Method of preparing crack-free monolithic polycrystalline cordierite substrates
Assignee: Corning Glass Works
•
Filing: 1974-05-28
•
Granted: 1977-01-04
•
Expires: 1994-05-28
Abstract
Abstract Cracking of large monolithic cordierite segments and in particular monolithic honeycombed substrates having a matrix of thin walls forming a multiplicity of open ended cells extending from one end of the substrate to the other end is reduced or eliminated by limiting the amount of raw clay used in formulating the clay-talc-alumina raw material batch. The raw clay may be eliminated entirely but is preferably at least 10% of the whole batch and not more than 31% of the whole batch with the balance of the clay constituent to the raw material batch being calcined clay. The raw material batch is preferably formulated to yield at least 90% cordierite phase upon reaction during sintering.
Inventors
- 👤 Rodney I. Frost
- 👤 Irwin M. Lachman
- 👤 Paul H. Rieth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:02
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/195; B; B01; B01J; B01J37/00; B01J37/0009
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
171 words
A method of producing a crack-free monolithic polycrystalline sintered ceramic substrate having a matrix of thin walls forming a multiplicity of open-ended cells extending from one end of the substrate to the other end thereof and predominantly consisting of cordierite, the method comprising the steps of formulating a batch of ceramic raw materials, blending, plasticizing and forming the batch into a green body having said matrix, and drying and sintering the green body, and wherein the improvement comprises: formulating the batch of raw materials consisting essentially of a mixture of raw clay, calcined clay, talc selected from raw talc and calcined talc, and alumina selected from hydrated alumina and calcined alumina, each of the raw materials included in the batch in an effective amount, in combination with the other raw materials therein, for yielding the sintered substrate whose predominant crystal phase is cordierite, and the effective amount of clay consists of, based by weight on the whole batch, 10-31% raw clay with the balance being at least about 12% calcined clay.
Claim 2
Independent Claim
171 words
A method of producing a crack-free monolithic polycrystalline sintered ceramic substrate having a matrix of thin walls forming a multiplicity of open-ended cells extending from one end of the substrate to the other end thereof and predominantly consisting of cordierite, the method comprising the steps of formulating a batch of ceramic raw materials, blending, plasticizing and forming the batch into a green body having said matrix, and drying and sintering the green body, and wherein the improvement comprises: formulating the batch of raw materials consisting essentially of a mixture of raw clay, calcined clay, talc selected from raw talc and calcined talc, and alumina selected from hydrated alumina and calcined alumina, each of the raw materials included in the batch in an effective amount, in combination with the other raw materials therein, for yielding the sintered substrate whose predominant crystal phase is cordierite, and the effective amount of clay consists of, based by weight on the whole batch, 10-31% raw clay with the balance being at least about 12% calcined clay.
Claim 3
Dependent Claim
67 words
The method of producing a substrate according to claim 1 wherein the substrate is generally cylindrical, 3-6 inches in diameter, and 10-40 inches long, and wherein the raw materials are selected in an effective amount for yielding a sintered substrate with a chemical oxide analysis of, by weight, 12.5-15.5% MgO, 34.2-39.5% Al 2 O 3 and 48.0-51.6% SiO 2 and at least 90% by volume cordierite phase.
Claim 4
Dependent Claim
19 words
The method of claim 2 wherein the raw clay is selected from laminated kaolin, delaminated kaolin, and mixtures thereof.
Claim 5
Dependent Claim
23 words
The method of claim 2 wherein the raw materials are selected from raw clay, calcined clay, raw talc, calcined talc and calcined alumina.
Claim 6
Dependent Claim
53 words
The method of claim 4 wherein the improvement further includes firing the green body to a peak temperature and for a time sufficient to produce the predominent cordierite phase in the sintered substrate and wherein the rate of temperature increase in reaching the peak temperature does not exceed about 100° C per hour.
Claim 7
Dependent Claim
19 words
The method of claim 4 wherein the raw clay is selected from laminated kaolin, delaminated kaolin, and mixtures thereof.
References Cited (Backward Citations)
US2731355A
Cited
US2786772A
Cited
US2864919A
Cited
GB836059A
Cited
US3026212A
Cited
US3146115A
Cited
US3389001A
Cited
US3473999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-04 | 1980-07-05 | 1981-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-04 | 1984-07-05 | 1985-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-04 | 1988-07-05 | 1989-01-04 | $7700.00 | Window Closed / Lapsed |