Composition for the storage of hydrogen and method of making the composition
Assignee: Battelle Memorial Institute Inc
•
Filing: 1979-11-09
•
Granted: 1983-01-11
•
Expires: 1999-11-09
Abstract
Abstract A magnesium powder composition for the reversible storage of hydrogen by absorption thereof in the magnesium to form the hydride which consists of an intimate mixture of magnesium powder and an inert powder which is stable under the conditions of formation and decomposition of the hydride. The stable inert powder, which prevents the agglomeration of the magnesium powder and maintains its hydrogen-storage capacity, is selected from the group which consists of metal powders such as manganese, iron, cobalt, nickel and copper, metal alloy powders such as iron-zinc alloys, and the oxides, carbides or nitrides of magnesium, calcium, boron, aluminum, silicon, titanium, zinc, vanadium, chromium, manganese and iron. The mixture is formed by intimately grinding the magnesium and inert powders together.
Inventors
- 👤 Olivier de Pous
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:59
CPC Classifications
F; F17; F17C; F17C11/00; F17C11/005; C; C01; C01B; C01B3/00; C01B3/0005; C01B3/001; C01B3/0078; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/32; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12708; Y10T428/12715
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
85 words
A composition for the storage of hydrogen which consists of a pulverulent intimate mixture of magnesium powder and between 1 and 20% by volume thereof of a separator-agent powder inert to hydrogen and magnesium under hydrogen absorption and desorption conditions, said separator-agent powder being uniformly distributed in said mixture, being physically stable and inhibiting agglomeration of the magnesium powder over a succession of absorption/desorption cycles whereby the magnesium powder is converted to magnesium hydride and hydrogen is released upon thermal decomposition of the hydride respectively.
Claim 2
Dependent Claim
85 words
A composition for the storage of hydrogen which consists of a pulverulent intimate mixture of magnesium powder and between 1 and 20% by volume thereof of a separator-agent powder inert to hydrogen and magnesium under hydrogen absorption and desorption conditions, said separator-agent powder being uniformly distributed in said mixture, being physically stable and inhibiting agglomeration of the magnesium powder over a succession of absorption/desorption cycles whereby the magnesium powder is converted to magnesium hydride and hydrogen is released upon thermal decomposition of the hydride respectively.
Claim 3
Dependent Claim
46 words
The composition defined in claim 1 wherein said separator-agent powder is composed of at least one of the metals selected from the group consisting of manganese, iron, cobalt, nickel and copper or an alloy thereof inert to hydrogen and magnesium under hydrogen absorption and desorption conditions.
Claim 4
Dependent Claim
25 words
The composition defined in claim 2 wherein the separator-agent powder is a primary alloy inert to hydrogen and magnesium under hydrogen absorption and desorption conditions.
Claim 5
Dependent Claim
36 words
The composition defined in claim 1 wherein said separator-agent powder is composed of at least one oxide, carbide or nitride of magnesium, calcium, boron, aluminum, silicon, titanium, zirconium, vanadium, chromium, manganese, iron or a combination thereof.
Claim 6
Dependent Claim
75 words
A process for producing a magnesium-based composition adapted to absorb hydrogen under predetermined absorption conditions and form magnesium hydride and adapted, upon thermal decomposition of said magnesium hydride, to release gaseous hydrogen, said process consisting of the steps of conjointly grinding magnesium powder and a powder of a separator agent inert to hydrogen and magnesium, physically stable under said conditions and adapted to prevent agglomeration of the magnesium powder during absorption/desorption cycling of the composition.
Claim 7
Dependent Claim
75 words
A process for producing a magnesium-based composition adapted to absorb hydrogen under predetermined absorption conditions and form magnesium hydride and adapted, upon thermal decomposition of said magnesium hydride, to release gaseous hydrogen, said process consisting of the steps of conjointly grinding magnesium powder and a powder of a separator agent inert to hydrogen and magnesium, physically stable under said conditions and adapted to prevent agglomeration of the magnesium powder during absorption/desorption cycling of the composition.
Claim 8
Dependent Claim
47 words
The process defined in claim 5 wherein said separator-agent powder is composed of at least one of the metals selected from the group which consists of manganese, iron, cobalt, nickel and copper or an alloy thereof inert to hydrogen and magnesium under hydrogen absorption and desorption conditions.
Claim 9
Dependent Claim
30 words
The process defined in claim 6 wherein said separator-agent powder is a primary alloy of one of said metals inert to hydrogen and magnesium under hydrogen absorption and desorption conditions.
Claim 10
Dependent Claim
88 words
A composition for the storage of hydrogen which consists of a pulverulent intimate mixture of magnesium powder and between 1 and 20% by volume thereof of a primary iron-zinc alloy separator-agent powder inert to hydrogen and magnesium under hydrogen absorption and desorption conditions, said separator-agent powder being uniformly distributed in said mixture, being physically stable and inhibiting agglomeration of the magnesium powder over a succession of absorption/desorption cycles whereby the magnesium powder is converted to magnesium hybride and hydrogen is released upon thermal decomposition of the hydride respectively.
Claim 11
Dependent Claim
88 words
A composition for the storage of hydrogen which consists of a pulverulent intimate mixture of magnesium powder and between 1 and 20% by volume thereof of a primary iron-zinc alloy separator-agent powder inert to hydrogen and magnesium under hydrogen absorption and desorption conditions, said separator-agent powder being uniformly distributed in said mixture, being physically stable and inhibiting agglomeration of the magnesium powder over a succession of absorption/desorption cycles whereby the magnesium powder is converted to magnesium hybride and hydrogen is released upon thermal decomposition of the hydride respectively.
Claim 12
Dependent Claim
57 words
A process for producing a magnesium-based composition adapted to absorb hydrogen under predetermined absorption conditions and form magnesium hydride and adapted, upon thermal decomposition of said magnesium hydride, to release gaseous hydrogen, said process comprising the steps of conjointly grinding magnesium powder and a powder of a separator agent in the form of a primary iron-zinc alloy.
Claim 13
Dependent Claim
57 words
A process for producing a magnesium-based composition adapted to absorb hydrogen under predetermined absorption conditions and form magnesium hydride and adapted, upon thermal decomposition of said magnesium hydride, to release gaseous hydrogen, said process comprising the steps of conjointly grinding magnesium powder and a powder of a separator agent in the form of a primary iron-zinc alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-10 | 1986-07-12 | 1987-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-10 | 1990-07-12 | 1991-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-10 | 1994-07-12 | 1995-01-11 | $7700.00 | Window Closed / Lapsed |