Formation of polymeric coatings
Assignee: Henkel Corp
•
Filing: 1980-10-02
•
Granted: 1982-12-28
•
Expires: 2000-10-02
Abstract
Abstract An aqueous coating composition containing a monomer which is capable of polymerizing in the presence of a metallic substrate in contact with the composition to form a polymer which has a multiplicity of groups capable of ionizing to form negatively charged groups on the polymer chain. Also, an autodepositing composition having included therein a monomeric constituent, that is, a material capable of being polymerized, for forming an organic coating on a metallic substrate.
Inventors
- 👤 Wilbur S. Hall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:24
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/088
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
140 words
A process for coating a metallic surface comprising immersing the surface in an acidic aqueous coating composition containing a monomer which is capable of polymerizing by addition polymerization to form an addition polymer which has a multiplicity of groups, namely carboxyl (--COOH), phenolic (--OH) or sulfonic (--SO 3 H) groups, which are capable of ionizing to form respectively on the polymer chain the negatively charged groups --COO - , --O - , or --SO 3 - , and wherein said monomer is soluble in the acidic aqueous medium of the composition which is free of organic solvent for the monomer, and including also an initiator selected from the group consisting of peroxides, hydroperoxides, organic azo compounds, permanganates, perborates and persulfates, and polymerizing said monomer to form said addition polymer on said surface which said surface is immersed in said composition.
Claim 2
Dependent Claim
140 words
A process for coating a metallic surface comprising immersing the surface in an acidic aqueous coating composition containing a monomer which is capable of polymerizing by addition polymerization to form an addition polymer which has a multiplicity of groups, namely carboxyl (--COOH), phenolic (--OH) or sulfonic (--SO 3 H) groups, which are capable of ionizing to form respectively on the polymer chain the negatively charged groups --COO - , --O - , or --SO 3 - , and wherein said monomer is soluble in the acidic aqueous medium of the composition which is free of organic solvent for the monomer, and including also an initiator selected from the group consisting of peroxides, hydroperoxides, organic azo compounds, permanganates, perborates and persulfates, and polymerizing said monomer to form said addition polymer on said surface which said surface is immersed in said composition.
Claim 3
Dependent Claim
138 words
A process for coating a metallic surface comprising immersing said surface in an acidic aqueous composition containing a monomer which is: (A) capable of polymerizing by addition polymerization to form an addition polymer; (B) soluble in the acidic aqueous medium of the composition which is free of organic solvent for the monomer; and (C) includes a group selected from the group consisting of carboxyl (--COOH), phenolic (--OH) and sulfonic (--SO 3 H) which is capable of ionizing in the composition to form respectively a negatively charged radical selected from the group consisting of --COO - , --O - , and --SO 3 - ; and forming on said surface, while immersed in said composition, from said monomer, a polymeric coating having a multiplicity of said groups capable of ionizing to form said negatively charged groups on the polymer.
Claim 4
Dependent Claim
138 words
A process for coating a metallic surface comprising immersing said surface in an acidic aqueous composition containing a monomer which is: (A) capable of polymerizing by addition polymerization to form an addition polymer; (B) soluble in the acidic aqueous medium of the composition which is free of organic solvent for the monomer; and (C) includes a group selected from the group consisting of carboxyl (--COOH), phenolic (--OH) and sulfonic (--SO 3 H) which is capable of ionizing in the composition to form respectively a negatively charged radical selected from the group consisting of --COO - , --O - , and --SO 3 - ; and forming on said surface, while immersed in said composition, from said monomer, a polymeric coating having a multiplicity of said groups capable of ionizing to form said negatively charged groups on the polymer.
Claim 5
Dependent Claim
12 words
A process according to claim 2 wherein said composition includes an initiator.
Claim 6
Dependent Claim
17 words
A process according to claim 1 or 2 wherein said monomer is an ethylenically unsaturated carboxylic acid.
Claim 7
Dependent Claim
38 words
A process according to claim 4 wherein said surface is a ferriferous surface and wherein said composition includes acrylic acid monomer, hydrogen peroxide initiator and HF, and wherein the polymerization of said monomer is initiated at room temperature.
Claim 8
Dependent Claim
108 words
A process for coating a metallic surface comprising contacting the surface with an autodepositing composition comprising an acidic aqueous coating solution having dispersed therein about 5 to about 550 g/l of pre-formed resin solids, a soluble ferric-containing compound in an amount equivalent to about 0.025 to about 3.5 g/l of ferric iron, and hydrofluoric acid and having a pH within the range of about 1.6 to about 5, and including also about 0.5 to about 50 wt.% of a monomer which is capable of polymerizing, and forming on the surface a coating including autodeposited resin formed from said pre-formed resin solids and also resin formed from said monomer.
Claim 9
Dependent Claim
108 words
A process for coating a metallic surface comprising contacting the surface with an autodepositing composition comprising an acidic aqueous coating solution having dispersed therein about 5 to about 550 g/l of pre-formed resin solids, a soluble ferric-containing compound in an amount equivalent to about 0.025 to about 3.5 g/l of ferric iron, and hydrofluoric acid and having a pH within the range of about 1.6 to about 5, and including also about 0.5 to about 50 wt.% of a monomer which is capable of polymerizing, and forming on the surface a coating including autodeposited resin formed from said pre-formed resin solids and also resin formed from said monomer.
Claim 10
Dependent Claim
16 words
A process according to claim 6 wherein said monomer is capable of forming an addition polymer.
Claim 11
Dependent Claim
29 words
A process according to claim 6 wherein said metallic surface is immersed in said composition and while immersed in said composition, said monomer polymerizes and deposits on said surface.
Claim 12
Dependent Claim
12 words
A process according to claim 7 wherein said monomer is diacetone acrylamide.
Claim 13
Dependent Claim
18 words
A process according to claim 6 wherein said autodepositing composition comprises resin solids, HF and FeF 3 .
Claim 14
Dependent Claim
18 words
A process according to claim 6, 7, 8, 9 or 10 wherein said surface is a ferriferous surface.
Claim 15
Dependent Claim
57 words
A process according to claim 6 wherein said autodepositing composition has a pH of about 1.6 to about 4 and consists essentially of ferric fluoride in an amount equivalent to about 0.5 to about 3.5 g/l of ferric iron, about 0.2 to about 5 g/l of HF and about 50 to about 125 g/l of resin solids.
Claim 16
Dependent Claim
13 words
A process according to claim 12 wherein said surface is a ferriferous surface.
Claim 17
Dependent Claim
16 words
A process according to claim 12 or 13 wherein said surface is immersed in said composition.
Claim 18
Dependent Claim
31 words
A process according to claim 6 or 12 wherein said metallic surface is immersed in said composition and including polymerizing said monomer while said metallic surface is immersed in said composition.
Claim 19
Dependent Claim
39 words
A process according to claim 6 or 12 wherein said metallic surface is immersed in said composition and forming on the surface a coating including autodeposited resin, and thereafter withdrawing the surface from the composition and polymerizing said monomer.
Claim 20
Dependent Claim
13 words
A process according to claim 14 wherein said surface is a ferriferous surface.
Claim 21
Dependent Claim
29 words
A process according to claim 6 or 12 wherein said monomer is soluble in the acidic aqueous medium of the composition in the absence of an organic solvent therefor.
References Cited (Backward Citations)
AU237781B2
Cited
US3397077A
Cited
US3585084A
Cited
US3914519A
Cited
US3501391A
Cited
GB1155497A
Cited
ZA721146B
Cited
US3873349A
Cited
US3865617A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |