Method of fabricating multi-mode optical fiber preforms
Assignee: NTT Inc
•
Filing: 1980-09-19
•
Granted: 1983-01-04
•
Expires: 2000-09-19
Abstract
Abstract A method of fabricating an optical fiber preform wherein a synthesizing torch is inclined between 10 DEG and 60 DEG with respect to the rotation axis of a seed rod. Moving the rod while rotating it, a glass raw material gas and a flame forming gas are blown out individually from the torch to synthesize glass particles which are deposited onto one end of the rod, so that a cylindrical porous preform is grown in the direction of the rotation axis of the rod. Then the porous preform is heated at a high temperature to vitrify the porous preform into a transparent optical fiber preform. At least one exhaust port is disposed at a distance of 1 mm to 50 mm from the periphery of the porous preform and in the vicinity of the growing surface of the porous preform. In fabricating the porous preform the outer diameter fluctuations are small, and the preform is formed stably without formation of cracking on the periphery of the preform.
Inventors
- 👤 Shoichi Suto
- 👤 Fumiaki Hanawa
- 👤 Masao Kawachi
- 👤 Takao Edahiro
- 👤 Motohiro Nakahara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:48
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/0144; C03B2203/00; C03B2203/10; C03B2203/22; C03B2203/24; C03B2207/00; C03B2207/04; C03B2207/06; C03B2207/10; C03B2207/16; C03B2207/18; C03B2207/20; C03B2207/42; C03B2207/50; C03B2207/60; C03B2207/64; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
221 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod about said axis; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at an inclination angle between 10° and 60° with respect to the axis of rotation of said seed rod to synthesize glass particles and then to deposit said glass particles onto one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
Claim 2
Independent Claim
221 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod about said axis; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at an inclination angle between 10° and 60° with respect to the axis of rotation of said seed rod to synthesize glass particles and then to deposit said glass particles onto one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
Claim 3
Dependent Claim
34 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 1, wherein said synthesizing torch is inclined at an angle between 30° and 40° with respect to said axis of rotation.
Claim 4
Independent Claim
323 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at a predetermined inclination angle with respect to the axis of rotation to synthesize fine glass particles from said glass raw material gas through hydrolysis by flame or thermal oxidation by a high temperature heat source, said glass particles being blown out and deposited on one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; exhausting glass particles not attached to the growing surface of said cylindrical porous preform of said glass particles, gas produced as a result of said hydrolysis or oxidation, non-reacted glass raw material gas and said flame forming gas through at least one exhaust port which is spaced from said synthesizing torch and disposed at a distance of 1 mm to 50 mm from the periphery of the cylindrical porous preform formed by the deposition of said glass particles and in the vicinity of the growing surface of said cylindrical porous preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
Claim 5
Independent Claim
323 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at a predetermined inclination angle with respect to the axis of rotation to synthesize fine glass particles from said glass raw material gas through hydrolysis by flame or thermal oxidation by a high temperature heat source, said glass particles being blown out and deposited on one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; exhausting glass particles not attached to the growing surface of said cylindrical porous preform of said glass particles, gas produced as a result of said hydrolysis or oxidation, non-reacted glass raw material gas and said flame forming gas through at least one exhaust port which is spaced from said synthesizing torch and disposed at a distance of 1 mm to 50 mm from the periphery of the cylindrical porous preform formed by the deposition of said glass particles and in the vicinity of the growing surface of said cylindrical porous preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
Claim 6
Dependent Claim
56 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 3, wherein said synthesizing torch is inclined at an angle between 10° and 60° with respect to the axis of rotation of said seed rod, so that said glass particles are obliquely blown out for deposit onto one end of said seed rod.
Claim 7
Dependent Claim
31 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 4, wherein said exhaust port is disposed opposite said synthesizing torch with respect to said cylindrical porous preform.
Claim 8
Dependent Claim
34 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 4, wherein said synthesizing torch is inclined at an angle between 30° and 40° with respect to said axis of rotation.
Claim 9
Dependent Claim
35 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 3, wherein the distance between said exhaust port and the periphery of said cylindrical porous preform is 5 mm to 10 mm.
Claim 10
Dependent Claim
34 words
A method of fabricating a multi-mode optical fiber preform as claimed in claim 7, wherein said synthesizing torch is inclined at an angle between 30° and 40° with respect to said axis of rotation.
Claim 11
Dependent Claim
59 words
A method of fabricating a multi-mode optical fiber as claimed in claim 1 or 3, wherein said cylindrical porous preform comprises the core of an optical fiber, said method comprising the further step of blowing out a glass raw material gas and a flame forming gas separately from a second synthesizing torch to form a cladding on said core.
Claim 12
Independent Claim
218 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod about said axis; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at a predetermined inclination angle with respect to the axis of rotation of said seed rod to synthesize glass particles and then to deposit said glass particles onto one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
Claim 13
Independent Claim
218 words
A method of fabricating a multi-mode optical fiber preform from a seed rod having an axis of rotation, comprising the steps of: translating said seed rod along said axis of rotation while rotating said seed rod about said axis; blowing out a glass raw material gas and a flame forming gas separately from a single synthesizing torch inclined at a predetermined inclination angle with respect to the axis of rotation of said seed rod to synthesize glass particles and then to deposit said glass particles onto one end of said seed rod so that a cylindrical porous preform is grown in the direction of said axis of rotation, said glass raw material gas including an additive material for controlling the refractive index of said preform, the inclination angle of said synthesizing torch resulting in a temperature distribution across said one end of said seed rod whereby the temperature of said one end decreases from the center toward the periphery thereof, said glass raw material gas reacting in accordance with the surface temperature of said seed rod and the concentration of said additive material in said preform to provide a predetermined refractive index profile across said preform; and heating said cylindrical porous preform at a high temperature to vitrify said cylindrical porous preform into a transparent optical fiber preform.
References Cited (Backward Citations)
DE2625064A1
Cited
US4062665A
Cited
JPS54103058A
Cited
US4259101A
Cited
JPS54134129A
Cited
JPS54134133A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-03 | 1986-07-05 | 1987-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-03 | 1990-07-05 | 1991-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-03 | 1994-07-05 | 1995-01-04 | $7700.00 | Window Closed / Lapsed |