Fibrous clay mixtures
Assignee: Chevron USA Inc
•
Filing: 1981-01-12
•
Granted: 1982-12-21
•
Expires: 2001-01-12
Abstract
Abstract A porous, ceramic composition suitable for use as a catalyst support for demetalation of asphaltene-containing feedstocks is made from a combination of fibrous clays, wherein the fibers of both clays are randomly dispersed and the resulting mass extruded and calcined. The first fibrous clay is preferably halloysite and the second fibrous clay is preferably attapulgite.
Inventors
- 👤 Donald S. Santilli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:57
CPC Classifications
B; B01; B01J; B01J21/00; B01J21/16; C; C10; C10G; C10G2300/00; C10G2300/10; C10G2300/107
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
61 words
A porous composition of matter comprising codispersed rods of a first fibrous clay and a second fibrous clay, said first fibrous clay having predominantly rods with the length range of 0.5-2 microns and a diameter range of 0.04-0.2 microns and said second fibrous clay having predominantly rods with a length range of 1-5 microns and a diameter range of 50-100 Angstroms.
Claim 2
Dependent Claim
61 words
A porous composition of matter comprising codispersed rods of a first fibrous clay and a second fibrous clay, said first fibrous clay having predominantly rods with the length range of 0.5-2 microns and a diameter range of 0.04-0.2 microns and said second fibrous clay having predominantly rods with a length range of 1-5 microns and a diameter range of 50-100 Angstroms.
Claim 3
Dependent Claim
26 words
The composition of claim 1 wherein the composition contains at least 5 weight percent of said second clay based on the total weight of said composition.
Claim 4
Dependent Claim
24 words
The composition of claim 1 including up to 15 weight percent of a refractory inorganic oxide based on the total weight of said composition.
Claim 5
Dependent Claim
12 words
The composition of claim 3 wherein said refractory inorganic oxide is alumina.
Claim 6
Dependent Claim
25 words
The composition of claim 1 wherein at least 60 percent of the volume of the pores is present in pores having diameters of 200-700 Angstroms.
Claim 7
Dependent Claim
17 words
The composition of claim 1 further comprising at least one metal selected from the transition metals group.
Claim 8
Dependent Claim
13 words
A composition of matter comprising codispersed rods of tubular halloysite and fibrous attapulgite.
Claim 9
Dependent Claim
13 words
A composition of matter comprising codispersed rods of tubular halloysite and fibrous attapulgite.
Claim 10
Dependent Claim
22 words
The composition of claim 7 wherein at least 5 weight percent of said composition is attapulgite based on total weight of composition.
Claim 11
Dependent Claim
22 words
The composition of claim 8 including up to 15 weight percent of a refractory inorganic oxide based on total weight of composition.
Claim 12
Dependent Claim
12 words
The composition of claim 9 wherein said refractory inorganic oxide is alumina.
Claim 13
Dependent Claim
24 words
The composition of claim 8 wherein said at least 60 percent of the pore volume is present in pores having diameters of 200-700 Angstroms.
Claim 14
Dependent Claim
18 words
The composition of claim 8 further comprising at least one metal selected from the transition group of metals.
Claim 15
Independent Claim
110 words
A method for preparing a porous composition of matter comprising preparing a mixture of a first fibrous clay and a second fibrous clay, said first fibrous clay having predominantly rods with a length range of 0.5-2 microns and a diameter range of 0.04-0.2 microns, and said second fibrous clay predominantly having rods with a length range of 1-5 microns and a diameter range of 50-100 Angstroms; adding sufficient water to create a slurry of no more than 25 weight percent solid content; vigorously agitating the slurry until the slurry ceases to thicken; drying the slurry to create a dry mass; and shaping the dried mass; and calcining the shaped mass.
Claim 16
Independent Claim
110 words
A method for preparing a porous composition of matter comprising preparing a mixture of a first fibrous clay and a second fibrous clay, said first fibrous clay having predominantly rods with a length range of 0.5-2 microns and a diameter range of 0.04-0.2 microns, and said second fibrous clay predominantly having rods with a length range of 1-5 microns and a diameter range of 50-100 Angstroms; adding sufficient water to create a slurry of no more than 25 weight percent solid content; vigorously agitating the slurry until the slurry ceases to thicken; drying the slurry to create a dry mass; and shaping the dried mass; and calcining the shaped mass.
Claim 17
Dependent Claim
27 words
The method of claim 13 wherein said mixture contains up to 15 dry weight percentage of a refractory inroganic oxide bond on total weight of the composition.
Claim 18
Dependent Claim
12 words
The method of claim 14 wherein the refractory inorganic oxide is alumina.
Claim 19
Dependent Claim
28 words
The method of claim 14 wherein said composition has at least 60 percent of the volume of the pores is present in pores having diameters of 200-700 Angstroms.
Claim 20
Independent Claim
56 words
A method for producing a composition of matter comprising: preparing a mixture of tubular halloysite and fibrous attapulgite; adding enough water to create a slurry of no more than 25 weight percent water content; vigorously agitating the slurry until the thickening of the slurry ceases; drying the mass, shaping the mass, and calcining the shaped mass.
Claim 21
Independent Claim
56 words
A method for producing a composition of matter comprising: preparing a mixture of tubular halloysite and fibrous attapulgite; adding enough water to create a slurry of no more than 25 weight percent water content; vigorously agitating the slurry until the thickening of the slurry ceases; drying the mass, shaping the mass, and calcining the shaped mass.
Claim 22
Dependent Claim
27 words
The method of claim 17 wherein the mixture contains up to 15 dry weight percent of a refractory inorganic oxide based on total weight of the composition.
Claim 23
Dependent Claim
12 words
The method of claim 17 wherein the refractory inorganic oxide is alumina.
Claim 24
Dependent Claim
27 words
The method of claim 17 wherein the mixture contains between 0.1 and 10 weight percent of a catalytic transition metal based on total weight of the composition.
Claim 25
Dependent Claim
28 words
The method of claim 17 wherein the calcined mass has at least 60 percent of the pore volume present as pores having diameters between 200 and 700 Angstroms.
References Cited (Backward Citations)
US3049449A
Cited
US3891541A
Cited
US3966641A
Cited
US4098676A
Cited
US4152250A
Cited
US4166026A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-20 | 1986-06-21 | 1986-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-20 | 1990-06-21 | 1990-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-20 | 1994-06-21 | 1994-12-21 | $7700.00 | Window Closed / Lapsed |