, said point being formed of an alloy comprising 0.015% to 2% carbon, about 5% to 65% cobalt, about 15% to 35% chromium and up to about 30% iron and amounts of boron, nickel, silicon molybdenum, vanadium, aluminum, tantalum, tungsten, titanium, copper and columbium for imparting the qualities generally associated therewith without detrimentally affecting the hot hardness and resistance to erosion of said alloy at said elevated temperature.
Inventors
- 👤 Lewis A. Way
- 👤 Robert C. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:54
CPC Classifications
B; B21; B21B; B21B25/00; B21B19/00; B21B19/02; B21B19/04
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
127 words
A method of piercing and enlarging elongated metal members such as seamless tube, particularly such members containing slag inclusions comprising the steps of urging said metal member at an elevated temperature above about 1750° F. over one of a piercing and enlarging point by rollig whereby said point passes through and forms an axial opening in the metal member, said point being formed of an alloy consisting essentially of 0.015% to 2% carbon, about 5% to 65% cobalt, about 15% to 35% chromium, up to about 30% iron and amounts of boron, nickel, silicon, molybdenum, vanadium aluminum, tantalum, tungsten, titanium, copper and columbium for imparting the qualities generally associated therewith without detrimentally affecting the hot hardness and resistance to erosion of said alloy at said elevated temperature.
Claim 2
Independent Claim
127 words
A method of piercing and enlarging elongated metal members such as seamless tube, particularly such members containing slag inclusions comprising the steps of urging said metal member at an elevated temperature above about 1750° F. over one of a piercing and enlarging point by rollig whereby said point passes through and forms an axial opening in the metal member, said point being formed of an alloy consisting essentially of 0.015% to 2% carbon, about 5% to 65% cobalt, about 15% to 35% chromium, up to about 30% iron and amounts of boron, nickel, silicon, molybdenum, vanadium aluminum, tantalum, tungsten, titanium, copper and columbium for imparting the qualities generally associated therewith without detrimentally affecting the hot hardness and resistance to erosion of said alloy at said elevated temperature.
Claim 3
Dependent Claim
70 words
A method of piercing and enlarging metal members as claimed in claim 1 wherein the alloy consists essentially of about 0.015% to 2% carbon, about 5% to 65% cobalt, about 15% to 35% chromium, up to about 30% iron, about 2% to 20% nickel, about 1.5% to 6% molybdenum, about 0.003% to 0.01% boron, up to about 0.25% titanium, about 15% to 18% tungsten and up to about 1.5% silicon.
Claim 4
Dependent Claim
65 words
A method of piercing and enlarging metal members as claimed in claim 1 wherein the alloy consists essentially of about 0.015% to 2% carbon, about 5% to 65% cobalt, about 15% to 35% chromium, up to about 30% iron, about 2% to 20% nickel, about 1.5% to 6% molybdenum, about 0.003% to 0.01% boron, up to about 0.25% titanium and up to about 1.5% silicon.
Claim 5
Dependent Claim
66 words
A method of piercing and enlarging metal members as claimed in claim 1 wherein the alloy consists essentially of about 0.02% to 0.71% carbon, about 10.6% to 61.35% cobalt, about 18.8% to 27.5% chromium, up to about 2.8% iron, about 2.3% to about 16.9% nickel, up to about 5.9% molybdenum, up to about 0.01% boron, up to about 0.22% titanium and up to about 17.88% tungsten.
Claim 6
Dependent Claim
35 words
A method of piercing and enlarging metal members as claimed in claim 4 wherein the alloy contains about 1.8% to 5.9% molybdenum, about 0.0035% to bout 0.01% boron and about 15.05% to about 17.88% tungsten.
References Cited (Backward Citations)
US1903952A
Cited
US2197098A
Cited
US2126750A
Cited
US2263020A
Cited
US2799003A
Cited
US3962897A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-07-11 | 1981-01-10 | 1981-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-07-11 | 1985-01-10 | 1985-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-07-11 | 1989-01-10 | 1989-07-12 | $7700.00 | Window Closed / Lapsed |