Assignee: United States, NATIONAL AERONAUTICS AND SPACE ADINISTRATION, Administrator of
•
Filing: 1981-07-10
•
Granted: 1983-05-24
•
Expires: 2001-07-10
Abstract
Abstract This invention relates to a method of carbonizing polyacrylonitrile fibers (PAN fibers) by exposing the fibers at an elevated temperature to an oxidizing atmosphere, then exposing the oxidized fibers to an atmosphere of an inert gas such as nitrogen containing a carbonaceous material such as acetylene. The fibers are preferably treated with an organic compound, for example benzoic acid, before the exposure to an oxidizing atmosphere. The invention also relates to the resulting fibers. The treated fibers have enhanced tensile strength.
Inventors
- 👤 Domenick E. Cagliostro
- 👤 Narcinda R. Lerner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:02
CPC Classifications
B; B82; B82Y; B82Y30/00; D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/20; D01F9/21; D01F9/22; D01F9/127; D01F9/1273; D01F9/1275
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
114 words
A method of treating polyacrylonitrile fibers to enhance their tensile strengths which comprises the following steps: (a) subjecting the fibers to oxidation by exposure to molecular oxygen at a temperature of about 220° to 350° C. for a period of time not exceeding about 3 hours, (b) then exposing the thus treated fibers to a carbonizing temperature not greater than about 1100° C. in a non-oxidizing atmosphere containing an added gaseous active carbon component in sufficient amount to enhance the tensile strength of the carbonized fiber as compared to the same fibers carbonized similarly in an inert atmosphere, said active carbon compound being one which undergoes decomposition at a substantial rate below 1000° C.
Claim 2
Independent Claim
114 words
A method of treating polyacrylonitrile fibers to enhance their tensile strengths which comprises the following steps: (a) subjecting the fibers to oxidation by exposure to molecular oxygen at a temperature of about 220° to 350° C. for a period of time not exceeding about 3 hours, (b) then exposing the thus treated fibers to a carbonizing temperature not greater than about 1100° C. in a non-oxidizing atmosphere containing an added gaseous active carbon component in sufficient amount to enhance the tensile strength of the carbonized fiber as compared to the same fibers carbonized similarly in an inert atmosphere, said active carbon compound being one which undergoes decomposition at a substantial rate below 1000° C.
Claim 3
Dependent Claim
43 words
The method of claim 1 wherein step (a) is preceded by treatment of the fibers at a temperature not exceeding about 190° C. with a liquid or gaseous organic compound capable of enhancing the effect of the active carbon component on tensile strength.
Claim 4
Dependent Claim
13 words
The method of claim 2 wherein the organic compound is molten benzoic acid.
Claim 5
Dependent Claim
13 words
The method of claim 3 wherein the active carbon component is a hydrocarbon.
Claim 6
Dependent Claim
24 words
The method of claim 4 wherein the atmosphere used in step (b) is a gaseous mixture of inert gas and such active carbon component.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-23 | 1986-11-22 | 1987-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-23 | 1990-11-22 | 1991-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-23 | 1994-11-22 | 1995-05-24 | $7700.00 | Window Closed / Lapsed |