US4047981A — Internally nitrided ferritic stainless steel stri…

Claim 1

Independent Claim 155 words

Internally nitrided substantially fully ferritic stainless steel cold reduced strip and sheet and products fabricated therefrom comprising a non-hardenable AISI Type 400 series ferritic stainless steel containing a nitride former chosen from the group consisting of titanium, zirconium, hafnium, columbium, vanadium, tantalum and rare earth metals, said nitride former being present in excess of the amount required to react completely with residual nitrogen and carbon in said steel, said excess nitride former being reacted with nitrogen internally to a depth sufficient to obtain an elevated temperature creep strength superior to that of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, and an oxidation resistance superior to that of AISI Type 316 austenitic stainless steel, by the Cyclic Oxidation Resistance Test defined herein, said nitrided strip, sheet and fabricated products exhibiting good room temperature formability, substantial freedom from chromium nitrides and chromium oxides, and containing less than about 5% austenite.

Claim 2

Dependent Claim 155 words

Internally nitrided substantially fully ferritic stainless steel cold reduced strip and sheet and products fabricated therefrom comprising a non-hardenable AISI Type 400 series ferritic stainless steel containing a nitride former chosen from the group consisting of titanium, zirconium, hafnium, columbium, vanadium, tantalum and rare earth metals, said nitride former being present in excess of the amount required to react completely with residual nitrogen and carbon in said steel, said excess nitride former being reacted with nitrogen internally to a depth sufficient to obtain an elevated temperature creep strength superior to that of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, and an oxidation resistance superior to that of AISI Type 316 austenitic stainless steel, by the Cyclic Oxidation Resistance Test defined herein, said nitrided strip, sheet and fabricated products exhibiting good room temperature formability, substantial freedom from chromium nitrides and chromium oxides, and containing less than about 5% austenite.

Claim 3

Dependent Claim 70 words

The strip, sheet and fabricated products claimed in claim 1, wherein said steel comprises, in weight percent, about 16% to about 26% chromium; about 0.4% to about 1.2% silicon; about 0.4% to about 2% total titanium, about 0.25% to about 1.25% of said titanium being in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron.

Claim 4

Dependent Claim 83 words

The strip, sheet and fabricated products claimed in claim 1, wherein said steel comprises, in weight percent, about 19% to about 21% chromium; about 0.4% to about 0.7% silicon; about 0.25% to about 0.6% titanium in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, manganese, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron, said nitrided strip, sheet and fabricated products containing at least 0.07% nitrogen in the form of a fine dispersion of titanium nitrides.

Claim 5

Dependent Claim 28 words

The strip, sheet and fabricated products claimed in claim 2, wherein said excess titanium is substantially fully combined with nitrogen in the form of finely dispersed internal nitrides.

Claim 6

Dependent Claim 23 words

The strip, sheet and fabricated products claimed in claim 2, wherein said chromium is at least 17.5% and said silicon is about 1%.

Claim 7

Dependent Claim 17 words

The strip, sheet and fabricated products claimed in claim 5, wherein said chromium is about 20.5% maximum.

Claim 8

Dependent Claim 16 words

Strip and sheet as claimed in claim 2, wherein said excess titanium is about 0.6% maximum.

Claim 9

Dependent Claim 15 words

Fabricated products as claimed in claim 2, wherein said excess titanium is about 1% maximum.

Claim 10

Dependent Claim 20 words

The strip, sheet and fabricated products claimed in claim 2, wherein said silicon ranges from about 0.4% to about 0.7%.

Claim 11

Dependent Claim 142 words

Internally nitrided substantially fully ferritic stainless steel cast products comprising, in weight percent, about 16% to about 26% chromium, about 0.4% to about 5% silicon; about 0.4% to about 2% total titanium, at least about 0.25% of said titanium being in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron; said excess titanium being reacted with nitrogen internally to a depth sufficient to obtain an elevated temperature creep strength superior to that of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, an oxidation resistance superior to that of AISI Type 316 austenitic stainless steel, by the Cyclic Oxidation Resistance Test defined herein, said cast products exhibiting substantial freedom from chromium nitrides and chromium oxides, and containing less than about 5% austenite.

Claim 12

Dependent Claim 142 words

Internally nitrided substantially fully ferritic stainless steel cast products comprising, in weight percent, about 16% to about 26% chromium, about 0.4% to about 5% silicon; about 0.4% to about 2% total titanium, at least about 0.25% of said titanium being in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron; said excess titanium being reacted with nitrogen internally to a depth sufficient to obtain an elevated temperature creep strength superior to that of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, an oxidation resistance superior to that of AISI Type 316 austenitic stainless steel, by the Cyclic Oxidation Resistance Test defined herein, said cast products exhibiting substantial freedom from chromium nitrides and chromium oxides, and containing less than about 5% austenite.

Claim 13

Independent Claim 281 words

A method of producing internally nitrided substantially fully ferritic stainless steel strip, sheet and fabricated products having elevated temperature creep strength and oxidation resistance superior to those of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, and by the Cyclic Oxidation Resistance Test defined herein, respectively, together with good room temperature formability, comprising the steps of providing a cold reduced substantially fully ferritic non-hardenable AISI Type 400 series stainless steel containing a nitride forming element chosen from the group consisting of titanium, zirconium, hafnium, columbium, vanadium, tantalum and rare earth metals, the nitride-former being present in excess of the amount required to react completely with residual nitrogen and carbon in said steel, and subjecting said strip, sheet and fabricated products to a nitriding heat treatment in a nitrogen-hydrogen atmosphere at a temperature of at least about 800° C but below the temperature at which austenite will form, in accordance with the following equation, wherein titanium is an exemplary nitride forming element: ##EQU3## where ξ = depth of internal nitridation N n .sup.(s) = mole fraction of nitrogen established at the surface D n = diffusion coefficient of nitrogen in the region 0 to ξ t = time N ti .sup.(O) = original mole fraction of titanium in the steel ν = ratio of N atoms to Ti atoms in precipitate = 1, in such manner as to avoid formation of chromium nitrides, chromium oxides, and austenite, said heat treatment being conducted for a period of time sufficient to cause at least 75% by weight of said excess nitride former to combine with said nitrogen in said atmosphere in the form of microscopic, uniformly dispersed nitrides.

Claim 14

Independent Claim 281 words

A method of producing internally nitrided substantially fully ferritic stainless steel strip, sheet and fabricated products having elevated temperature creep strength and oxidation resistance superior to those of AISI Type 316 austenitic stainless steel, by the 982° C Sag Test defined herein, and by the Cyclic Oxidation Resistance Test defined herein, respectively, together with good room temperature formability, comprising the steps of providing a cold reduced substantially fully ferritic non-hardenable AISI Type 400 series stainless steel containing a nitride forming element chosen from the group consisting of titanium, zirconium, hafnium, columbium, vanadium, tantalum and rare earth metals, the nitride-former being present in excess of the amount required to react completely with residual nitrogen and carbon in said steel, and subjecting said strip, sheet and fabricated products to a nitriding heat treatment in a nitrogen-hydrogen atmosphere at a temperature of at least about 800° C but below the temperature at which austenite will form, in accordance with the following equation, wherein titanium is an exemplary nitride forming element: ##EQU3## where ξ = depth of internal nitridation N n .sup.(s) = mole fraction of nitrogen established at the surface D n = diffusion coefficient of nitrogen in the region 0 to ξ t = time N ti .sup.(O) = original mole fraction of titanium in the steel ν = ratio of N atoms to Ti atoms in precipitate = 1, in such manner as to avoid formation of chromium nitrides, chromium oxides, and austenite, said heat treatment being conducted for a period of time sufficient to cause at least 75% by weight of said excess nitride former to combine with said nitrogen in said atmosphere in the form of microscopic, uniformly dispersed nitrides.

Claim 15

Dependent Claim 44 words

The method claimed in claim 11, including the step of subjecting said cold reduced steel to an air anneal at 900° to about 1095° C, and wherein said nitriding heat treatment is conducted with the annealing scale still on the surfaces of said steel.

Claim 16

Dependent Claim 34 words

The method claimed in claim 11, wherein said nitriding heat treatment is conducted at a temperature of about 900° to about 950° C with a time at temperature of at least about 5 hours.

Claim 17

Dependent Claim 56 words

The method claimed in claim 13, wherein said nitriding heat treatment is conducted in an atmosphere comprising about 1% to about 2% by volume nitrogen and balance essentially hydrogen, with a dew point not higher than about -15° C, for a period of time sufficient to effect complete through-thickness reaction of said nitride former with nitrogen.

Claim 18

Dependent Claim 70 words

The method claimed in claim 11, wherein said steel, prior to nitriding, comprises, in weight percent, about 16% to about 26% chromium; about 0.4% to about 1.2% silicon; about 0.4% to about 2% total titanium; about 0.25% to about 1.25% of said titanium being in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, nitrogen, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron.

Claim 19

Dependent Claim 61 words

The method claimed in claim 11, wherein said steel, prior to nitriding, comprises, in weight percent, about 19% to about 21% chromium; about 0.4% to about 0.7% silicon; about 0.25% to about 0.6% titanium in excess of the amount required to react completely with residual nitrogen and carbon; residual carbon, nitrogen, manganese, phosphorus, sulfur, nickel, aluminum and molybdenum, and balance iron.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1980-09-12	1981-03-14	1981-09-13	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1984-09-12	1985-03-14	1985-09-13	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1988-09-12	1989-03-14	1989-09-13	$7700.00	Window Closed / Lapsed

Internally nitrided ferritic stainless steel strip, sheet and fabricated products and method therefor

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag