Novel compositions and process
Assignee: Dow Chemical Co
•
Filing: 1982-06-07
•
Granted: 1983-05-24
•
Expires: 2002-06-07
Abstract
Abstract Polyurethanes having a two phase morphology and characterized by high impact strength and, optionally, high modulus are obtained by reaction of 4,4'-methylenebis(phenyl isocyanate) and modified forms thereof with an aliphatic glycol extender and a blend of at least two polyoxypropylene-polyoxyethylene polyols both of which have average functionalities in the range of 2 to 4, one of which has a molecular weight in the range of about 3000 to 10,000 and contains at least 23 percent by weight of ethylene oxide residues and the other has a molecular weight in the range of about 750 to about 2000 and contains at least 45 percent by weight of ethylene oxide. The two or more such polyols are employed in proportions such that the aliphatic glycol extender is completely miscible with said polyols if blended together.
Inventors
- 👤 Louis M. Alberino
- 👤 Robert J. Lockwood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:05
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4804; C08G18/4816; C08G18/4812; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G2120/00; C08G2130/00; Y; Y10; Y10S; Y10S521/00; Y10S521/914
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
140 words
In a process for the preparation of a polyurethane by reaction of an organic polyisocyanate, a polyol and low molecular weight aliphatic glycol extender the improvement which comprises employing as the polyol component a mixture which comprises; (a) a polyoxypropylene polyoxyethylene polyol having an average functionality from 2 to 4, a molecular weight in the range of about 3,000 to about 10,000 and containing at least 23 percent by weight of ethylene oxide residues; and (b) a polyoxypropylene polyoxyethylene polyol having an average functionality from 2 to 4, a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide; the proportions by weight of the components (a) and (b) being adjusted so that the aliphatic glycol extender is completely miscible with said mixture of components (a) and (b).
Claim 2
Dependent Claim
140 words
In a process for the preparation of a polyurethane by reaction of an organic polyisocyanate, a polyol and low molecular weight aliphatic glycol extender the improvement which comprises employing as the polyol component a mixture which comprises; (a) a polyoxypropylene polyoxyethylene polyol having an average functionality from 2 to 4, a molecular weight in the range of about 3,000 to about 10,000 and containing at least 23 percent by weight of ethylene oxide residues; and (b) a polyoxypropylene polyoxyethylene polyol having an average functionality from 2 to 4, a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide; the proportions by weight of the components (a) and (b) being adjusted so that the aliphatic glycol extender is completely miscible with said mixture of components (a) and (b).
Claim 3
Dependent Claim
15 words
A process in accordance with claim 1 wherein the aliphatic glycol extender is ethylene glycol.
Claim 4
Dependent Claim
36 words
A process in accordance with claim 2 wherein the components (a) and (b) are employed in a ratio by weight of from 0.10 to 4.0 parts of the component (b) per part of the component (a).
Claim 5
Dependent Claim
14 words
A process in accordance with claim 1 wherein the organic polyisocyanate is 4,4'-methylenebis(phenyl isocyanate).
Claim 6
Dependent Claim
22 words
A process in accordance with claim 4 wherein the 4,4'-methylenebis(phenyl isocyanate) is in a form which is a liquid at 15° C.
Claim 7
Dependent Claim
136 words
In a process for the preparation of a polyurethane using a reaction injection molding technique in which an organic polyisocyanate, a polyol and a low molecular weight aliphatic glycol extender are brought together and reacted, the improvement which comprises employing as the polyol component a mixture which comprises: (a) a polyoxypropylene polyoxyethylene triol having a molecular weight in the range of about 3,000 to about 10,000 containing at least 23 percent by weight of ethylene oxide residues; and (b) a polyoxypropylene polyoxyethylene diol having a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide; the proportions by weight of the components (a) and (b) being adjusted so that the aliphatic glycol extender is completely miscible with said mixture of components (a) and (b).
Claim 8
Dependent Claim
136 words
In a process for the preparation of a polyurethane using a reaction injection molding technique in which an organic polyisocyanate, a polyol and a low molecular weight aliphatic glycol extender are brought together and reacted, the improvement which comprises employing as the polyol component a mixture which comprises: (a) a polyoxypropylene polyoxyethylene triol having a molecular weight in the range of about 3,000 to about 10,000 containing at least 23 percent by weight of ethylene oxide residues; and (b) a polyoxypropylene polyoxyethylene diol having a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide; the proportions by weight of the components (a) and (b) being adjusted so that the aliphatic glycol extender is completely miscible with said mixture of components (a) and (b).
Claim 9
Dependent Claim
38 words
A process in accordance with claim 6 wherein the aliphatic glycol extender is ethylene glycol and said extender is incorporated into the blend of said components (a) and (b) prior to reaction of said blend with said polyisocyanate.
Claim 10
Dependent Claim
16 words
A process in accordance with claim 6 or 7 wherein the organic polyisocyanate is 4,4'-methylenebis(phenyl isocyanate).
Claim 11
Dependent Claim
22 words
A process in accordance with claim 8 wherein the 4,4'-methylenebis(phenyl isocyanate) is in a form which is a liquid at 15° C.
Claim 12
Dependent Claim
49 words
A process in accordance with claim 6 wherein component (a) has a molecular weight of about 6,500 and contains approximately 27 percent by weight of ethylene oxide residues and component (b) has a molecular weight of about 1,000 and contains approximately 50 percent by weight of ethylene oxide residues.
Claim 13
Dependent Claim
168 words
In a process for the preparation of an elastomeric polyurethane utilizing two reaction Streams A and B which are brought together and reacted using a reaction injection molding technique said Stream A comprising an organic polyisocyanate and said Stream B comprising a blend of polyol and low molecular weight aliphatic glycol extender, the improvement comprising employing as Stream B a homogeneous blend of from 5 to 50 parts by weight, per 100 parts by weight of said blend, of aliphatic glycol extender the remainder of said blend comprising a mixture of a polyoxypropylene polyoxyethylene triol having a molecular weight in the range of about 3,000 to about 10,000 and containing at least 23 percent by weight of ethylene oxide residues and a polyoxypropylene polyoxyethylene diol having a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide, said triol and said diol being present in such proportions that said aliphatic glycol extender is completely miscible therein.
Claim 14
Dependent Claim
168 words
In a process for the preparation of an elastomeric polyurethane utilizing two reaction Streams A and B which are brought together and reacted using a reaction injection molding technique said Stream A comprising an organic polyisocyanate and said Stream B comprising a blend of polyol and low molecular weight aliphatic glycol extender, the improvement comprising employing as Stream B a homogeneous blend of from 5 to 50 parts by weight, per 100 parts by weight of said blend, of aliphatic glycol extender the remainder of said blend comprising a mixture of a polyoxypropylene polyoxyethylene triol having a molecular weight in the range of about 3,000 to about 10,000 and containing at least 23 percent by weight of ethylene oxide residues and a polyoxypropylene polyoxyethylene diol having a molecular weight in the range of about 750 to about 2,000 and containing at least 45 percent by weight of ethylene oxide, said triol and said diol being present in such proportions that said aliphatic glycol extender is completely miscible therein.
Claim 15
Dependent Claim
102 words
A process in accordance with claim 11 wherein said Stream B comprises a blend of from 7.5 to 25 parts, per 100 parts of the blend, of ethylene glycol, the remainder of said blend comprising a mixture of a polyoxypropylene polyoxyethylene triol having a molecular weight of about 6,500 and containing approximately 27 percent by weight of ethylene oxide residues and a polyoxypropylene polyoxyethylene glycol having a molecular weight of about 1,000 and containing approximately 50 percent by weight of ethylene oxide residues said triol and said diol being present in such proportions that said aliphatic glycol extender is completely miscible therein.
References Cited (Backward Citations)
US3857800A
Cited
US3798200A
Cited
US3963681A
Cited
US3945939A
Cited
US4065410A
Cited
US4273884A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-23 | 1986-11-22 | 1987-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-23 | 1990-11-22 | 1991-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-23 | 1994-11-22 | 1995-05-24 | $7700.00 | Window Closed / Lapsed |