Fabrication of film circuits having a thick film crossunder and a thin film capacitor
Assignee: AT&T Inc
•
Filing: 1981-07-27
•
Granted: 1983-02-15
•
Expires: 2001-07-27
Abstract
Abstract A method of fabricating film circuits whereby thick film crossunders may be included with thin film capacitors (22) on a single substrate (10). At least one dielectric layer (12) is formed on the crossunder electrode (11) and a layer capable of smoothing irregularities (13) is also formed in the area of capacitor formation. Firing of the capacitor underlayer is compatible with the dielectric layer. A layer such as beta tantalum (14) is formed over essentially the entire circuit and etched from the contact areas (21) of the crossunder electrode. The layer is oxidized to form a protective layer (15) for the previously deposited layers as well as an underlay for subsequently formed thin film components.
Inventors
- 👤 Raymond C. Pitetti
- 👤 John Rutkiewicz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:01
CPC Classifications
H; H10; H10D; H10D86/00; H10D86/80; H10D86/85
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
176 words
A method of fabricating a film circuit on an insulating substrate (10) comprising the steps of: forming a thick film electrode (11) on one portion of said substrate; depositing and firing at least one dielectric layer (12) on a portion of said electrode and depositing and firing at least one layer capable of smoothing irregularities of the substrate on a portion of the substrate remote from said electrode where a capacitor (22) is to be formed, the firing of each such layer being such as not to melt a previously deposited layer; subsequent to formation of said layers forming a first metal layer (14) over essentially the entire substrate including said layers and said thick film electrode; removing a portion of said metal layer from an area (21) of the thick film electrode to accommodate an electrical contact thereto; oxidizing the metal layer to form a protective oxide layer (15); and forming over said oxide layer at least one thin film capacitor (22), and a thin film conductor (19) electrically coupled to the thick film electrode.
Claim 2
Independent Claim
176 words
A method of fabricating a film circuit on an insulating substrate (10) comprising the steps of: forming a thick film electrode (11) on one portion of said substrate; depositing and firing at least one dielectric layer (12) on a portion of said electrode and depositing and firing at least one layer capable of smoothing irregularities of the substrate on a portion of the substrate remote from said electrode where a capacitor (22) is to be formed, the firing of each such layer being such as not to melt a previously deposited layer; subsequent to formation of said layers forming a first metal layer (14) over essentially the entire substrate including said layers and said thick film electrode; removing a portion of said metal layer from an area (21) of the thick film electrode to accommodate an electrical contact thereto; oxidizing the metal layer to form a protective oxide layer (15); and forming over said oxide layer at least one thin film capacitor (22), and a thin film conductor (19) electrically coupled to the thick film electrode.
Claim 3
Dependent Claim
50 words
The method according to claim 1 wherein there is deposited a plurality of dielectric layers on the thick film electrode, and the layer smoothing irregularities of the substrate is the same composition as the top dielectric layer on the thick film electrode and said layers are deposited and fired simultaneously.
Claim 4
Dependent Claim
35 words
The method according to claim 2 wherein the plurality of dielectric layers (12+13) and the layer smoothing irregularities of the substrate (13) are deposited from a paste comprising glass powders dispersed in an organic vehicle.
Claim 5
Dependent Claim
105 words
The method according to claim 2 wherein the bottom dielectric layer (12) on the thick film electrode is deposited from a paste comprising glass powders comprising oxides of silicon, lead, calcium, aluminum, boron, potassium, magnesium and sodium dispersed in an organic vehicle comprising cellulose based ppolymers dissolved in a solvent system of pine oil derivatives and a mixed ester, and the top dielectric layer and the layer smoothing irregularities (13) are deposited from a paste comprising glass powders comprising the oxides of silicon, boron, calcium, barium, aluminum, lead, bismuth, titanium, and potassium dispersed in an organic vehicle comprising cellulose based polymers dissolved in alpha terpineol.
Claim 6
Dependent Claim
49 words
The method according to claim 4 wherein the bottom dielectric layer is fired at a temperature in the range 800-950 degrees Celsius for 10-20 minutes, and the top dielectric layer and the layer smoothing irregularities are fired at a temperature in the range 850-975 degrees Celsius for 10-20 minutes.
