Plastic transparencies having improved resistance to cracking
Assignee: GKN Aerospace Transparency Systems Inc
•
Filing: 1980-12-29
•
Granted: 1983-03-22
•
Expires: 2000-12-29
Abstract
Abstract A plastic transparency for particular use as an airplane window, including a transparent sheet member and a thin resinous coating overlying the peripheral edge surface of the sheet member. The sheet member is formed of a multi-axially oriented plastic material that is absorptive of moisture, the volume of the member varying in accordance with the amount of moisture absorbed. The edge coating has a moisture permeation rate substantially less than that of the underlying sheet member, so when the window is exposed to an environment of high or variable humidity, any moisture gradient adjacent the peripheral edge surface is reduced, and the resultant tensile stress and incidence of cracking in the window are correspondingly reduced.
Inventors
- 👤 William F. Fischer
- 👤 II Charles A. Bailey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:57
CPC Classifications
B; B64; B64C; B64C1/00; B64C1/14; B64C1/1476; B64C1/1484; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J2333/00; C08J2333/04; C08J2333/06; C08J2333/10; C08J2333/12; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24777; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31928
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
131 words
A transparency having improved resistance to crazing and cracking when exposed to an environment of variable humidity, the transparency comprising: a transparent, plastic sheet member having a peripheral edge surface, the sheet member being formed of a multiaxially oriented material that is absorptive of moisture, the volume of the sheet member varying in accordance with the amount of moisture absorbed; and a thin, resinous coating overlying the peripheral edge surface of the sheet member and in direct contact with it, the resinous coating having a moisture permeation rate substantially lower than that of the underlying sheet member, whereby the magnitude of any moisture gradient adjacent the edge surface, caused by an environment of variable humidity, is reduced and the concomitant incidence of crazing and cracking in the transparency is correspondingly reduced.
Claim 2
Dependent Claim
131 words
A transparency having improved resistance to crazing and cracking when exposed to an environment of variable humidity, the transparency comprising: a transparent, plastic sheet member having a peripheral edge surface, the sheet member being formed of a multiaxially oriented material that is absorptive of moisture, the volume of the sheet member varying in accordance with the amount of moisture absorbed; and a thin, resinous coating overlying the peripheral edge surface of the sheet member and in direct contact with it, the resinous coating having a moisture permeation rate substantially lower than that of the underlying sheet member, whereby the magnitude of any moisture gradient adjacent the edge surface, caused by an environment of variable humidity, is reduced and the concomitant incidence of crazing and cracking in the transparency is correspondingly reduced.
Claim 3
Dependent Claim
18 words
A transparency as defined in claim 1, wherein the transparent sheet member is formed of stretched polymethyl methacrylate.
Claim 4
Dependent Claim
41 words
A transparency as defined in claim 2, wherein the thin resinous coating is formed of a material selected from the group consisting of polyvinylidene chloride, polytetrafluoroethylene, chlorinated polyether, polyvinylidene fluoride, polyethylene, polyvinyl chloride, butyl rubber, polyethylene terephthalate, neoprene, and nitrile elastomers.
Claim 5
Dependent Claim
21 words
A transparency as defined in claim 1, wherein the thin resinous coating has a thickness of at least about 0.00025 inches.
Claim 6
Dependent Claim
122 words
In a transparency including a transparent, plastic sheet member having a peripheral edge surface, wherein the sheet member is formed of a multi-axially oriented material that is absorptive of moisture, the volume of the sheet member varying in accordance with the amount of moisture absorbed, an improvement comprising: a thin, resinous coating overlying the peripheral edge surface of the sheet member and in direct contact with it, the resinous coating having a moisture permeation rate substantially lower than that of the underlying sheet member, whereby the magnitude of any moisture gradient adjacent the edge surface, caused by an environment of variable humidity, is reduced and the concomitant incidence of crazing and cracking in the edge surface of the transparency is correspondingly reduced.
Claim 7
Dependent Claim
122 words
In a transparency including a transparent, plastic sheet member having a peripheral edge surface, wherein the sheet member is formed of a multi-axially oriented material that is absorptive of moisture, the volume of the sheet member varying in accordance with the amount of moisture absorbed, an improvement comprising: a thin, resinous coating overlying the peripheral edge surface of the sheet member and in direct contact with it, the resinous coating having a moisture permeation rate substantially lower than that of the underlying sheet member, whereby the magnitude of any moisture gradient adjacent the edge surface, caused by an environment of variable humidity, is reduced and the concomitant incidence of crazing and cracking in the edge surface of the transparency is correspondingly reduced.
Claim 8
Dependent Claim
52 words
An improvement as defined in claim 5, wherein: the transparent sheet member is formed of stretched polymethyl methacrylate; and the thin, resinous coating is formed of a material selected from the group consisting of polyvinylidene chloride, polytetrafluoroethylene, chlorinated polyether, polyvinylidene fluoride, polyethylene, polyvinyl chloride, butyl rubber, polyethylene terephthalate, neoprene, and nitrile elastomers.
Claim 9
Dependent Claim
21 words
An improvement as defined in claim 6, wherein the thin resinous coating has a thickness of at least about 0.00025 inches.
References Cited (Backward Citations)
US2918696A
Cited
US2991209A
Cited
US2817618A
Cited
US2912716A
Cited
US2991207A
Cited
US3398044A
Cited
GB1065780A
Cited
US3424642A
Cited
US3409344A
Cited
US3596311A
Cited
US3562383A
Cited
US3632841A
Cited
US3764445A
Cited
US3843474A
Cited
US3935368A
Cited
US3833451A
Cited
US4118454A
Cited
FR2397927B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |