Method for making silicon coated polycarbonates and article obtained therefrom
Assignee: General Electric Co
•
Filing: 1981-10-23
•
Granted: 1983-07-26
•
Expires: 2001-10-23
Abstract
Abstract A method is provided for improving the weatherability of a polycarbonate substrate by initially treating the surface of the polycarbonate substrate with a solution of a hydrolyzed silylated organic U.V. screen followed by the application of a curable silicone hardcoat composition onto the treated substrate.
Inventors
- 👤 Ta-Yen Ching
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:33
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/043; C08J7/0427; C08J7/046; C08J2369/00; C08J2483/00; C08J2483/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
108 words
A method for making a composite of a polycarbonate substrate and a silicon hardcoat having improved weatherability which comprises, (1) treating a polycarbonate substrate with a solution of the hydrolysis product of a silylated organic UV screen which has been allowed to hydrolyze for a period not exceeding about three days and curing the applied hydrolyzate on the treated substrate at a temperature of from 75° C. to 150° C. and (2) applying onto the treated polycarbonate substrate a silicone hardcoat composition and thereafter heating the resulting composite to a temperature in the range of from 75° C. to 150° C. until the applied hardcoat composition is cured.
Claim 2
Independent Claim
108 words
A method for making a composite of a polycarbonate substrate and a silicon hardcoat having improved weatherability which comprises, (1) treating a polycarbonate substrate with a solution of the hydrolysis product of a silylated organic UV screen which has been allowed to hydrolyze for a period not exceeding about three days and curing the applied hydrolyzate on the treated substrate at a temperature of from 75° C. to 150° C. and (2) applying onto the treated polycarbonate substrate a silicone hardcoat composition and thereafter heating the resulting composite to a temperature in the range of from 75° C. to 150° C. until the applied hardcoat composition is cured.
Claim 3
Dependent Claim
278 words
A method in accordance with claim 1, were the silylated organic UV screen has the formula, ##STR10## where R 1 is a C.sub.(1-13) monovalent hydrocarbon radical or substituted monovalent hydrocarbon radical, R 2 is a C.sub.(1-8) aliphatic organic radical selected from alkyl radicals, alkyl ether radicals, alkyl ester radicals, alkyl ketone radicals, alkylene radicals and C.sub.(7-13) aralkyl radicals, Q is selected from ##STR11## Y is H or OH, Z is H, OH, OQ 1 or OM, where at least one Z is OH if Y is H, M is C m H 2m+1 and m is an integer equal to 1 to 18 inclusive, X is selected from ##STR12## R 3 is a member selected from the class consisting of hydrogen, C.sub.(1-8) alkoxy, carboxy, halogen, hydroxy, amino, carbethoxy and D-CH 2 (CH 2 ) n Si(OR 2 ) 3 , R 4 is a member selected from the class consisting of hydrogen, halogen, hydroxy, C.sub.(1-8) alkyl and C.sub.(1-8) alkoxy, R 5 is a member selected from the class consisting of hydrogen, C.sub.(1-8) alkyl, C.sub.(1-8) alkoxy and halogen, D is selected from --NH-- or O, X 1 is selected from R 3 or ##STR13## Y 1 is R 5 or --CH 2 (CH 2 ) n (OR 2 ) 3 , Q 1 is --CH 2 (CH 2 ) n Si(R 1 ) x (OR 2 ) y , Z 1 is ##STR14## x is 0, 1 or 2, y is 1, 2 or 3, x+y is 3 and n is 0, 1 or 2, a and b are integers equal to 1 to 3 inclusive, a+b is equal to 3, and c is equal to 0 or 1.
Claim 4
Dependent Claim
104 words
A method in accordance with claim 1, where the silicone hardcoat comprises a dispersion of colloidal silica in an aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH) 3 , where R is selected from the group consisting of C.sub.(1-3) alkyl and C.sub.(6-13) aryl, at least 70 weight percent of the silanol being CH 3 SI(OH) 3 , said composition containing 10 to 50 weight percent solids, said solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition having a pH of from 3.5 to 8.0.
Claim 5
Dependent Claim
15 words
A method in accordance with claim 1, where the silylated organic UV screen is 4-[γ(triethoxysilyl)propoxy]-2-hydroxybenzophenone.
Claim 6
Dependent Claim
11 words
A polycarbonate silicone hardcoat composite made in accordance with claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-25 | 1987-01-24 | 1987-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-25 | 1991-01-24 | 1991-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-25 | 1995-01-24 | 1995-07-26 | $7700.00 | Window Closed / Lapsed |