Claim 7
Dependent Claim
81 words
The method according to claim 1 wherein there is deposited a plurality of dielectric layers on the thick film electrode and the bottom dielectric layer (12) is fired at a temperature in the range 800-875 degrees Celsius for a time of 10-20 minutes, the top dielectric layer (13) is fired at a temperature in the range 800-850 degrees Celsius for 10-20 minutes, and the layer smoothing irregularities is fired at a temperature in the range 850-950 degrees Celsius for 10-20 minutes.
Claim 8
Dependent Claim
19 words
The method according to claim 1 wherein the thick film electrode is deposited from a paste comprising fritted gold.
Claim 9
Dependent Claim
13 words
The method according to claim 1 wherein the first metal layer comprises tantalum.
Claim 10
Dependent Claim
26 words
The method according to claim 8 wherein the portion of the metal layer is removed by an etchant comprising HF, HNO 3 and H 2 O.
Claim 11
Dependent Claim
45 words
The method according to claim 1 wherein the firing of the dielectric layer increases the melting point of the layer as deposited and the firing of the layer smoothing irregularities is done at a temperature above the melting point of the dielectric layer as deposited.
Claim 12
Independent Claim
220 words
A method of fabricating a film circuit on a ceramic substrate (10) comprising the steps of: depositing a thick film electrode (11) comprising gold on one portion of said substrate; depositing on a portion of said electrode a first glass layer (12) and firing at a temperature in the range 800-950 degrees Celsius for 10-20 minutes; depositing over said first layer and also on a portion of the substrate remote from said electrode where a capacitor is to be formed a second glass layer (13) which is also capable of smoothing irregularities of the substrate, and firing at a temperature within the range 850-975 degrees Celsius for 10-20 minutes such that firing the second layer does not melt the first layer; subsequent to formation of said layers, forming a first metal layer comprising tantalum over essentially the entire substrate including said layers and said thick film electrode; removing a portion of said metal layer from an area (21) of the thick film electrode to accommodate an electrical contact thereto utilizing an etchant comprising HF, HNO 3 and H 2 O; oxidizing the metal layer to form a protective oxide layer (15); and forming over said oxide layer at least one thin film capacitor (22), thin film resistor (20) and thin film conductor (19) electrically coupled to the thick film electrode.
Claim 13
Independent Claim
220 words
A method of fabricating a film circuit on a ceramic substrate (10) comprising the steps of: depositing a thick film electrode (11) comprising gold on one portion of said substrate; depositing on a portion of said electrode a first glass layer (12) and firing at a temperature in the range 800-950 degrees Celsius for 10-20 minutes; depositing over said first layer and also on a portion of the substrate remote from said electrode where a capacitor is to be formed a second glass layer (13) which is also capable of smoothing irregularities of the substrate, and firing at a temperature within the range 850-975 degrees Celsius for 10-20 minutes such that firing the second layer does not melt the first layer; subsequent to formation of said layers, forming a first metal layer comprising tantalum over essentially the entire substrate including said layers and said thick film electrode; removing a portion of said metal layer from an area (21) of the thick film electrode to accommodate an electrical contact thereto utilizing an etchant comprising HF, HNO 3 and H 2 O; oxidizing the metal layer to form a protective oxide layer (15); and forming over said oxide layer at least one thin film capacitor (22), thin film resistor (20) and thin film conductor (19) electrically coupled to the thick film electrode.
Claim 14
Dependent Claim
94 words
The method according to claim 11 wherein the first glass layer is deposited from a paste comprising glass powders comprising oxides of silicon, lead, calcium, aluminum, boron, potassium, magnesium and sodium dispersed in an organic vehicle comprising cellulose based polymers dissolved in a solvent system of pine oil derivatives and a mixed ester and the second glass protective layer is deposited from a paste comprising glass powders comprising the oxides of silicon, boron, calcium, barium, aluminum, lead, bismuth, titanium, and potassium dispersed in an organic vehicle comprising cellulose based polymers dissolved in alpha terpineol.
Claim 15
Dependent Claim
47 words
The method according to claim 11 wherein the firing of the first glass layer increases the melting point of the layer as deposited, and the firing of the second glass layer is done at a temperature above the melting point of the first glass layer as deposited.
References Cited (Backward Citations)
US3317653A
Cited
US3560256A
Cited
US3607679A
Cited
US4031272A
Cited
US4241103A
Cited
US4251326A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-14 | 1986-08-16 | 1987-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-14 | 1990-08-16 | 1991-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-14 | 1994-08-16 | 1995-02-15 | $7700.00 | Window Closed / Lapsed |