Coating composition for fibrous polyolefin sheets
Assignee: EIDU PONT DE NEMOURS AND COMPANY WILMINGTON DE A CORPOF DE
•
Filing: 1981-06-29
•
Granted: 1983-05-10
•
Expires: 2001-06-29
Abstract
Abstract A coating composition, in the form of an aqueous dispersion, which includes a water-insoluble wax, a nonionic surfactant and a water-insoluble resin, and optionally an antistat, is improved by the inclusion of finely divided particles of polytetrafluoroethylene in the dispersion to provide fibrous polyolefin sheets on which the coating is applied and dried with desirable blood-barrier characteristics. Such coated sheets are suitable for gowns and drapes in operating rooms.
Inventors
- 👤 Don M. Coates
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:01
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/244; D06M15/256; C; C09; C09D; C09D127/00; C09D127/02; C09D127/12; C09D127/18; C08; C08L; C08L91/00; C08L91/06; Y; Y10; Y10S; Y10S524/00; Y10S524/91; Y10S524/912; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/31504; Y10T428/31801; Y10T442/00; Y10T442/20; Y10T442/2164; Y10T442/2205; Y10T442/2344; Y10T442/2418
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
66 words
An improved coating composition in the form of an aqueous dispersion that contains 10 to 40% by weight of solids, which solids include effective amounts of a water-insoluble wax, a nonionic surfactant and a water-insoluble resin, the improvement comprising an effective amount of finely divided polytetrafluoroethylene particles which provides a fibrous polyolefin sheet on which the coating composition is applied and dried with improved blood-barrier characteristics.
Claim 2
Dependent Claim
66 words
An improved coating composition in the form of an aqueous dispersion that contains 10 to 40% by weight of solids, which solids include effective amounts of a water-insoluble wax, a nonionic surfactant and a water-insoluble resin, the improvement comprising an effective amount of finely divided polytetrafluoroethylene particles which provides a fibrous polyolefin sheet on which the coating composition is applied and dried with improved blood-barrier characteristics.
Claim 3
Dependent Claim
26 words
The coating composition of claim 1 wherein the polytetrafluoroethylene particles amount to 10 to 35% by weight of the coating composition, on a dry solid basis.
Claim 4
Dependent Claim
155 words
The coating composition of claim 1 wherein (a) the water-insoluble wax is dispersible in water at a concentration of 10% by weight based on the total amount of wax and water, and requires for dispersion in water only a nonionic surfactant or a mixture of two or more nonionic surfactants in an amount of at least 15% and not more than 100% by weight based on the amount of wax; (b) the nonionic surfactant has a hydrophilic-lipophilic balance in the range of about 6 to about 10 and is present in an amount in the range of about 15 to about 100% by weight based on the amount of wax; (c) the water-insoluble binder is capable of wetting a fibrous polyolefin sheet and in the form of an aqueous dispersion, does not coagulate in the presence of an antistat; (d) the polytetrafluorethylene particles amount to 15 to 35% by weight of the dry coating composition.
Claim 5
Dependent Claim
16 words
A fibrous polyolefin sheet coated with the composition of claim 1, 2 or 3 and dried.
Claim 6
Dependent Claim
19 words
A nonwoven sheet of polyethylene film-fibril elements coated with the composition of claim 1, 2 or 3 and dried.
Claim 7
Dependent Claim
68 words
A process for preparing the coating composition of claim 1, 2 or 3 comprising the steps of forming a molten mixture of the water-insoluble wax and the nonionic surfactant, dispersing the finely divided polytetrafluorethylene particles in the molten mixture, adding steam and then liquid water to the molten mixture containing the polytetrafluorethylene particles to form an aqueous dispersion, and adding the water-insoluble resin binder to the aqueous dispersion.
Claim 8
Dependent Claim
62 words
A process for preparing the coating composition of claim 1, 2 or 3 comprising the steps of forming a molten mixture of the water-insoluble wax and the nonionic surfactant, preparing a slurry of the finely divided polytetrafluoroethylene particles in an aqueous mixture of the water-insoluble resin and dispersing the slurry in the molten mixture while adding steam and then liquid water thereto.
Claim 9
Dependent Claim
13 words
The coating composition of claim 1, 2 or 3 further comprising an antistat.
Claim 10
Dependent Claim
21 words
The process of claim 6 wherein an antistat is added to the aqueous dispersion after the resin binder has been added.
Claim 11
Dependent Claim
24 words
The process of claim 7 wherein an antistat is added to the aqueous dispersion after the slurry has been dispersed in the molten mixture.
References Cited (Backward Citations)
US3168426A
Cited
US3151015A
Cited
US3498826A
Cited
US3480547A
Cited
US3713878A
Cited
US3838082A
Cited
US3816229A
Cited
US4076672A
Cited
US4113679A
Cited
US4082887A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-09 | 1986-11-08 | 1987-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-09 | 1990-11-08 | 1991-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-09 | 1994-11-08 | 1995-05-10 | $7700.00 | Window Closed / Lapsed |