Method for producing a cordierite body
Assignee: Soken Inc
•
Filing: 1981-08-04
•
Granted: 1983-05-24
•
Expires: 2001-08-04
Abstract
Abstract A method for producing a cordierite body having isotropic coefficient of thermal expansion comprises the steps of preparing a batch by mixing and kneading particles of fired talc, alumina supplying substance such as alumina and aluminum hydroxide, and silica supplying substance such as silica and kaoline, anisostatically forming the batch and drying and firing the obtained formed body.
Inventors
- 👤 Kazuhiro Inoguchi
- 👤 Tomohiko Nakanishi
- 👤 Kunio Okamoto
- 👤 Mitsuru Asano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:21
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/195
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
85 words
A method for producing a cordierite body comprising the steps of: (a) preparing a batch by mixing and kneading raw materials composed of magnesia, alumina and silica-supplying substances, the magnesia supplying substance composed of particles of fired talc produced by delaminating a block of raw talc into plate-shaped particles, firing said plate-shaped particles and pulverizing said fired particles into fine, isodimensional particles; (b) anisostatically forming said batch into a formed body; and thereafter (c) drying and firing said formed body to produce a cordierite body.
Claim 2
Independent Claim
85 words
A method for producing a cordierite body comprising the steps of: (a) preparing a batch by mixing and kneading raw materials composed of magnesia, alumina and silica-supplying substances, the magnesia supplying substance composed of particles of fired talc produced by delaminating a block of raw talc into plate-shaped particles, firing said plate-shaped particles and pulverizing said fired particles into fine, isodimensional particles; (b) anisostatically forming said batch into a formed body; and thereafter (c) drying and firing said formed body to produce a cordierite body.
Claim 3
Dependent Claim
33 words
A method according to claim 1, wherein: said alumina supplying substance is at least one of aluminum hydroxide and alumina; and said silica supplying substance is at least one of silica and kaolin.
Claim 4
Dependent Claim
18 words
A method according to claim 1, wherein: said batch contains 30 to 45% by weight of fired talc.
Claim 5
Dependent Claim
19 words
A method according to claim 1, wherein: said batch is anisostatically formed into said formed body by extrusion forming.
Claim 6
Dependent Claim
21 words
A method according to claim 1, wherein: said formed body is fired in step (c) at 1340° C. to 1460° C.
Claim 7
Dependent Claim
23 words
A method according to claim 1, wherein: said fired particles are pulverized so as to have average diameter of not more than 50μ.
Claim 8
Dependent Claim
29 words
A method according to claim 1 wherein: said fired particles are pulverized so as to have average diameter of not more than 50% of that of said fired particles.
Claim 9
Dependent Claim
18 words
A method according to claim 1, wherein: said plate-shaped particles are fired at 900° C. to 1400° C.
Claim 10
Independent Claim
87 words
A method for producing a cordierite body having a honeycomb structure, said method comprising the steps of: (a) mixing and kneading raw materials containing fired, fine, isodimensional talc particles not greater than about 50 microns in size and particles of alumina and silica supplying substance to form a batch; (b) extruding said batch by means of an extrusion die provided with grid-shaped extrusion slots into a honeycomb structure having a large number of open passages separated by thin walls; and (c) drying and firing said honeycomb structure.
Claim 11
Independent Claim
87 words
A method for producing a cordierite body having a honeycomb structure, said method comprising the steps of: (a) mixing and kneading raw materials containing fired, fine, isodimensional talc particles not greater than about 50 microns in size and particles of alumina and silica supplying substance to form a batch; (b) extruding said batch by means of an extrusion die provided with grid-shaped extrusion slots into a honeycomb structure having a large number of open passages separated by thin walls; and (c) drying and firing said honeycomb structure.
Claim 12
Independent Claim
156 words
A method of producing a cordierite body exhibiting improved thermal shock resistance and a low coefficient of thermal expansion in all directions, said method comprising the sequential steps of: (a) firing delaminated talc particles at a temperature of greater than 900° C. to remove water and thermally stabilize the talc particles; and thereafter, (b) pulverizing the thus fired talc particles to produce fine, isodimensional particles, provided that the pulverizing is conducted so that the ratio of: ##EQU2## does not exceed 50%; (c) preparing a formable batch by mixing and kneading together alumina-containing and silica-containing materials together with from 30 to 45% by weight of the fired fine particles of step (b); (d) anisostatically forming the batch into a formed body, and thereafter (e) drying and firing the formed body, the resulting cordierite body having a coefficient of thermal expansion in all directions no greater than 16.0×10 -7 /°C. over the range of 25° to 1000° C.
Claim 13
Independent Claim
156 words
A method of producing a cordierite body exhibiting improved thermal shock resistance and a low coefficient of thermal expansion in all directions, said method comprising the sequential steps of: (a) firing delaminated talc particles at a temperature of greater than 900° C. to remove water and thermally stabilize the talc particles; and thereafter, (b) pulverizing the thus fired talc particles to produce fine, isodimensional particles, provided that the pulverizing is conducted so that the ratio of: ##EQU2## does not exceed 50%; (c) preparing a formable batch by mixing and kneading together alumina-containing and silica-containing materials together with from 30 to 45% by weight of the fired fine particles of step (b); (d) anisostatically forming the batch into a formed body, and thereafter (e) drying and firing the formed body, the resulting cordierite body having a coefficient of thermal expansion in all directions no greater than 16.0×10 -7 /°C. over the range of 25° to 1000° C.
Claim 14
Dependent Claim
29 words
The method of claim 10 in which the talc particles are fired in step (a) at a temperature in the range of about 900° C. to about 1400° C.
Claim 15
Dependent Claim
19 words
The method of claim 10 in which the pulverizing ratio of step (b) is about 30% to about 10%.
Claim 16
Dependent Claim
21 words
The method of claim 10 or 12 in which the pulverized particles have an average diameter not greater than 50 microns.
Claim 17
Dependent Claim
39 words
A thermally stable, thermal shock resistant extruded cordierite body having a coefficient of thermal expansion in all directions not greater than 16.0×10 -7 /°C. over the range of 25° to 1000° C. produced by the method of claim 10.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-23 | 1986-11-22 | 1987-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-23 | 1990-11-22 | 1991-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-23 | 1994-11-22 | 1995-05-24 | $7700.00 | Window Closed / Lapsed |