Polycrystalline translucent alumina sintered body, a method for producing the same and a high pressure vapor discharge lamp obtained by using said sintered body
Abstract A polycrystalline translucent alumina sintered body having high in-line transmission, which is suitable for an envelope for a high pressure vapor discharge lamp, is produced by adding to alumina powder having a purity of more than 99.8% MgO or a compound forming MgO in an amount of 0.01-0.1% by weight calculated as MgO, La 2 O 3 or a compound forming La 2 O 3 in an amount of 0.001-0.05% by weight calculated as La 2 O 3 , and Y 2 O 3 or a compound forming Y 2 O 3 in an amount of 0.001-0.5% by weight calculated as Y 2 O 3 , thoroughly mixing the resulting mixture, shaping the mixture into a desired form and firing the shaped article under vacuum or either atmosphere of hydrogen gas or dissociated ammonia gas under oxygen concentration of 10 -15 -10 -25 atm.
A polycrystalline translucent alumina sintered body in which the content of MgO is 0.001-0.04% by weight, the content of each of La 2 O 3 and Y 2 O 3 is 0.001-0.01% by weight, a weight ratio of MgO/La 2 O 3 +Y 2 O 3 is 0.5-2, and an in-line transmission is more than 40%.
Claim 2
Dependent Claim
56 words
A polycrystalline translucent alumina sintered body in which the content of MgO is 0.001-0.04% by weight, the content of each of La 2 O 3 and Y 2 O 3 is 0.001-0.01% by weight, a weight ratio of MgO/La 2 O 3 +Y 2 O 3 is 0.5-2, and an in-line transmission is more than 40%.
Claim 3
Dependent Claim
68 words
In a high pressure vapor discharge lamp having an envelope, the improvement wherein the envelope comprises polycrystalline translucent alumina in which the content of MgO is 0.001-0.04% by weight, the content of each La 2 O 3 and Y 2 O 3 is 0.001-O.01% by weight, a weight ratio of MgO/La 2 O 3 +Y 2 O 3 is 0.5-2, and an in-line transmission is more than 40%.
Claim 4
Dependent Claim
68 words
In a high pressure vapor discharge lamp having an envelope, the improvement wherein the envelope comprises polycrystalline translucent alumina in which the content of MgO is 0.001-0.04% by weight, the content of each La 2 O 3 and Y 2 O 3 is 0.001-O.01% by weight, a weight ratio of MgO/La 2 O 3 +Y 2 O 3 is 0.5-2, and an in-line transmission is more than 40%.