Method for hardening steel
Assignee: Nachi Fujikoshi Corp
•
Filing: 1981-03-20
•
Granted: 1982-12-28
•
Expires: 2001-03-20
Abstract
Abstract A method of hardening steel so that it may have a surface layer with sufficient hardness to permit fabrication into machinery parts with a minimum of strain developed therein. The method comprises heating steel at a temperature in a range not lower than 100° C. below its A 1 transformation point (about 630° C.) and not higher than 50° C. thereabove (about 780° C.) in an atmosphere consisting solely of ammonia gas, or composed of ammonia gas and at least one of organic liquids, petroleum gases, endothermic gases and neutral gases, while ammonia gas is being supplied continuously at a lower flow rate, or at a higher flow rate followed by a diffusion treatment to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and quenching the steel to transform the austenitized surface layer into a martensite layer.
Inventors
- 👤 Jun Takeuchi
- 👤 Kaishu Yamazumi
- 👤 Takao Ishihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:23
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/80; C21; C21D; C21D1/00; C21D1/78; C23C8/06; C23C8/08; C23C8/24; C23C8/26
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
96 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed solely of ammonia gas being supplied at a flow rate of from about 0.1 to 2 furnace volume per hour to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 2
Independent Claim
96 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed solely of ammonia gas being supplied at a flow rate of from about 0.1 to 2 furnace volume per hour to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 3
Independent Claim
120 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmospere composed solely of ammonia gas being supplied at a flow rate of from about 2.1 to 7.5 furnace volume per hour to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and discontinuing the supply of ammonia gas and heating at the same temperature for about half an hour to one hour for diffusion treatment, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 4
Independent Claim
120 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmospere composed solely of ammonia gas being supplied at a flow rate of from about 2.1 to 7.5 furnace volume per hour to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and discontinuing the supply of ammonia gas and heating at the same temperature for about half an hour to one hour for diffusion treatment, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 5
Independent Claim
147 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed of ammonia gas being supplied continuously at a partial pressure of from about 0.05 to 0.3, and at least one substance selected from the group consisting of (a) petroleum gas such as propane and butane, (b) endothermic gas generated by reforming petroleum gas, (c) a carburizing and reducing gas or liquid, including an organic liquid such as alcohols, esters and ketones, and (d) a neutral gas such as nitrogen and argon, to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 6
Independent Claim
147 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed of ammonia gas being supplied continuously at a partial pressure of from about 0.05 to 0.3, and at least one substance selected from the group consisting of (a) petroleum gas such as propane and butane, (b) endothermic gas generated by reforming petroleum gas, (c) a carburizing and reducing gas or liquid, including an organic liquid such as alcohols, esters and ketones, and (d) a neutral gas such as nitrogen and argon, to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 7
Independent Claim
170 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed of ammonia gas being supplied at a partial pressure of from about 0.31 to 0.95, and at least one substance selected from the group consisting of (a) petroleum gas such as propane and butane, (b) endothermic gas generated by reforming petroleum gas, (c) a carburizing and reducing gas or liquid, including an organic liquid such as alcohols, esters and ketones, and (d) a neutral gas such as nitrogen and argon, to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and discontinuing the supply of ammonia gas and heating at the same temperature for about half an hour to one hour for diffusion treatment, and quenching the steel to transform said austenitized surface layer into a martensite layer.
Claim 8
Independent Claim
170 words
A method of hardening steel, comprising: heating the steel at a temperature in a range not lower than 100° C. below the A 1 transformation point of the steel (about 630° C.) and not higher than 50° C. above said transformation point (about 780° C.) in an atmosphere composed of ammonia gas being supplied at a partial pressure of from about 0.31 to 0.95, and at least one substance selected from the group consisting of (a) petroleum gas such as propane and butane, (b) endothermic gas generated by reforming petroleum gas, (c) a carburizing and reducing gas or liquid, including an organic liquid such as alcohols, esters and ketones, and (d) a neutral gas such as nitrogen and argon, to austenitize a surface layer of the steel by penetration of nitrogen thereinto, and discontinuing the supply of ammonia gas and heating at the same temperature for about half an hour to one hour for diffusion treatment, and quenching the steel to transform said austenitized surface layer into a martensite layer.
References Cited (Backward Citations)
US2339223A
Cited
US3137596A
Cited
US3265541A
Cited
US3282746A
Cited
US3357869A
Cited
US3647572A
Cited
US3705058A
Cited
US4047981A
Cited
US4145232A
Cited
US4124199A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |