Method of making buried channel charge coupled device with means for controlling excess charge
Assignee: RCA Corp
•
Filing: 1981-08-27
•
Granted: 1982-12-07
•
Expires: 2001-08-27
Abstract
Abstract The preferred embodiment of a method of making a buried channel CCD starts with a body of P type semiconductor material over which an oxide layer and a photoresist are deposited. Openings are formed to expose regions of the body surface where drains are to be formed and N type impurity atoms are implanted through the openings. The openings are then enlarged to expose an additional area of the surface surrounding the drains and P type atoms are implanted through the enlarged openings to form channel stops. Afterward, the surface of the body is exposed and N type atoms are implanted to form buried channel regions on each side of the channel stops and to convert a thin layer of the channel stops to lightly doped compensation regions extending between the drains and the buried channel regions.
Inventors
- 👤 Lloyd F. Wallace
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:23
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0198; H10D84/02; H10D84/03; H10D84/038; H10F; H10F39/00; H10F39/10; H10F39/12; H10F39/15; H10F39/158; H10P; H10P30/00; H10P30/20; H10P30/22; H10P76/00; H10P76/40
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
196 words
A method of making a buried channel CCD on a body of semiconductor material of one conductivity type, said method comprising: forming an oxide layer over a surface of the body and applying a mask over the surface of said oxide layer; forming openings through said mask and said oxide layer to expose surface regions of the body where drains are to be formed and implanting ions of the opposite conductivity type through said openings into the exposed surface regions of said body to form drains extending into said body a predetermined distance from said surface; enlarging the size of said openings to expose an additional area of said surface around each of said drains and implanting ions of said one conductivity type through said enlarged openings into the exposed surface of said body to form channel stops extending into said body around and below said drains; exposing the surface of said body and implanting ions of said opposite conductivity type into said surface to form buried channel regions on each side of said channel stops and to convert a thin layer thereof adjacent said surface to lightly doped compensation regions of said opposite conductivity type.
Claim 2
Independent Claim
196 words
A method of making a buried channel CCD on a body of semiconductor material of one conductivity type, said method comprising: forming an oxide layer over a surface of the body and applying a mask over the surface of said oxide layer; forming openings through said mask and said oxide layer to expose surface regions of the body where drains are to be formed and implanting ions of the opposite conductivity type through said openings into the exposed surface regions of said body to form drains extending into said body a predetermined distance from said surface; enlarging the size of said openings to expose an additional area of said surface around each of said drains and implanting ions of said one conductivity type through said enlarged openings into the exposed surface of said body to form channel stops extending into said body around and below said drains; exposing the surface of said body and implanting ions of said opposite conductivity type into said surface to form buried channel regions on each side of said channel stops and to convert a thin layer thereof adjacent said surface to lightly doped compensation regions of said opposite conductivity type.
Claim 3
Dependent Claim
22 words
A method in accordance with claim 1 wherein the ions implanted to form said drain and said channel stops are activated simultaneously.
Claim 4
Dependent Claim
29 words
A method in accordance with claim 1 wherein said openings are enlarged by exposing said body to an etchant that removes said oxide layer without removing said masking material.
Claim 5
Dependent Claim
37 words
A method in accordance with claim 1 wherein after said buried channel regions and said compensation regions are formed, a channel oxide layer is formed over said surface and electrodes are formed over said channel oxide layer.
Claim 6
Dependent Claim
32 words
A method in accordance with claim 4 wherein said channel oxide layer is thermally grown under conditions that simultaneously activates the impurity atoms in said buried channel regions and said compensation regions.
Claim 7
Dependent Claim
41 words
A method in accordance with claim 1 wherein said drains are formed by implanting arsenic (As) ions through said openings with the masking material in place and wherein said openings are enlarged by etching said oxide layer with hydrofluoric acid (HF).
Claim 8
Dependent Claim
32 words
A method in accordance with claim 1 wherein a thin oxide layer is formed on said exposed surface portions after enlarging the size of said openings and before forming said channel stops.
Claim 9
Dependent Claim
32 words
A method in accordance with claim 1 wherein said mask is stripped from said oxide layer by plasma etching after enlarging the size of said openings and before forming said channel stops.
Claim 10
Independent Claim
306 words
A method of making a buried channel CCD on a body of semiconductor material of one conductivity type, said method comprising: forming an oxide layer over a surface of the body and applying a photoresist over the surface of said oxide layer; forming openings through said mask and said oxide layer to expose surface regions of the body where drains are to be formed and implanting ions of the opposite conductivity type through said openings into said body a predetermined distance from said surface; enlarging the size of said openings to expose an additional area of said surface around said drains by etching said oxide layer without removing said photoresist and then stripping said photoresist from said oxide layer by plasma etching; depositing a thin oxide layer over the exposed, enlarged surface region and then implanting ions of said one conductivity type through said enlarged openings into said body a distance greater than said predetermined distance to form channel stops extending into said body around and below said drains; simultaneously activating the atoms in said drain and said channel stops by heating said body in an inert ambient; stripping said oxide layer from said surface and forming another relatively thin oxide layer thereover, implanting ions of said opposite conductivity type into said surface a distance greater than said predetermined distance and less than said distance of channel stops to form buried channel regions on each side of channel stops and to convert a thin layer thereof adjacent said surface to lightly doped compensation regions of said opposite conductivity type, said thin layer extending into said body a distance less than said predetermined distance; thermally growing a channel oxide layer over said surface under conditions that simultaneously activate the atoms in said buried channel regions and said compensation regions and forming electrodes over said channel oxide layer.
Claim 11
Independent Claim
306 words
A method of making a buried channel CCD on a body of semiconductor material of one conductivity type, said method comprising: forming an oxide layer over a surface of the body and applying a photoresist over the surface of said oxide layer; forming openings through said mask and said oxide layer to expose surface regions of the body where drains are to be formed and implanting ions of the opposite conductivity type through said openings into said body a predetermined distance from said surface; enlarging the size of said openings to expose an additional area of said surface around said drains by etching said oxide layer without removing said photoresist and then stripping said photoresist from said oxide layer by plasma etching; depositing a thin oxide layer over the exposed, enlarged surface region and then implanting ions of said one conductivity type through said enlarged openings into said body a distance greater than said predetermined distance to form channel stops extending into said body around and below said drains; simultaneously activating the atoms in said drain and said channel stops by heating said body in an inert ambient; stripping said oxide layer from said surface and forming another relatively thin oxide layer thereover, implanting ions of said opposite conductivity type into said surface a distance greater than said predetermined distance and less than said distance of channel stops to form buried channel regions on each side of channel stops and to convert a thin layer thereof adjacent said surface to lightly doped compensation regions of said opposite conductivity type, said thin layer extending into said body a distance less than said predetermined distance; thermally growing a channel oxide layer over said surface under conditions that simultaneously activate the atoms in said buried channel regions and said compensation regions and forming electrodes over said channel oxide layer.
References Cited (Backward Citations)
US3863065A
Cited
US4028716A
Cited
US3896474A
Cited
US3927468A
Cited
US3930893A
Cited
US4076557A
Cited
US4108686A
Cited
US4173064A
Cited
US4152715A
Cited
US4212683A
Cited
US4197630A
Cited
US4280855A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-06 | 1986-06-07 | 1986-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-06 | 1990-06-07 | 1990-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-06 | 1994-06-07 | 1994-12-07 | $7700.00 | Window Closed / Lapsed |